Skin compositions and methods of use thereof

ABSTRACT

Provided are body corrective cosmetic formulations and methods of use thereof.

RELATED APPLICATIONS

This application is claims the benefit of U.S. Provisional PatentApplication No. 61/500,455, filed Jun. 23, 2011; U.S. Provisional PatentApplication No. 61/499,002, filed Jun. 20, 2011; U.S. Provisional PatentApplication 61/496,420, filed Jun. 13, 2011; U.S. Provisional PatentApplication No. 61/493,020, filed Jun. 3, 2011; U.S. Provisional PatentApplication No. 61/489,119, filed May 23, 2011; U.S. Provisional PatentApplication No. 61/486,643, filed May 16, 2011; U.S. Provisional PatentApplication No. 61/472,995, filed Apr. 7, 2011; U.S. Provisional PatentApplication No. 61/446,337, filed Feb. 24, 2011; U.S. Provisional PatentApplication No. 61/432,458, filed Jan. 13, 2011; U.S. Provisional PatentApplication No. 61/412,531, filed on Nov. 11, 2010 and U.S. ProvisionalPatent Application No. 61/378,504, filed on Aug. 31, 2010. The entirecontents of the foregoing applications are hereby incorporated byreference.

BACKGROUND OF THE INVENTION

Current methods for reducing the appearance of skin imperfections, forexample wrinkles, fine lines, age spots, enlarged pores or scars,include invasive and non-invasive methods and formulations. Invasivetechniques, such as surgery, fillers (e.g., Restylane, Juvederm), laserresurfacing or Botox®, may provide longer-lasting effects and can treatprominent imperfections. However, many consumers either cannot afford ordo not wish undergo such drastic cosmetic treatments.

Examples of non-invasive methods include hiding imperfections byapplying a foundation-type make-up to the skin or applying a cosmeticformulation that includes an ingredient that may reduce the appearanceof the imperfections over time (e.g., an anti-wrinkle cream).Unfortunately, foundation make-up is not durable and cannot reduce theappearance of pronounced skin imperfections, such as deep wrinkles orscars, while cosmetic formulations containing ingredients that mayreduce the appearance of an imperfection take time to produce an effect,and also may not reduce the appearance of a pronounced imperfection. Inparticular, many current cosmetic formulations do not have the requiredmechanical properties to reduce the appearance of pronouncedimperfections.

High molecular weight polymers, including proteins and polysaccharides,have been used in attempts to develop anti-aging skin care cosmeticformulations (Jachowicz et al. Skin Res. and Tech., 2008, 14:312-319).While these polymers change the physical properties (e.g., elasticityand stiffness) of the skin upon application to the skin, they did notprovide the durability to enable natural, repeated facial motion forextended wear. The commercially available polymer materials used inskincare products today do not necessarily provide the elasticity,environmental resistance and skin adhesion for long lasting productperformance nor do they provide the aesthetic feel and appearancerequired by the consumer of cosmetic products.

SUMMARY OF THE INVENTION

The present invention provides durable, natural looking, non-invasivecompositions that exhibit desired aesthetic qualities and reduceappearance of skin and body imperfections, while providing cosmeticeffects that typically are achieved through more invasive, dermatologistadministered procedures, if at all.

In one embodiment, the invention provides non-invasive body correctiveformulations that form a body corrective film upon application to thesubject, thereby ameliorating body imperfections. The invention alsoprovides methods of using such body corrective formulations. In anotherembodiment, the invention provides cleansers to remove the film.

Accordingly, in one embodiment, the invention pertains, at least inpart, to body corrective formulations for application to a subject'sskin that comprise a) a reactive reinforcing component; and b) across-linking component; in which the cross-linking component catalyzesan in situ cross-linking of the reactive reinforcing component, suchthat a body corrective film is formed on the subject's skin and the filmhas an appearance of natural skin.

In one embodiment, the invention pertains, at least in part, to two partbody corrective formulation for application to a subject's skin thatcomprise a) a reactive reinforcing component; and b) a cross-linkingcomponent; in which the reactive reinforcing component and thecross-linking component are prevented from coming into contact prior touse; and in which the cross-linking component catalyzes an in situcross-linking of the reactive reinforcing component, such that a bodycorrective film is formed on the subject's skin.

In one embodiment, the invention provides, at least in part, to bodycorrective formulations for application to a subject's skin thatcomprise a) a reactive reinforcing component; and b) a cross-linkingcomponent; in which the reactive reinforcing component has a viscosityof between about 5,000 and about 1,000,000 cSt or cP at 25° C.; and inwhich the cross-linking component catalyzes an in situ cross-linking ofthe reactive reinforcing component, such that a body corrective film isformed on the subject's skin.

In one embodiment, the invention pertains, at least in part, to bodycorrective formulations for application to a subject's skin thatcomprise a) a reactive reinforcing component; and b) a cross-linkingcomponent in which the reactive reinforcing component has a vinyl tofunctional hydride ratio of between about 1:10 and about 1:100; and inwhich the cross-linking component catalyzes an in situ cross-linking ofthe reactive reinforcing component, such that a body corrective film isformed on the subject's skin.

In one embodiment, the invention pertains, at least in part, to bodycorrective films prepared by a process comprising the steps of: a)applying a reactive reinforcing component to a subject's skin; and b)applying a cross-linking component to the reactive reinforcingcomponent, in which the cross-linking component catalyzes an in situcross-linking of the reactive reinforcing component, such that a bodycorrective film is formed on the subject's skin.

In one embodiment, the invention pertains, at least in part, to bodyshaping films prepared by a process comprising the steps of a) applyinga reactive reinforcing component to a subject's skin; and b) applying across-linking component to the reactive reinforcing component, in whichthe cross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component, such that a body shaping film is formedon the subject's skin.

In one embodiment, the invention pertains, at least in part, to methodsfor correcting body imperfections in a subject comprising applying tothe subject's skin a formulation comprising a) a first reactivereinforcing component; and b) a second cross-linking component; in whichthe cross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component, such that a film is formed on the skin,thereby correcting the body imperfections.

In one embodiment, the invention pertains, at least in part, to methodsfor protecting a subject's skin comprising applying to the subject'sskin a formulation comprising a) a first reactive reinforcing component;and b) a second cross-linking component; in which the cross-linkingcomponent catalyzes an in situ cross-linking of the reactive reinforcingcomponent such that a film is formed on the skin, thereby protecting theskin.

In one embodiment, the invention pertains, at least in part, to methodsfor shaping a subject's body, comprising applying to the subject's bodya formulation comprising a) a first reactive reinforcing component; andb) a second cross-linking component; in which the cross-linkingcomponent catalyzes an in situ cross-linking of the reactive reinforcingcomponent such that a film is formed on the body, thereby shaping thebody.

In one embodiment, the invention pertains, at least in part, to methodsfor delivering an agent to a subject, comprising applying to thesubject's skin a formulation comprising a) a first reactive reinforcingcomponent optionally comprising one or more agents; and b) a secondcross-linking component optionally comprising one or more agents; inwhich the cross-linking component catalyzes an in situ cross-linking ofthe reactive reinforcing component such that a film is formed on theskin, thereby delivering the agent to the subject.

In one embodiment, the invention pertains, at least in part, to bodycorrective formulations for application to a subject's body, comprisingat least one preselected function modulating component, in which thecomposition forms a body corrective film upon application to thesubject's body.

In one embodiment, the invention pertains, at least in part, to bodycorrective formulations for application to a subject's skin that targeta treatment area on a subject's body, comprising at least onepreselected treatment specific component, wherein the composition formsa body corrective film upon application to the target treatment area onthe subject's body.

In one embodiment, the invention pertains, at least in part, to a filmremoving cleanser for use in removing, a body corrective film, whereinthe film is prepared by a process comprising the steps of applying areactive reinforcing component to skin; and applying a cross-linkingcomponent to said reactive reinforcing component, and wherein saidcross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component.

In another embodiment, the invention pertains, at least in part, to afilm removing cleanser comprising a film wetting component, apenetration component, a film swelling component and a film releasecomponent.

In some embodiments, the invention pertains to a formulation forrepairing a body corrective film applied to skin, wherein saidformulation comprises a) a first reactive reinforcing component and b) asecond cross-linking component, wherein the cross-linking componentcatalyzes an in situ cross-linking of the reactive reinforcing componentsuch that a film is formed on the skin.

In some embodiments, the invention pertains, at least in part, to amethod for repairing a body corrective film applied to skin comprisingthe steps of a) identifying an area of the film in need of repair; b)optionally smoothing the edges of the film; and c) applying aformulation for repairing the film, wherein the formulation comprises afirst reactive reinforcing component and a second cross-linkingcomponent, wherein the cross-linking component catalyzes an in situcross-linking of the reactive reinforcing component such that a film isformed on the skin, thereby repairing the body corrective film.

In some embodiment, the invention pertains, at least in part, to a kitfor repairing a body corrective film, the kit comprising a formulationcomprising a) a first reactive reinforcing component and b) a secondcross-linking component, wherein the cross-linking component catalyzesan in situ cross-linking of the reactive reinforcing component such thata film is formed on the skin.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a chart illustrating the change in the Young's Modulus of theskin after the application of a formulation of the invention. The changein Young's Modulus indicates that there is a reduction in the stiffnessof skin upon application of the formulation.

FIG. 2 is a chart illustrating the change in the retraction time afterapplication of a formulation of the invention. The change in theretraction time indicates that the skin is more elastic upon applicationof the formulation.

FIG. 3 is a chart illustrating the investigator's assessment of twoformulations by attribute in a randomized double blind clinical trial.The formulations are provided in Example 5. The attributes scoredincluded extent of shine reduction, pore reduction, deep wrinklereduction and fine wrinkle reduction. For all attributes theapplications of these two films provided an improvement for the 22subjects evaluated. These four attributes were further detailed bytreatment site. These sites are forehead, crow's feet, undereye, and thenose bridge (‘number 11's’). Improvements were observed for eachtargeted treatment area.

FIG. 4 is a chart illustrating the assessor's assessment of twoformulations described in Example 5 by attribute in a randomized doubleblind clinical trial. The assessor's assessments show an improvement ineach of the beauty attributes scored following application of theformulations.

FIG. 5 is a chart illustrating the panelist's assessment of twoformulations described in Example 5, by attribute, in a randomizeddouble blind clinical trial. The attributes evaluated were youthfulappearance, mattification (or shine reduction), pore size, even skintone, tightened skin appearance, and wrinkling. For each attribute, thepanelists, on average experienced an improvement in each benefitfollowing treatment with the formulations.

FIG. 6 is a chart illustrating the average age reduction of thepanelists as determined by the assessors. Overall age reductions of 8.7years and 7.7 years age were observed for formulation 60-140-LX2 and forformulation 60-140-1, respectively.

FIG. 7 is a chart illustrating the average Griffith's score result fromthe blinded evaluation of the panelist's photographs. The Griffith'sscore is a standardized quantitative measure of the extent ofphotodamage, where a score of 0 corresponds to no photodamage, and ascore of 9 represents severe photodamage. For the two examples, theGriffith's score was reduced by 2.15 and by 1.25 points, followingapplication of formula 60-140-LX2 and 60-140-1, respectively. Thisresult is consistent with FIGS. 4 and 5, where panelists appearedyounger following formulation application.

DETAILED DESCRIPTION OF THE INVENTION

In some embodiments, the invention pertains, at least in part, to bodycorrective formulations for application to the skin that comprise a) areactive reinforcing component; and b) a cross-linking component; inwhich the cross-linking component catalyzes an in situ cross-linking ofthe reactive reinforcing component, such that a body corrective film isformed on the skin.

The language “body corrective formulation” or “formulation” includescosmetic compositions that, when applied to the body, form a film on thebody that ameliorate body imperfections. The language “bodyimperfections” includes those parts of a subject's body that the subjectperceives as blemished or a flawed, or in which a skilled artisan, forexample a dermatologist, an aesthetician or a plastic surgeon, wouldconsider as blemished or flawed. The language “body imperfections”include skin imperfections, as well as sagging of soft body tissues(e.g., loose or sagging skin, sagging breasts, buttocks, abdomen, jowls,neck and the like). The language “skin imperfections” include thoseitems on a subject's skin that the subject perceives as a blemish or aflaw. Examples of skin imperfections include port wine stain or nevusflammeus (e.g., nevus flammeus nuchae or midline nevus flammeus)melasma, wrinkles, blemishes, acne, moles, scars, tattoos, bruises, skindisfigurements, birth marks, sun damage, age damage, uneven skin tone,sagging skin, skin roughness, hyperpigmentation, enlarged pores,telangiectasia, redness, shine, cellulite, stretch marks or loss of skinelasticity.

In one embodiment of the invention, the compositions, formulations orfilms of the invention result in visual and or tactile improvement inskin properties. In certain embodiments, the compositions, formulationsor films of the invention mask, conceal, or cover, but do not treat theskin or body imperfection of the subject.

In at least one embodiment, a skin or body imperfection does not includewounds or dermatological disorders.

The language “wounds” includes injuries to the skin wherein the skin istorn, cut or punctured. A wound is a break in the skin. In oneembodiment, the wound is caused by skin contact with a foreign object.The break in the skin may cause external bleeding. Wounds include openwounds, for example, abrasions, lacerations, incisions, punctures,avulsions, or amputations. Wounds also include burn wounds. A burn is atype of injury to flesh caused by heat, electricity, chemicals, light,radiation or friction.

The language “dermatological disorder” includes disorders that cause atleast one symptom on the skin of a subject requiring medical treatment.In one embodiment, dermatological disorders are caused by autoimmunedisorders. In another embodiment, a dermatological disorder is caused byenvironmental factors, such a allergens or chemicals. Examples ofsymptoms of dermatological disorders requiring treatment is dermatitis,itchy skin, dry skin, crusting, blistering, or cracking skin, skinedema, or skin lesion formation. Dermatological disorders include, butare not limited to, lichen simplex chronicus, cutaneous lupus (e.g.,acute cutaneous lupus, subacute cutaneous lupus, chronic cutaneouslupus, chilblain lupus erythematosus, discoid lupus erythematosus, lupuserythematosus-lichen planus overlap syndrome, lupus erythematosuspanniculitis, tumid lupus erythematosus and verrucous lupuserythematosus), psoriasis (e.g., psoriasis vulgaris, psoriaticerythroderma, pustular psoriasis, drug-induced psoriasis, inversepsoriasis, seborrheic-like psoriasis and guttate psoriasis), eczema(e.g., atopic eczema, atopic dermatitis, contact dermatitis, xeroticeczema, seborrhoeic dermatitis, dyshidrosis, discoid eczema, venouseczema, dermatitis herpetiformis, neurodermatitis andautoeczematization), or chronic dry skin.

In some embodiments, the body corrective formulation is a skincorrective formulation. The language “skin corrective formulation,”includes cosmetic compositions that, when applied to the skin, form afilm on the skin that ameliorate skin imperfections. In someembodiments, the amelioration is a complete amelioration or a partialamelioration. One of skill in the art would be able to determine theextent of amelioration of one or more of the body imperfections by usingthe methods described in Example 6.

In some embodiments, the body corrective formulation is a body shapingformulation. A body shaping formulation includes cosmetic compositionsthat when applied to the skin, form a body shaping film on the subject'sskin.

In some embodiments, the body corrective formulation is a skinprotective formulation. A skin protective formulation includes cosmeticcompositions that when applied to the skin, form a protective film onthe subject's skin.

In some embodiments, the body corrective formulation can delivercosmetic or therapeutic agents to a subject in need thereof.

In some embodiments, the body corrective formulation is used to repair abody corrective film.

In one embodiment, the body corrective formulations include a reactivereinforcing component and a cross-linking component. The language“reactive reinforcing component” includes a component that, when appliedto the skin as a first component, is the basis of the body correctivefilm that is formed upon application of the cross-linking component tothe reactive reinforcing component. In one embodiment, the reactivereinforcing component includes at least one reactive constituent and atleast one reinforcing constituent.

The language “reactive constituent” includes one or more constituents ofthe reactive reinforcing component that provide the reactivefilm-forming elements of the formulation. In some embodiments, thereactive constituent includes at least one polysiloxane, polyethyleneoxide, polypropylene oxide, polyurea, polyurethane, polyester (includingpolylactic-co-glycolic acid, polycaprolactone, polylactic acid,polyglycolic acid, and polyhydroxybutyrate, polyamide, or polysulfone.In another embodiment, the reactive constituent is a compound of formulaI:

wherein

W is R¹R²R³SiO—, OR⁴, —NR⁵R⁶, —CR⁷R⁸R⁹ or C₅₋₁₀ aryl;

X is —R¹¹R¹²Si—O—, —OCONR¹³—, —NR¹⁴CONR¹⁵—, —CO—, —NR¹⁶CO—, —SO₂—, —O—,—S— or —NR¹⁷—;

V is absent, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, —O—, —NR¹⁰— or —S—;

Y is —R¹⁸R¹⁹Si—O—, —OCONR²⁰—, —NR²¹CONR²²—, —CO—, —NR²³CO—, —SO₂—, —O—,—S— or —NR²⁴;

Z is —SiR²⁵R²⁶R²⁷, OR²⁸, —NR²⁹R³⁰, —CR³¹R³²R³³ or C₅₋₁₀ aryl;

R¹, R², R³, R⁷, R⁸, R⁹, R¹¹, R¹², R¹⁸ R¹⁹, R²⁵, R²⁶, R²⁷, R³¹, R³² andR³³ are each independently hydrogen, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀aryl, hydroxyl or C₁₋₂₀ alkoxyl;

R⁴, R⁵, R⁶, R¹³, R¹⁴, R¹⁵, R¹⁶, R¹⁷, R²⁰, R²¹, R²², R²³, R²⁴, R²⁸, R²⁹and R³⁰ are each independently hydrogen, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl,C₅₋₁₀ aryl; and

s and t are each independently an integer from about 0 to about 6000.

X and Y of formula I represent an independent “monomer unit.” The numberof X and Y monomer units present in formula I is provided by the valueof s and t, respectively. Representative monomer units include:

where R is as for defined for R¹, R², R³, etc, above.It is understood that when more than one X (or Y) monomer unit ispresent (e.g. s (or t) is more than one), the values for R¹¹, R¹², R¹³,R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸R¹⁹, R²⁰, R²¹, R²², R²³, and R²⁴ are selectedindependently for each individual monomer unit described by —[X]_(s)—(or —[Y]_(t)—). For example, if the value of the monomer unit X is—R¹¹R¹²Si—O— and the value of s is 3, then —[X]_(s)— is

—[R¹¹R¹²Si—O—R¹¹R¹²Si—O—R¹¹R¹²Si—O]—.

In this example, it is understood that the three R¹¹ groups present inmay be the same or different from each other, for example, one R¹¹ maybe hydrogen, and the two other R¹¹ groups may be methyl.

W and Z of formula I represent independent terminal caps, one on eachend of the. For example, terminal caps include:

wherein

denotes attachment to a monomer unit and wherein R is as for defined forR¹, R², R³, etc, above. In one embodiment,

W is R¹R²R³SiO—, —OR⁴, —NR⁵R⁶, —CR⁷R⁸R⁹ or C₅₋₁₀ aryl;

X is —R¹¹R¹²Si—O—, or —NR¹⁴CONR¹⁵—;

V is absent, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, —O—, —NR¹⁰— or —S—;

Y is —R¹⁸R¹⁹Si—O—, or —NR²¹CONR²²—;

Z is —SiR²⁵R²⁶R²⁷, —OR²⁸, —NR²⁹R³⁰, —CR³¹R³²R³³ or C₅₋₁₀ aryl;

R¹, R², R³, R⁷, R⁸, R⁹, R¹¹, R¹², R¹⁸R¹⁹, R²⁵, R²⁶, R²⁷, R³¹, R³² andR³³ are each independently hydrogen, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀aryl, hydroxyl or C₁₋₂₀ alkoxyl;

R⁴, R⁵, R⁶, R¹⁴, R¹⁵, R²¹, R²², R²⁸, R²⁹ and R³⁰ are each independentlyhydrogen, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀ aryl; and

s and t are each independently an integer from about 0 to about 6000,wherein the sum of s and t is not 0.

In one embodiment,

W is R¹R²R³SiO—, —CR⁷R⁸R⁹ or C₅₋₁₀ aryl;

X is —R¹¹R¹²Si—O—, or —NR¹⁴CONR¹⁵—;

V is absent, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, or C₅₋₁₀ aryl;

Y is —R¹⁸R¹⁹Si—O—, or —NR²¹CONR²²—;

Z is —SiR²⁵R²⁶R²⁷, —CR³¹R³²R³³ or C₅₋₁₀ aryl;

R¹, R², R³, R⁷, R⁸, R⁹, R¹¹, R¹², R¹⁸R¹⁹, R²⁵, R²⁶, R²⁷, R³¹, R³² andR³³ are each independently hydrogen, C₁₋₂₀ alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀aryl, hydroxyl or C₁₋₂₀ alkoxyl;

R¹⁴, R¹⁵, R²¹, and R²² are each independently hydrogen, C₁₋₂₀ alkyl,C₂₋₂₀ alkenyl, C₅₋₁₀ aryl; and

s and t are each independently an integer from about 0 to about 6000,wherein the sum of s and t is not 0.

In one embodiment, V is absent, W is R¹R²R³SiO—; X is −R¹¹R¹²Si—O—; Y is—R¹⁸R¹⁹Si—O—; Z is —SiR²⁵R²⁶R²⁷; and R¹, R², R³, R¹¹, R¹², R¹⁸, R¹⁹,R²⁵, R²⁶ and R²⁷ are each independently selected from C₁₋₂₀ alkyl (e.g.,C₁ alkyl, such as methyl) or C₂₋₂₀ alkenyl (e.g., C₂ alkenyl, such asvinyl). In one embodiment, at least one of R¹, R², R³, R¹¹, R¹², R¹⁸,R¹⁹, R²⁵, R²⁶ and R²⁷ is C₂₋₂₀ alkenyl, for example, C₂ alkenyl (e.g.,vinyl). In another embodiment, at least two of R¹, R², R³, R¹¹, R¹²,R¹⁸, R¹⁹, R²⁵, R²⁶ and R²⁷ are C₂₋₂₀ alkenyl, for example, C₂ alkenyl(e.g., vinyl). In some embodiments, at least one of R¹, R², R³, R²⁵, R²⁶and R²⁷ are each C₂₋₂₀ alkenyl, for example, C₂ alkenyl (e.g., vinyl).

In one embodiment, V is absent, W is R¹R²R³SiO—; X is —R¹¹R¹²Si—O—; Y is—R¹⁸R¹⁹Si—O—; Z is —SiR²⁵R²⁶R²⁷; and R¹, R², R³, R²⁵, R²⁶ and R²⁷ areeach independently selected from C₁₋₂₀ alkyl (e.g., C₁ alkyl, such asmethyl) or C₂₋₂₀ alkenyl (e.g., C₂ alkenyl, such as vinyl); and R¹¹,R¹², R¹⁸, and R¹⁹ are each independently selected from C₁₋₂₀ alkyl(e.g., C₁ alkyl, such as methyl). In one embodiment, at least one of R¹,R², R³, and at least one of R²⁵, R²⁶ and R²⁷ is C₂₋₂₀ alkenyl, forexample, C₂ alkenyl (e.g., vinyl). In one embodiment, one of R¹, R², R³is C₂ alkenyl (e.g., vinyl) and the others are C₁₋₂₀ alkyl (e.g., C₁alkyl, such as methyl), and at least one of R²⁵, R²⁶ and R²⁷ is C₂₋₂₀alkenyl, for example, C₂ alkenyl (e.g., vinyl) and the others are C₁₋₂₀alkyl (e.g., C₁ alkyl, such as methyl). In one embodiment, at least oneof R¹¹ or R¹² and at least one of R¹⁸ or R¹⁹ is C₂₋₂₀ alkenyl, forexample, C₂ alkenyl (e.g., vinyl) for at least one monomer unit. In oneembodiment, one of R¹¹ or R¹² is C₂ alkenyl (e.g., vinyl) and the othersare C₁₋₂₀ alkyl (e.g., C₁ alkyl, such as methyl), and at least one ofR¹⁸ or R¹⁹ is C₂₋₂₀ alkenyl, for example, C₂ alkenyl (e.g., vinyl) andthe others are C₁₋₂₀ alkyl (e.g., C₁ alkyl, such as methyl) for at leastone monomer unit.

In some embodiments, the organopolysiloxane includes vinyl moieties onlyat the terminal caps of the polymer. In some embodiments, theorganopolysiloxane include vinyl moieties only in the monomer units, butnot at the terminal cap of the polymer. In other embodiments, theorganopolysiloxane includes vinyl moieties at both the terminal cap orin the monomer unit of the polymer. In one embodiment, the polymerincludes two vinyl moieties located either at the terminal cap, orwithin the monomer unit, or a combination thereof.

In one embodiment, on average at least two vinyl moieties are present inthe polymer. In a specific embodiment, at least two vinyl moieties arepresent in the polymer and at least two vinyl moieties are present onthe two terminal caps of the polymer. In a specific embodiment, only twovinyl moieties are present in the polymer. In a specific embodiment,only two vinyl moieties are present in the polymer and are located oneach of the terminal caps. In a specific embodiment, on average at leasttwo vinyl moieties are present in the polymer and at least two vinylmoieties are present in one or more monomer units of the polymer. In aspecific embodiment, on average at least two vinyl moieties are presentanywhere in the polymer, but separated from another vinyl moiety byabout 2000 monomer units, for example, 1500, 1600, 1700, 1800, 1900,2000, 2100, 2200, 2300, 2400, or 2500 monomer units. In a specificembodiment, on average at least two vinyl moieties are present anywherein the polymer, but separated from another vinyl moiety by about 850monomer units, for example, 350, 450, 550, 650, 750, 850, 950, 1050,1150, 1250, or 1350 monomer units. In a specific embodiment, on averagegreater two vinyl moieties are present anywhere in the polymer, butseparated from another vinyl moiety by about 40 monomer units, forexample, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or80 monomer units. In a specific embodiment, one or more Si—H units arepresent in addition to the vinyl moiety. Alternatively, in oneembodiment, if a vinyl moiety is present then a Si—H is not present.

In one embodiment, V is absent, W is R¹R²R³SiO—; X is R¹¹R¹²Si—O—; Y is—R¹⁸R¹⁹Si—O—; Z is —SiR²⁵R²⁶R²⁷; R¹, R², R³, R¹¹, R¹², R¹⁸, R¹⁹, R²⁵,R²⁶ and R²⁷ are each independently are each independently selected fromhydrogen or C₁₋₂₀ alkyl (e.g., C₁ alkyl, such as methyl). In oneembodiment, R¹, R², R³, R²⁵, R²⁶ and R²⁷ are each independently selectedfrom C₁₋₂₀ alkyl (e.g., C₁ alkyl, such as methyl); and R¹¹, R¹², R¹⁸,and R¹⁹ are each independently selected from hydrogen or C₁₋₂₀ alkyl(e.g., C₁ alkyl, such as methyl), wherein at least one of and R¹¹, R¹²,R¹⁸, and R¹⁹ are hydrogen for at least one monomer unit. In oneembodiment, on average greater than two Si—H units (e.g. one or more ofR¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen) are present in the polymer, forexample 3-15 Si—H units may be present. In a specific embodiment, 8 Si—Hunits are present. In one embodiment, one or more Si—H units (e.g. oneor more of R¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen) are present in thepolymer. In one embodiment, at least two monomer units include a —Si—Hunit (e.g. one or more of R¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen). In oneembodiment, at least three monomer units include a —Si—H unit (e.g. oneor more of R¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen). In one embodiment, atleast four monomer units include a —Si—H unit (e.g. one or more of R¹¹,R¹², and R¹⁹ is hydrogen). In one embodiment, at least five monomerunits include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, and R¹⁹is hydrogen). In one embodiment, at least six monomer units include a—Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen). Inone embodiment, at least seven monomer units include a —Si—H unit (e.g.one or more of R¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen). In one embodiment,at least eight monomer units include a —Si—H unit (e.g. one or more ofR¹¹, R¹², R¹⁸, and R¹⁹ is hydrogen). In one embodiment, a Si—H unit maybe present in one or both the terminal caps in addition to being presentin a monomer unit as described above. In a specific embodiment,Si-(alkyl) or Si-(vinyl) units may also be present in the polymer. In aspecific embodiment, only Si—CH₃ and Si—H units are present. In aspecific embodiment, monomer units or terminal caps include C₁-C₂₀alkyl,specifically methyl groups, for the non-Si—H positions of the polymer.

In a specific embodiment, on average at least two Si—H units are presentin the polymer. In a specific embodiment, on average at least two Si—Hmoieties are present anywhere in the polymer, but separated from anotherSi—H moiety by about 2000 monomer units, for example, 1500, 1600, 1700,1800, 1900, 2000, 2100, 2200, 2300, 2400, or 2500 monomer units. In aspecific embodiment, on average at least two Si—H units are presentanywhere in the polymer, but separated from another Si—H moiety by about850 monomer units, for example, 350, 450, 550, 650, 750, 800, 850, 950,1050, 1150, 1250, or 1350 monomer units. In a specific embodiment, onaverage greater than two Si—H units are present anywhere in the polymer,but separated from another Si—H moiety by about 40 monomer units, forexample, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, or80 monomer units.

In one aspect of any one of the above embodiments, the sum of s and t isan integer from about 1000 to about 8000; from about 1300 to about 2700;from about 1500 about 2700; from about 1600 to about 2600; from about1600 to about 2500; from about 1700 to about 2500; from about 1800 toabout 2400; from about 1800 to about 2300; from about 1900 to about2300; from about 2000 to about 2200; from about 2050 to about 2150; fromabout 2100.

In one aspect of any one of the above embodiments, the sum of s and t isan integer from about 200 to about 1100; from about 600 to about 1100;from about 700 to about 1000; from about 800 to about 900; from about825 to about 875; from about 850; from about 200 to about 800; fromabout 225 to about 700; from about 250 to about 600; from about 275 toabout 500; from about 300 to about 400; from about 350 to about 400;from about 375. In a specific embodiment, the sum of s and t is aninteger from about 850.

In one aspect of any one of the above embodiments, the sum of s and t isan integer from about 5 to about 1300; from about 10 to about 1100; fromabout 10 to about 600; from about 15 to about 500; from about 15 toabout 400; from about 20 to about 300; from about 20 to about 200; fromabout 25 to about 100; from about 25 to about 75; from about 30 to about50; from about 40.

In some embodiments the reactive constituent comprises at least oneorganopolysiloxane. The term “organopolysiloxane” includes compounds offormula II:

wherein R^(1a), R^(2a), R^(1a), R^(4a), R^(5a), R^(6a), R^(7a), R^(8a),R^(9a) and R^(10a) are each independently selected from hydrogen, C₁₋₂₀alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, hydroxyl or C₁₋₂₀ alkoxyl and p and qare each independently an integer from between 10 and about 6000.

In some embodiments, the organopolysiloxane is a compound of formulaIIa:

wherein R^(1a)′, R^(3a′), R^(4a′), R^(5a′), R^(6a′), R^(8a′), R^(9a′)and R^(10a′) are each independently selected from hydrogen, C₁₋₂₀ alkyl,C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, hydroxyl or C₁₋₂₀ alkoxyl and p and q areeach independently an integer from between 10 and about 6000. In oneembodiment, R^(1a)′, R^(3a′), R^(4a′), R^(5a′), R^(6a′), R^(8a′),R^(9a′) and R^(10a′) are alkyl (e.g., C₁ alkyl, such as methyl).

The term “alkyl” includes both branched and straight-chain saturatedaliphatic hydrocarbon groups having the specified number of carbonatoms. The term “C₁₋₂₀ alkyl” includes branched and straight chainaliphatic groups having between 1 and 20 carbons. Examples of alkylmoieties include methyl, ethyl, n-propyl, i-propyl, n-butyl, s-butyl,t-butyl, n-pentyl, n-hexyl, isopropyl, isobutyl, sec-butyl, tert-butyl,isopentyl, and s-pentyl. Moreover, the term alkyl includes both“unsubstituted alkyls” and “substituted alkyls,” the latter of whichrefers to alkyl moieties having substituents (e.g., F, Cl, Br, I, NO₂,CN, alkyl, aryl, hydroxyl, alkoxy, COCH₃ and the like) replacing ahydrogen on one or more carbons of the hydrocarbon backbone.

The term “alkenyl” includes the specified number of hydrocarbon atoms ineither straight or branched configuration with one or more unsaturatedcarbon-carbon bonds that may occur in any stable point along the chain,such as ethenyl and propenyl. The language “C₂₋₂₀ alkenyl” includesbranched and straight chain hydrocarbon groups with between 1 and 20carbons and with one or more unsaturated carbon-carbon bonds. Moreover,the term “alkenyl” includes both “unsubstituted alkenyls” and“substituted alkenyls,” the latter of which refers to alkenyl moietieshaving substituents F, Cl, Br, I, NO₂, CN, alkyl, aryl, hydroxyl,alkoxy, COCH₃ and the like) replacing a hydrogen on one or more carbonsof the hydrocarbon backbone.

The term “aryl” includes 5-10 membered monocyclic, bicyclic, ortricyclic rings, wherein at least one ring, if more than one is present,is aromatic. The term “aryl” also includes “heteraryl” moieties in whichone heteroatom (e.g., N, O or S) replaces one or more carbons in themonocyclic, bicyclic, or tricyclic ring. The term “aryl” also includesboth “unsubstituted aryls” and “substituted aryls,” the latter of whichrefers to aryl moieties having substituents (e.g., F, Cl, Br, I, NO₂,CN, alkyl, hydroxyl, alkoxy, COCH₃ and the like) replacing a hydrogen onone or more carbons aromatic ring.

The term “hydroxyl” includes —OH.

The term “alkoxy” includes moieties in which an O is covalently bondedto a C₁₋₂₀ alkyl group, as defined above.

In some embodiments, the organopolysiloxane is vinyl terminated. Thelanguage “vinyl terminated organopolysiloxane” includesorganopolysiloxanes of formula II in which one or both of R^(2a) andR^(7a) are substituted with a C₂ alkyl moiety, for example, a vinylmoiety (e.g., —CH═CH₂). In a specific embodiment, a “vinyl terminatedorganopolysiloxane” includes organopolysiloxanes of formula II in whichone or both of R^(2a) and R^(7a) are substituted with a C₂ alkyl moiety,for example, a vinyl moiety (e.g., —CH═CH₂), and R^(1a), R^(3a), R^(4a),R^(5a), R^(6a), R^(8a), R^(9a) and R^(10a) are independently selectedfrom C₁₋₂₀ alkyl, for example, methyl.

In other embodiments, the organopolysiloxane is selected from: vinylterminated polydimethylsiloxane; vinyl terminateddiphenylsiloxane-dimethylsiloxane copolymers; vinyl terminatedpolyphenylmethylsiloxane, vinylphenylmethyl terminatedvinylphenylsiloxane-phenylmethylsiloxane copolymer; vinyl terminatedtrifluoropropylmethylsiloxane-dimethylsiloxane copolymer; vinylterminated diethylsiloxane-dimethylsiloxane copolymer;vinylmethylsiloxane-dimethylsiloxane copolymer, trimethylsiloxyterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, silanolterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, vinylterminated; vinyl gums; vinylmethylsiloxane homopolymers; vinylT-structure polymers; monovinyl terminated polydimethylsiloxanes;vinylmethylsiloxane terpolymers; vinylmethoxysilane homopolymers andcombinations thereof.

In some embodiments, the organopolysiloxane is a high viscosityorganopolysiloxane, a low viscosity organopolysiloxane or a combinationthereof.

When the organopolysiloxane is a combination of high and low viscosityorganopolysiloxanes, the combination of a high viscosity and a lowviscosity vinyl organosiloxane provides a bimodal distribution oforganosiloxane molecular weights. In at least one embodiment, theorganopolysiloxane is a combination of high and low viscosityvinyl-terminal organopolysiloxanes providing a bimodal distribution ofthe vinyl-terminated organopolysiloxane. In one embodiment, theorganopolysiloxane is a combination of formulas I, II, IIa, IIb, andIIc, specifically, of formula IIa, IIb and/or IIc, or more specifically,of formula IIb and IIc, providing a bimodal distribution of thevinyl-terminated organopolysiloxane. In one embodiment, the bimodaldistribution of polymer molecular weight is represented by a ratio ofthe molecular weights (for example, the sum of s and t) of the highviscosity organopolysiloxanes to the low viscosity organopolysiloxane.In one embodiment, this ratio is from 2 to 3. In a specific embodiment,this ratio is 2.5.

The term “viscosity” refers to the measure of the resistance of a fluidwhich is being deformed by either shear stress or tensile stress. One ofskill in the art without undue experimentation would be able todetermine how to measure the viscosity of a fluid, for example, using aviscometer or a rheometer. Representative methods include use of acapillary viscometer, rotational viscometer or rheometer to measureviscosity at an instrument specific strain. Specific methods fordetermining the viscosity of a fluid are shown in Example 8.

The language “high viscosity organopolysiloxane” includesorganopolysiloxanes with a viscosity of between about 100,000 and about500,000 cSt or cP at 25° C., for example, between about 110,000 andabout 450,000 cSt or cP at 25° C., between about 120,000 and about400,000 cSt or cP at 25° C., between about 125,000 and about 350,000 cStor cP at 25° C., between about 130,000 and about 300,000 cSt or cP at25° C., between about 135,000 and about 250,000 cSt or cP at 25° C.,between about 140,000 and about 200,000 cSt or cP at 25° C., betweenabout 145,000 and about 190,000 cSt or cP at 25° C., between about150,000 and about 185,000 cSt or cP at 25° C., between about 155,000 andabout 175,000 cSt or cP at 25° C., or between about 160,000 and about170,000 cSt or cP at 25° C. In some embodiments, the viscosity of thehigh viscosity organopolysiloxane is between about 140,000 and about200,000 cSt or cP at 25° C. In one embodiment, the high viscosityorganopolysiloxane has a viscosity of about 165,000 cSt or cP at 25° C.

In one embodiment, the average molecular weight of the high viscosityorganopolysiloxane is between about 100,000 and about 200,000 Da, forexample, between about 115,000 and about 195,000 Da, between about120,000 and about 190,000 Da, between about 125,000 and about 185,000Da, between about 130,000 and about 180,000 Da, between about 135,000and about 175,000 Da, between about 140,000 and about 170,000 Da,between about 145,000 and about 165,000 Da or between about 150,000 andabout 160,000 Da. In one embodiment, the average molecular weight of thehigh viscosity organopolysiloxane is about 155,000 Da.

In some embodiments, the high viscosity organopolysiloxane is of formulaII, in which R^(2a) and R^(7a) are C₂₋₂₀ alkenyl, for example, C₂alkenyl (e.g., vinyl) and R^(1a), R^(3a), R^(4a), R^(5a), R^(6a),R^(8a), R^(9a) and R^(10a) are each C₁₋₂₀ alkyl, for example, C₁ alkyl(e.g., methyl). In some embodiments, the high viscosityorganopolysiloxane is vinyl terminated. In other embodiments, the highviscosity organopolysiloxane is vinyl terminated polydimethylsiloxane.

In some embodiments, the vinyl terminated high viscosityorganopolysiloxane has a weight percent of vinyl of between about 0.010and about 0.100, for example, between about 0.015 and about 0.080,between about 0.020 and about 0.075, between about 0.025 and about0.060, or between about 0.030 and about 0.050. In one embodiment, thehigh viscosity organopolysiloxane has a weight percent of vinyl ofbetween about 0.030 and about 0.040.

In other embodiments, the high viscosity organopolysiloxane has a vinylequivalent per kilogram of between about 0.0100 and about 0.0200, forexample, between about 0.0110 and about 0.0190, between about 0.0115 andabout 0.0180, between about 0.0120 and about 0.0170, between about0.0125 and about 0.0165 or between about 0.013 and about 0.016.

In one embodiment, the high viscosity organopolysiloxane has on averageat least two vinyl units per high viscosity organopolysiloxane. In oneembodiment, the monomer unit including a vinyl moiety are spacedthroughout the polymer. In one embodiment, the vinyl-containing monomerunit is spaced about 2000 monomer units away from anothervinyl-containing monomer unit or a vinyl-containing terminal cap. Forexample, the vinyl units in the high viscosity organopolysiloxanes areseparated by 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400,or 2500 monomer units.

In some embodiments, the high viscosity organopolysiloxane is selectedfrom: vinyl terminated polydimethylsiloxane; vinyl terminateddiphenylsiloxane-dimethylsiloxane copolymers; vinyl terminatedpolyphenylmethylsiloxane, vinylphenylmethyl terminatedvinylphenylsiloxane-phenylmethylsiloxane copolymer; vinyl terminatedtrifluoropropylmethylsiloxane-dimethylsiloxane copolymer; vinylterminated diethylsiloxane-dimethylsiloxane copolymer;vinylmethylsiloxane-dimethylsiloxane copolymer, trimethylsiloxyterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, silanolterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, vinylterminated; vinyl gums; vinylmethylsiloxane homopolymers; vinylT-structure polymers; monovinyl terminated polydimethylsiloxanes;vinylmethylsiloxane terpolymers; vinylmethoxysilane homopolymers andcombinations thereof.

The language “low viscosity organopolysiloxane” includesorganopolysiloxanes with a viscosity of between about 500 and about50,000 cSt or cP at 25° C., for example, between about 1,000 and about45,000 cSt or cP at 25° C., between about 1,500 and about 40,000 cSt orcP at 25° C., between about 2,000 and about 35,000 cSt or cP at 25° C.,between about 2,500 and about 30,000 cSt or cP at 25° C., between about3,000 and about 25,000 cSt or cP at 25° C., between about 3,500 andabout 20,000 cSt or cP at 25° C., between about 4,000 and about 15,000cSt or cP at 25° C., or between about 4,000 and about 12,000 cSt or cPat 25° C. In some embodiments, the low viscosity organopolysiloxaneincludes organopolysiloxanes with a viscosity of between about 100 andabout 5,000 cSt or cP at 25° C., for example, between about 200 andabout 4000 cSt or cP at 25° C., between about 300 and about 3000 cSt orcP at 25° C., between about 400 and about 2000 cSt or cP at 25° C. orbetween about 750 and about 1500 cSt or cP at 25° C. In one embodiment,the low viscosity organopolysiloxane has a viscosity of about 10,000 cStor cP at 25° C. In some embodiments, the low viscosityorganopolysiloxane has a viscosity of about 1000 cSt or cP at 25° C.

In some embodiments, the low viscosity organopolysiloxane has an averagemolecular weight of between about 20,000 and about 80,000 Da, forexample, between about 50,000 and about 75,000 Da, between about 55,000and about 70,000 Da, between about 60,000 and about 65,000 Da or between62,000 and about 63,000 Da. In one embodiment, the low viscosityorganopolysiloxane has an average molecular weight of about 62,700 Da.In one embodiment, the low viscosity organopolysiloxane has an averagemolecular weight of about 28,000 Da.

In some embodiments, the low viscosity organopolysiloxane is of formulaII, in which R^(2a) and R^(7a) are C₂₋₂₀ alkenyl, for example, C₂alkenyl (e.g., vinyl) and R^(1a), R^(3a), R^(4a), R^(5a), R^(6a),R^(8a), R^(9a) and R^(10a) are each C₁₋₂₀ alkyl, for example, C₁ alkyl(e.g., methyl). In some embodiments, the low viscosityorganopolysiloxane is vinyl terminated. In other embodiments, the lowviscosity organopolysiloxane is vinyl terminated polydimethylsiloxane.

In some embodiments, the low viscosity organopolysiloxane has a weightpercent of vinyl of between about 0.010 and about 0.30, for example,between about 0.020 and about 0.29, between about 0.030 and about 0.28,between about 0.040 and about 0.27, between about 0.050 and about 0.26,between about 0.060 between about 0.25, between about 0.070 and about0.24, between about 0.080 and about 0.23, or between about 0.090 andabout 0.22. In some embodiments, the low viscosity organopolysiloxanehas a weight percent of vinyl of between about 0.18 and about 0.26.

In other embodiments, the low viscosity organopolysiloxane has a vinylequivalent per kilogram of between about 0.010 and about 0.100, forexample, between about 0.015 and about 0.090, between about 0.020 andabout 0.080, between about 0.025 and about 0.070, between about 0.030and about 0.060 or between about 0.040 and about 0.050. In someembodiments, the low viscosity organopolysiloxane has a vinyl equivalentper kilogram of between about 0.030 and about 0.040.

In other embodiments, the low viscosity organopolysiloxane has onaverage at least two vinyl units per low viscosity organpolysiloxane. Inone embodiment, the monomer unit including a vinyl moiety are spacedthroughout the polymer. In one embodiment, the vinyl-containing monomerunit is spaced about 800 monomer units away from anothervinyl-containing monomer unit or a vinyl-containing terminal cap. Forexample, the vinyl units in the low viscosity organopolysiloxanes areseparated by 450, 550, 650, 750, 800, 850, 950, 1050, 1150, 1250, or1350 monomer units.

In some embodiments, the low viscosity organopolysiloxane is selectedfrom: vinyl terminated polydimethylsiloxane; vinyl terminateddiphenylsiloxane-dimethylsiloxane copolymers; vinyl terminatedpolyphenylmethylsiloxane, vinylphenylmethyl terminatedvinylphenylsiloxane-phenylmethylsiloxane copolymer; vinyl terminatedtrifluoropropylmethylsiloxane-dimethylsiloxane copolymer; vinylterminated diethylsiloxne-dimethylsiloxane copolymer;vinylmethylsiloxane-dimethylsiloxane copolymer, trimethylsiloxyterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, silanolterminated; vinylmethylsiloxane-dimethylsiloxane copolymers, vinylterminated; vinyl gums; vinylmethylsiloxane homopolymers; vinylT-structure polymers; monovinyl terminated polydimethylsiloxanes;vinylmethylsiloxane terpolymers; vinylmethoxysilane homopolymers andcombinations thereof.

In some embodiments, the organopolysiloxane is a compound of formulaIIb:

wherein R^(1c), R^(3c), R^(4c), R^(5c), R^(6c), R^(8c), R^(9c) andR^(10c) are each independently selected from hydrogen, C₁₋₂₀ alkyl,C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, hydroxyl or C₁₋₂₀ alkoxyl and e and f areeach independently an integer from between 10 and about 6000. In oneembodiment, R^(1c), R^(3c), R^(4c), R^(5c), R^(6c), R^(8c), R^(9c) andR^(10c) are alkyl (e.g., C₁ alkyl, such as methyl). In some embodiments,the sum of e and f is an integer from about 1000 to about 8000; fromabout 1300 to about 2700; from about 1500 to about 2700; from about 1600to about 2600; from about 1600 to about 2500; from about 1700 to about2500; from about 1800 to about 2400; from about 1800 to about 2300; fromabout 1900 to about 2300; from about 2000 to about 2200; from about 2050to about 2150; from about 2100.

In some embodiments, the organopolysiloxane is a compound of formulaIIc:

wherein R^(1d), R^(3d), R^(4d), R^(5d), R^(6d), R^(8d), R^(9d) andR^(10d) are each independently selected from hydrogen, C)_(—20) alkyl,C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, hydroxyl or C₁₋₂₀ alkoxyl and g and j areeach independently an integer from between 10 and about 6000. In oneembodiment, R^(1d), R^(3d), R^(4d), R^(5d), R^(6d), R^(8d), R^(9d) andR^(10d) are alkyl (e.g., C₁ alkyl, such as methyl). In some embodiments,the sum of g and j is an integer from about 200 to about 1100; fromabout 600 to about 1100; from about 700 to about 1000; from about 800 toabout 900; from about 825 to about 875; from about 850; from about 200to about 800; from about 225 to about 700; from about 250 to about 600;from about 275 to about 500; from about 300 to about 400; from about 350to about 400; from about 375. In some embodiments, the sum of g and j isan integer from about 850.

In some embodiments, the reactive constituent comprises at least onehydride functionalized polysiloxane. The language “hydridefunctionalized polysiloxane” includes compounds of formula III:

wherein R^(1b), R^(2b), R^(3b), R^(4b), R^(5b), R^(6b), R^(7b), R^(8b),R^(9b) and R^(10b) are each independently selected from hydrogen, C₁₋₂₀alkyl, C₂₋₂₀ alkenyl, C₅₋₁₀ aryl, hydroxyl or C₁₋₂₀ alkoxy and m and nare each independently an integer from between 10 and about 6000;provided that at least one of R^(1b), R^(2b), R^(3b), R^(4b), R^(5b),R^(6b), R^(7b), R^(8b), R^(9b) and R^(10b) is hydrogen. In someembodiments, at least one of R^(1b), R^(2b), R^(3b), R^(4b), R^(5b),R^(6b), R^(7b), R^(8b), R^(9b) and R^(10b) is hydrogen and the remainderare C₁₋₂₀ alkyl. In some embodiments, at least two of R^(1b), R^(2b),R^(3b), R^(4b), R^(5b), R^(6b), R^(7b), R^(8b), R^(9b) and R^(10b) arehydrogen (e.g., two Si—H units per functionalized hydride polysiloxanemolecule). In other embodiments, at least three of R^(1b), R^(2b),R^(3b), R^(4b), R^(5b), R^(6b), R^(7b), R^(8b), R^(9b) and R^(10b) arehydrogen (e.g., three Si—H units per functionalized hydride polysiloxanemolecule). In some embodiments, at least two of R^(1b), R^(2b), R^(3b),R^(4b), R^(5b), R^(6b), R^(7b), R^(8b), R^(9b) and R^(10b) are hydrogen(e.g., two Si—H units per functionalized hydride polysiloxane molecule)and the remainder are C₁₋₂₀ alkyl. In other embodiments, at least threeof R^(1b), R^(2b), R^(3b), R^(4b), R^(5b), R^(6b), R^(7b), R^(8b),R^(9b) and R^(10b) are hydrogen (e.g., three Si—H units perfunctionalized hydride polysiloxane molecule) and the remainder arealkyl. In some embodiments, at least two of R^(4b), R^(5b), R^(9b) andR^(10b) are hydrogen (e.g., two Si—H units per functionalized hydridepolysiloxane molecule) and the remainder are C₁₋₂₀ alkyl. In otherembodiments, at least three of R^(4b), R^(5b), R^(9b) and R^(10b) arehydrogen (e.g., three Si—H units per functionalized hydride polysiloxanemolecule) and the remainder are C₁₋₂₀ alkyl.

In one embodiment, at least greater than two monomer units of formulaIII include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, and R¹⁹ ishydrogen). For example, on average 2 to 15 monomer units of formula IIIinclude a Si—H unit. In one embodiment, at least two monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In one embodiment, at least three monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In one embodiment, at least four monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸ andR¹⁹ is hydrogen). In one embodiment, at least five monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In one embodiment, at least six monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In one embodiment, at least seven monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In one embodiment, at least eight monomer units offormula III include a —Si—H unit (e.g. one or more of R¹¹, R¹², R¹⁸, andR¹⁹ is hydrogen). In a specific embodiment, the non Si—H positions mayinclude a Si-(alkyl) or Si-(vinyl) unit. In a specific embodiment, thenon-Si—H positions are Si—CH₃. In one embodiment, the Si—H units in thehydride-functionalized organopolysiloxanes are separated by 5, 10, 15,20, 25, 30, 35, 40, 45, 50, 60, 65, 70, 75; 80, 85, 90, 100, 125, 150,or 200 monomer units.

In one aspect of any one of the above embodiments, the sum of m and n isan integer from about 10 to about 1300; from about 10 to about 1100;from about 10 to about 600; from about 15 to about 500; from about 15 toabout 400; from about 20 to about 300; from about 20 to about 200; fromabout 25 to about 100; from about 25 to about 75; from about 30 to about50; from about 40.

In some embodiments, the hydride functionalized polysiloxane includesSi—H units only at the terminal caps of the polymer. In someembodiments, the polysiloxane include Si—H units only in the monomerunits, but not at the terminal cap of the polymer. In other embodiments,the polysiloxane includes Si—H units at both the terminal cap or in themonomer unit of the polymer. In one embodiment, the polysiloxaneincludes two to twelve Si—H units located either at the terminal cap, orwithin the monomer unit, or a combination thereof. In one embodiment,the polysiloxane includes four to fifteen Si—H units located either atthe terminal cap, or within the monomer unit, or a combination thereof.In one embodiment, the polysiloxane includes eight Si—H units locatedeither at the terminal cap, or within the monomer unit, or a combinationthereof.

In some embodiments, the hydride functionalized polysiloxane has aviscosity of between about 5 and about 11,000 cSt or cP at 25° C., forexample, between about 10 and about 10,000 cSt or cP at 25° C., betweenabout 15 and about 5,000 cSt or cP at 25° C., between about 20 and about1,000 cSt or cP at 25° C., between about 25 and about 500 cSt or cP at25° C., between about 30 and about 100 cSt or cP at 25° C., and betweenabout 40 and about 50 cSt or cP at 25° C. In one embodiment, the hydridefunctionalized polysiloxane has a viscosity of about 45 cSt or cP at 25°C.

In some embodiments, the hydride functionalized polysiloxane has anaverage molecular weight of between about 900 and about 60,000 Da, forexample, between about 1000 and about 50,000 Da, between about 1200 andabout 25,000 Da, between about 1400 and about 20,000 Da, between about1600 and about 15,000 Da, between about 1800 and about 10,000 Da,between about 2000 and about 5000 Da, between about 2200 and about 4000Da, and between 2300 and about 2500 Da. In one embodiment, the averagemolecular weight of the hydride functionalized polysiloxane is about2400 Da.

In some embodiments, the hydride functionalized polysiloxane has apercent SiH content of between about 3 and about 45%, for example,between about 5 and about 40%, between about 10 and about 35%, betweenabout 20 and about 30%, or between about 26 and 27%. In someembodiments, the hydride functionalized polysiloxane has a percent SiHcontent of about 26%.

In some embodiments, the hydride functionalized polysiloxane has an SiHcontent of between about 0.500 mmol/g and about 10.00 mmol/g, forexample, between about 1.00 mmol/g and about 9.00 mmol/g, between about2.00 and about 8.00 mmol/g, between about 3.00 mmol/g and about 7.00mmol/g, and about 4.00 mmol/g and about 6.00 mmol/g. In one embodiment,the hydride functionalized polysiloxane has an SiH content of betweenabout 4.00 and about 5.00 mmol/g, for example, 4.35 mmol/g.

In other embodiments, the hydride functionalized polysiloxane is alkylterminated. The language “alkyl terminated” includes hydridefunctionalized polysiloxanes of formula III in which one or both ofR^(2h) and R^(7h) are C₁₋₂₀ alkyl. In some embodiments, “alkylterminated” includes hydride functionalized polysiloxanes of formula IIIin which one, two, three, four, five or six of R^(1b), R^(2b), R^(3b),R^(6b), R^(7b) and R^(8b) are C₁₋₂₀ alkyl. In one embodiment, R^(1b),R^(2b), R^(3b), R^(6b), R^(7b) and R^(8b) and R^(10b) are each C₁₋₂₀alkyl, for example, C₁ alkyl (e.g., methyl) and R^(9b) is hydrogen. Inone embodiment, R^(1b), R^(2b), R^(3b), R^(6b), R^(7b) and R^(8b) andR^(9b) are each C₁₋₂₀ alkyl, for example, C₁ alkyl (e.g., methyl) andR^(10b) is hydrogen.

In some embodiments, the hydride functionalized polysiloxane is selectedfrom the group consisting of hydride terminated polydimethylsiloxane;polyphenyl-(dimethylhydrosiloxy)siloxane, hydride terminated;methylhydrosiloxane-phenylmethylsiloxane copolymer, hydride terminated;methylhydrosiloxane-dimethylsiloxane copolymers, trimethylsiloxyterminated; polymethylhydrosiloxanes, trimethylsiloxy terminated;polyethylhydrosiloxane, triethylsiloxane,methylhydrosiloxane-phenyloctylmethylsiloxane copolymer;methylhydrosiloxane-phenyloctylmethylsiloxane terpolymer andcombinations thereof.

In some embodiments, the reactive constituent comprises combinations ofpolymers of formulas I, II, IIa, IIb, IIc, IId, and/or III. In aspecific embodiment, the reactive constituent comprises a combination ofpolymers of formulas IIa, IIb, IIc and/or III. In a specific embodiment,the reactive constituent comprises a combination of polymers of formulasIIb, IIc and III.

In some embodiments, the reactive constituent comprises combinations ofhigh molecular weight vinyl organopolysiloxanes, low molecular weightvinyl organopolysiloxanes, and/or hydride-functionalizedorganopolysiloxanes. In one embodiment, each of the high and lowmolecular weight organopolysiloxanes includes on average at least twovinyl moieties per polymer. In a specific embodiment, each vinylorganopolysiloxane includes exactly two vinyl moieties. In oneembodiment, the ratio of the high molecular organopolysiloxane to thelow molecular weight organopolysiloxane is 2 to 3, for example 2, 2.5 or3. The ratio may be selected in order to adjust the chemical andphysical properties of the film in order to suit a specific method orpart of the body. In one embodiment, the hydride-functionalizedorganopolymer includes on average greater than two Si—H units in thepolymer. In a specific embodiment, there are 8 Si—H units perhydride-functionalized organopolysiloxane.

In some embodiments, the reactive constituent comprises combinations ofhigh molecular weight hydride-functionalized organopolysiloxanes, lowmolecular weight hydride functionalized organopolysiloxanes, and/orvinyl organopolysiloxanes. In one embodiment, each of the high and lowmolecular weight organopolysiloxanes include on average at least twoSi—H units per polymer. In a specific embodiment, eachhydride-functionalized organopolysiloxane includes exactly two Si—Hmoieties. In one embodiment, the ratio of the high molecularorganopolysiloxane to the low molecular weight organopolysiloxane is 2to 3, for example 2, 2.5 or 3. The ratio may be selected in order toadjust the chemical and physical properties of the film in order to suita specific method or part of the body. In one embodiment, the vinylorganopolymer includes on average greater than at least two vinyl unitsin the polymer. In a specific embodiment, there are 8 vinyl units pervinyl organopolysiloxane.

The language “reinforcing constituent” includes one or more constituentsof the reactive reinforcing component that provide the required physicalproperties of the film that results from the in situ reaction betweenthe reactive reinforcing component and the cross-linking component. Suchphysical properties include, for example, mechanical elements (e.g.,elasticity, durability, fracture strain, tensile strength, etc. . . . ),biocompatibility (e.g., selective breathability, adhesion, etc. . . . ),optical effects (e.g., reflectance, color, etc. . . . ) and surfacemodulation (e.g., texture, chemistry, etc. . . . ). Examples ofreinforcing constituents include clays, (e.g., Al₂O₃, SiO₂), chalk,talc, calcite (e.g., CaCO₃), mica, barium sulfate, zirconium dioxide,zinc sulfide, zinc oxide, titanium dioxide, aluminum oxide, silicaaluminates, calcium silicates, or optionally surface treated silica(e.g., fumed silica, hydrated silica or anhydrous silica). In someembodiments, reinforcing constituent is silica, for example, surfacetreated silica, such as silica treated with hexamethyldisilazane.

In some embodiments, the reinforcing constituent has a surface area ofbetween about 100 and about 300 m²/g, for example, between about 110 andabout 250 m²/g, between about 120 and about 225 m²/g, between about 130and about 200 m²/g, between about 135 and about 185 m²/g, between about160 and about 170 m²/g, and between about 164 and about 166 m²/g. In oneembodiment, the reinforcing constituent has a surface area of about160±25 m²/g.

In some embodiments, the reinforcing constituent has an average particlesize of between about 1 and about 20 μm.

In some embodiments, the reinforcing constituent is compounded with thelow viscosity and/or the high viscosity organopolysiloxane.

In some embodiments, reactive constituent and reinforcing constituentcomprise between about 20 and about 90% of the reactive reinforcingcomponent, for example, between about 40% and about 60% of the reactivereinforcing component. In some embodiments, the reactive constituent andreinforcing constituent comprise between about 45.0 and about 61.0% ofthe reactive reinforcing component, for example, about 45.0%, about45.5%, about 46.0%, about 46.5%, about 47.0%, about 47.5%, about 48.5%,about 49.0%, about 49.5%, about 50.0%, about 50.5%, about 51.0%, about51.5%, about 52.0%, about 52.5%, about 53.0%, about 53.5%, about 54.0%,about 54.5%, about 55.0%, about 55.5%, about 56.0%, about 56.5%, about57.0%, about 58.0%, about 58.5%, about 59.0%, about 59.5%, about 60.0%,or about 60.5%. In some embodiments, the reactive constituent and thereinforcing constituent comprise about 45% of the reactive reinforcingcomponent. In one embodiment, the reactive constituent and reinforcingconstituent comprise about 48.0% of the reactive reinforcing component.In some embodiments, the reactive constituent and the reinforcingconstituent comprise about 50.0% of the reactive reinforcing component.In another embodiment, the reactive constituent and reinforcingconstituent comprise about 51.0% of the reactive reinforcing component.In some embodiments, the reactive constituent and the reinforcingconstituent comprise about 51.5% of the reactive reinforcing component.In another embodiment, the reactive constituent and reinforcingconstituent comprise about 54.5% of the reactive reinforcing component.In another embodiment, the reactive constituent and reinforcingconstituent comprise about 55.0% of the reactive reinforcing component.In some embodiments, the reactive constituent and the reinforcingconstituent comprise about 59.5% of the reactive reinforcing component.In another embodiment, the reactive constituent and reinforcingconstituent comprise about 60.5% of the reactive reinforcing component.In some embodiments, the reactive constituent and reinforcingconstituent comprise between about 30.0 and about 40.0% of the reactivereinforcing component, for example, about 30.0%, about 30.5%, about31.0%, about 31.5%, about 32.0%, about 32.5%, about 33.0, about 33.5%,about 34.0%, about 34.5%, about 35.0%, about 35.5%, about 36.0%, about36.5%, about 37.0%, about 37.5%, about 38.0%, about 38.5%, about 39.0%,about 39.5%, about 40.0%. In some embodiments, the reactive constituentand reinforcing constituent comprise between about 33.0 and about 40.0%of the reactive reinforcing component

In one embodiment, the reinforcing constituent comprises between about8.0 and about 13.0% of the reactive reinforcing component, for example,about 8.5%, about 9.0%, about 9.5%, about 10.0%, about 10.5%, about11.0%, about 11.5%, about 12.0% or about 12.5%. In some embodiments, thereinforcing constituent comprises about 8.5% of the reactive reinforcingcomponent. In one embodiment, the reinforcing constituent comprisesabout 9.0% of the reactive reinforcing component. In another embodiment,the reinforcing constituent comprises about 9.5% of the reactivereinforcing component. In some embodiments, the reinforcing constituentcomprises about 10.0% of the reactive reinforcing component. In someembodiments, the reinforcing constituent comprises about 10.5% of thereactive reinforcing component. In another embodiment, the reinforcingconstituent comprises about 11.0% of the reactive reinforcing component.In another embodiment, the reinforcing constituent comprises about 12.0%of the reactive reinforcing component. In another embodiment, thereinforcing constituent comprises about 13.0% of the reactivereinforcing component.

In another embodiment, the reactive constituent comprises between about30.0 and about 60.0% of the reactive reinforcing component, for example,about 30.5%, about 31.0%, about 32.0%, about 33.0%, about 34%, about35.0%, about 36.0%, about 37.0%, about 38.0%, about 39.0%, about 40.0%,about 41.0%, about 42.0%, about 43.0%, about 44.0%, about 45.0%, about46.0%, about 47.0%, about 48.0%, about 49.0%, about 50.0%, about 51.0%,about 52.0%, about 53.0%, about 54.0%, about 55.0%, about 56.0%, about57.0%, about 58.0% or about 59.0%.

In some embodiments, the reactive reinforcing component has a viscosityof between about 5,000 and 1,000,000 cSt or cP at 25° C. In someembodiments, the reactive reinforcing component has a viscosity ofbetween about 10,000 and 10,000,000 cSt or cP at 25° C., for example,about 10,000,000, about 9,000,000, about 8,000,000, about 7,000,000,about 6,000,000, about 5,000,000, about 4,000,000, about 3,000,000 orabout 2,000,000, about 1,000,000, about 900,000, about 800,000, about700,000, about 600,000, about 500,000, about 400,000, about 300,000,about 200,000, about 100,000, about 90,000, about 80,000, about 70,000,about 60,000, about 50,000, about 40,000, about 30,000, about 20,000,about 10,000 cSt. In one embodiment, the reactive reinforcing componenthas a viscosity of about 1,000,000 cSt.

In some embodiments, the reactive reinforcing component has a vinyl tofunctional hydride (e.g., —CH═CH₂ of the one or more organopolysiloxanesto Si—H of the hydride functionalized polysiloxane) ratio of betweenabout 1:10 and about 1:100, for example, between about 1:15 and about1:90, between about 1:20 and about 1:80, between about 1:25 and about1:70, between about 1:30 and about 1:60, between about 1:35 and about1:50. In one embodiment, the reactive reinforcing component has a vinylto functional hydride ratio of about 1:40. In another embodiment, thereactive reinforcing component has a vinyl to functional hydride ratioof about 1:20. In some embodiments, the reactive reinforcing componenthas a vinyl to functional hydride ratio of about 1:15.

The language “cross-linking component” includes a component that, whenapplied to the reactive reinforcing component, catalyzes the in situformation of the body corrective film.

The term “catalyzes the in situ formation of the body corrective film”includes causing a reaction to occur between the reactive constituentsof the reactive reinforcing component, such that a body corrective filmis formed on the skin. Without being bound by theory, the cross-linkingcomponent induces a reaction between the one or more organopolysiloxanesand the hydride functionalized polysiloxane of the reactive reinforcingcomponent causing the condensation of these constituents, such that afilm is formed upon the skin.

In some embodiments, the cross-linking component comprises a metalcatalyst, for example, a platinum catalyst, a rhodium catalyst or a tincatalyst. Examples of platinum catalysts include, for example, platinumcarbonyl cyclovinylmethylsiloxane complexes, platinumdivinyltetramethyldisiloxane complexes, platinumcyclovinylmethylsiloxane complexes, platinum octanaldehyde/octanolcomplexes and combinations thereof. An example of a rhodium catalystincludes Tris (dibutylsulfide) Rhodium trichloride. Examples of tincatalysts include tin II octoate, Tin II neodecanoate, dibutyltindiisooctylmaleate, Di-n-butylbis(2,4 pentanedionate)tin,di-n-butylbutoxychlorotin, dibutyltin dilaurate, dimethyltindineodecanoate, dimethylhydroxy(oleate)tin and tin II oleate.

In some embodiments, the cross-linking component further comprises avinyl terminated organopolysiloxane (e.g., a compound of Formula I, IIIIa, IIb or IIc). In some embodiments, the amount of vinyl-terminatedpolysiloxane is a stabilizing amount of vinyl-terminated polysiloxane.The language “stabilizing amount” includes an amount that prevents thedegradation of the catalyst and/or the crosslinking component and/or thebody corrective film. In some embodiments, the stabilizing amount ofvinyl-terminated polysiloxane is less than about 50%, less than about40%, less than about 30%, less than about 20%, less than about 10%, lessthan about 5% or less than about 2%. In some embodiments, thestabilizing amount of vinyl-terminated polysiloxane is about 1%.

In some embodiments, the cross-linking component has a viscosity ofbetween about 1,000 and about 50,000 cSt or cP at 25° C.

In some embodiments, the catalyst is added as a solution and thesolution comprises between about 1.0 and about 5.0% of the cross-linkingcomponent, for example, about 1.5%, about 2.0%, about 2.5%, about 3.0%,about 3.5%, about 4.0% or about 4.5%. In one embodiment, the catalyst isabout 2.0% of the cross-linking component.

In some embodiments, the catalyst comprises between about 0.005 andabout 0.04% of the cross-linking component, for example, about 0.005%,about 0.010%, about 0.015%, about 0.020%, about 0.025%, about 0.030% orabout 0.035% or about 0.040%. In one embodiment, the catalyst is about0.02% of the cross-linking component.

In some embodiments, the catalyst is present in the cross-linkingcomponent in an amount of between about 100 ppm and about 500 ppm.

In some embodiments; the reactive reinforcing component and thecross-linking component are prevented from coming into contact prior touse. The reactive reinforcing component and the cross-linking componentcan be kept from coming into contact prior to use by usual means knownto one of skill in the art. In one embodiment, the skin correctiveformulation is a two part formulation in which the reactive reinforcingcomponent and said cross-linking component are packaged in separatecontainers and mixed prior to use. In another embodiment, the reactivereinforcing component is applied to the skin first, and thecross-linking component is applied on top of the reactive reinforcingcomponent. In yet another embodiment, the cross-linking component isapplied to the skin first and the reactive reinforcing component isapplied on top of the cross-linking component. In a further embodiment,the reactive reinforcing component and the cross-linking component arepackaged together in the same container with a barrier between the twocomponents, and are mixed when the components are extracted from thecontainer.

The term “body” includes any part of the subject's body that can benefitfrom the formulations disclosed herein. Examples of the subject's bodyinclude the skin, the neck, the brow, the jowls, the eyes, the hands,the feet, the face, the cheeks, the breasts, the abdomen, the buttocks,the thighs, the back, the legs, the ankles, cellulite, fat deposits, andthe like.

The term “skin” includes the epidermis of the subject's skin, which isthe outer layer of the skin and includes the stratified squamousepithelium composed of proliferating basal and differentiated suprabasalkeratinocytes.

The term “subject” includes subjects in which the formulations disclosedherein would be appropriate for use. In one example, the subject is amammal, for example, a human. In another embodiment, the subject issuffering from skin imperfections, body imperfections, or has recentlyundergone a cosmetic procedure. In another embodiment, the subjectdesires to look younger or wishes to enhance his/her body.

In one embodiment, the body corrective formulation further comprises oneor more of feel modifiers, tack modifiers, spreadability enhancers,diluents, adhesion modifiers, optics modifiers, particles, volatilesiloxanes, emulsifiers, emollients, surfactants, thickeners, solvents,film formers, humectants, preservatives, pigments, cosmetic agents ortherapeutic agents. In other embodiments, the reactive reinforcingcomponent and/or the cross-linking component further comprise one ormore of feel modifiers, tack modifiers, spreadability enhancers,diluents, adhesion modifiers, optics modifiers, particles, volatilesiloxanes, emulsifiers, emollients, surfactants, thickeners, solvents,film formers, humectants, preservatives, pigments, cosmetic agents ortherapeutic agents. One of skill in the art could readily determinefurther appropriate additives based on the INCI dictionary, which isincorporated herein by reference in its entirety.

Examples of cosmetic or therapeutic agents include sunscreens (forexample, UV protecting agents) anti-aging agents, anti-acne agents,anti-wrinkle agents, spot reducers, moisturizers, anti-oxidants,vitamins.

In some embodiments, the emulsifier is SIMULGEL™ 400.

In some embodiments, the composition or film is administered first,followed by administration of the one or more additional cosmetic ortherapeutic agents. In some embodiments, the composition or film isadministered after the one or more additional cosmetic or therapeuticagents. In some embodiments, the film and the one or more additionalcosmetic or therapeutic agents are administered substantially at thesame time. In some embodiments, the composition or film is used todeliver the one or more additional cosmetic or therapeutic agents.

In some embodiments, a finishing formulation may be applied to the bodycorrective formulation during or after formation of the film on thebody. The term “finishing formulation” includes a composition comprisingcomponents that provide a desired tactile sensation or a desiredaesthetic look to the film after formation. For example, the finishingformulation may provide a silky, soft and/or smooth tactile sensation ora dewy, fresh, matte, shiny or luminescent aesthetic look afterapplication to the film.

In some embodiments, the finishing formulation comprises one or more ofoils, esters or ethers, for example, triglycerides, PPG-3 benzyl ethermyristate, Schercemol DISD ester, or particles, for example, nylon,silica and silicone elastomer beads. In some embodiments, the one ormore of these components comprise from about 0.5% to about 100% of thefinishing formulation.

In some embodiments, the finishing formulation is a cream, spray, foam,ointment, serum, gel or powder.

In some embodiments, the finishing formulation further comprises one ormore f feel modifiers, tack modifiers, spreadability enhancers,diluents, adhesion modifiers, optics modifiers; particles, volatilesiloxanes, emulsifiers, emollients, surfactants, thickeners, solvents,film formers, humectants, preservatives, pigments, dyes (e.g.,fluorescent dyes), cosmetic agents or therapeutic agents.

In some embodiments, the films and formulations described hereincomprise one or more pigments. The include natural or non-naturalcoloring agents or dyes. In one embodiment, the pigments are fluorescentdyes.

In some embodiments, the films and formulation further comprise apigment dispersion formulation. The language “pigment dispersionformulation” includes a formulations that are capable of providing oneor more pigments to the films or formulations as a separate component ofthe formulation or film. In some embodiments, the pigment dispersionformulation allows for an even distribution of the pigment in the filmsand formulations. In some embodiments, the pigment dispersionformulation comprises at least one reactive constituent. In someembodiments, the pigment dispersion formulation comprises at least onereinforcing constituent. In some embodiments, the pigment dispersionformulation comprises one or more of feel modifiers, tack modifiers,spreadability enhancers, diluents, adhesion modifiers, optics modifiers,particles, volatile siloxanes, emulsifiers, emollients, surfactants,thickeners, solvents, film formers, humectants, preservatives, pigments,cosmetic agents or therapeutic agents. In other embodiments, thereactive reinforcing component and/or the cross-linking componentfurther comprise one or more of feel modifiers, tack modifiers,spreadability enhancers, diluents, adhesion modifiers, optics modifiers,particles, volatile siloxanes, emulsifiers, emollients, surfactants,thickeners, solvents, film formers, humectants, preservatives, pigments,cosmetic agents or therapeutic agents.

In some embodiments, the pigment dispersion formulation is applied priorto or after the application of the reactive reinforcing component to theskin. In some embodiments, the pigment dispersion formulation is appliedprior to or after the application of the cross-linking component to theskin. In some embodiments, the pigment dispersion formulation is appliedin between the application of the reactive reinforcing component and thecross-linking component to the skin.

In some embodiments, the pigment dispersion formulation may be appliedto skin that has not been subjected to the application of a bodycorrective formulation or film. For example, a subject may apply thepigment dispersion formulation to the skin in the area around the bodycorrective film or formulation, or the subject may apply the pigmentformulation to the skin in lieu of applying the body corrective film orformulation.

The terms “apply,” “applied” and “application” includes methods toadminister the formulations disclosed herein to a subject's body, suchas application by fingers, brush, cotton ball, pad, spray, sponge,cotton swab, roll-on and the like. One of skill in the art can readilydetermine appropriate methods to apply the formulations disclosedherein.

In some embodiments, the invention pertains, at least in part, to a kitcomprising a body corrective formulation comprising a reactivereinforcing component and a cross-linking component. In someembodiments, the kit is a multi-compartment kit comprising at least twocompartments in which one compartment comprises the reactive reinforcingcomponent and the second compartment comprises the cross linkingcomponent. In some embodiments, the kit further comprises instructionsfor use of the kit, one or more brushes, one or more swabs, a filmremoving cleanser or a mirror. In some embodiments, the kit furthercomprises one or more finishing formulations.

In some embodiments, the invention pertains, at least in part, to a bodycorrective film prepared by a process comprising the steps of applying areactive reinforcing component to the body; and applying a cross-linkingcomponent to the reactive reinforcing component, in which thecross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component.

In some embodiments, the invention pertains, at least in part, to a bodycorrective film prepared by a process comprising the steps of applying across-linking component to the body; and applying a reactive reinforcingcomponent to the cross-linking component, in which the cross-linkingcomponent catalyzes an in situ cross-linking of the reactive reinforcingcomponent.

The language “body corrective film” includes films that are formed uponthe reaction of the reactive reinforcing component and the cross-linkingcomponent and that, upon formation, ameliorate one or more bodyimperfections. In some embodiments, the body corrective film is a skincorrective film (e.g., a film that ameliorates one or more skinimperfections).

In some embodiments, the body corrective film has an appearance ofnatural skin upon application to the skin. The language “appearance ofnatural skin” includes the perception that the body corrective film,when applied to the skin, has the look, feel and texture of real skinand that the film treated skin has the physical properties (e.g., theelasticity and stiffness) of real (e.g., live) skin. A trained observerand/or a technician would be able to determine whether the film uponapplication to the body has the appearance of natural skin. For example,a trained observer would be able to determine whether the film, uponapplication to the body, appears excessively shiny, as described inExample 3, or whether the film appears not to move with the underlyingmusculature of the skin by, for example, breaking, buckling ordeforming, in response to natural skin motion.

A technician would be able to determine whether the film has theappearance of natural skin upon application to the body. For example,the elasticity and stiffness of skin, with or without the bodycorrective film applied to it, can be assessed by a wide variety ofmethods (Agache et al., Arch. Dermatol. Rev., 269 (1980) 221, theteachings of which are incorporated herein by reference). For example,the DermaLab suction cup instrument provides one common method to assessthe mechanical properties of skin, and has previously shown younger skinto be less stiff and more elastic than aged skin (Grahame et al.Clinical Science 39 (1970) 223-238, the teachings of which areincorporated herein by reference). With this method, the stiffness ofthe skin is indicated by the Young's Modulus, a measure calculated bythe instrument based on the pressure required to suck skin up apredetermined distance.

In some embodiments, the Young's Modulus of the skin treated with a bodycorrective formulation is reduced by between about 5% to about 70%, forexample, between about 30% and about 60%, or between about 40% and about50% compared to untreated skin. In some embodiments, the Young's Modulusof skin treated with a body corrective formulation is reduced by betweenabout 5% and about 25% compared to untreated skin.

The elasticity of the skin is determined by the skin retraction time.The retraction time is obtained by measuring the time it takes for theskin to drop a predetermined distance towards its natural position,after the suction pressure is removed. In some embodiments, theretraction time of skin treated with a body corrective formulation isdecreased by between about 5% and about 75%, for example, between about30% and about 60%, or about 50% and about 65% when compared to untreatedskin. In some embodiments, the retraction time of skin treated with abody corrective formulation is decreased by between about 5% and about10% compared to untreated skin. In some embodiments, the retraction timeof the skin treated with the film approaches the retraction time of thefilm alone.

The skin of the bicep and hand was evaluated before and after the bodycorrective treatment was applied, as shown in FIGS. 1 and 2. TheDermaLab results confirmed that the skin was less stiff (FIG. 1) andmore elastic (FIG. 2) after product application. The observed reductionin stiffness and the increase in skin elasticity are consistent withskin being more youthful.

In some embodiments, the body corrective film, upon application to theskin, has the appearance and physical properties of youthful,unblemished natural skin. The language “youthful skin” includes skinthat has mild or no damage, as measured by the Griffith's score. TheGriffith's score (GS), as shown below, is a quantitative measurement ofthe amount of skin damage subject has.

-   -   0-1: No damage    -   2-3: Mild damage    -   4-5: Moderate damage    -   6-7: Moderate to severe damage    -   8-9: Severe damage

In some embodiments, youthful skin includes skin that has a Griffith'sscore of between about 0 and about 3.

In some embodiments, the subject has a negative change in Griffith'sscore (ΔGS) of about 1, about 2, about 3, about 4, about 5, about 6,about 7 or about 8 after application of the body corrective formulation.In some embodiments, the subject has a ΔGS of between about −0.5 andabout −3.0 upon application of the body corrective formulation. In oneembodiment, the subject has a ΔGS between about −1 and about −1.5,between about −1.2 and about −1.3 (e.g., about −1.25) upon applicationof the body corrective formulation. In another embodiment, the subjecthas a ΔGS of between about −2.0 and about −3.0, for example, betweenabout −2.0 and about −2.5, or between about −2.1 and about −2.2 (e.g.,about −2.15) upon application of the body corrective formulation.

One of skill in the art would be able to determine whether the film,upon application to the body, has the appearance of youthful,unblemished natural skin by the methods disclosed in Example 6.

In other embodiments, the film, upon application to the skin, providesstiffness and elasticity such that the skin treated with the film appearsubstantially more similar to youthful skin than untreated skin. Theterm “elasticity” includes the skin's tendency to return to its originalshape once it's been deformed. The language “elasticity substantiallysimilar to youthful skin” includes the ability of the skin to return toits original shape once it's been deformed in a manner similar to thatof young skin. The term “stiffness” includes the skin's resistance todeformation. The language “stiffness substantially similar to youthfulskin” includes the ability of the skin to resist deformation in a mannersimilar to that of young skin. A technician would also be able todetermine whether the film, upon application to the body, has theaforementioned physical properties of youthful, unblemished, naturalskin by the techniques described above (e.g., using the Dermalab suctioncup instrument).

In some embodiments, the subject and/or observers of the subjectperceive an age reduction upon application of the body correctionformulation. In some embodiments, the perceived age reduction is about 1year, about 2 years, about 3 years, about 4 years, about 5 years, about6 year, about 7 years, about 8 years, about 9 years, about 10 years,about 11 years, about 12 years, about 13 years, about 14 years or about15 years less than the subject's actual age. In some embodiments, theperceived age reduction is about 7.5 years less than the subject'sactual age upon application of the body corrective formulation. In otherembodiments, the perceived age reduction is about 8.5 years less thanthe subject's actual age upon application of the body correctiveformulation.

The language “the film is formed” and “film formation” includes theresults of the polymerization reaction that occurs upon the interactionof the reactive reinforcing component and the cross-linking component.Without being bound by theory, film formation is characterized by aphase transition from the viscous sol state of a mixture to that of acontinuous interconnected polymer state of film.

A technician could determine when the film is formed on the body byusing routine methods. For example, rheological measurements using smallamplitude oscillatory shear can determine the continuous evolution ofthe viscoelastic properties, such as elastic modulus (G′), the viscousmodulus (G″) and the loss of tangent (tan 6) of the reacting mixturecontinuously through the film formation process. In some embodiments,the rheometer can be used to determine the cross over time between G′and G″ and the time when tan δ becomes frequency independent, which is ameasure of film formation. In some embodiments; the film is formedwithin at least about five minutes, for example, within about oneminute, about two minutes, about three minutes or about four minutes. Insome embodiments, the film is formed within at least about 10 secondsand about 3 minutes.

In some embodiments, the skin or body corrective film has a Young'sModulus (e.g., tensile strength) of between about 0.01 and about 1 MPa,as illustrated in Example 1.

In some embodiments, the fracture strain of the skin or body correctivefilm has a fracture strain of at least about 150%, as measured byExample 1.

In some embodiments, the skin or body corrective film has a leatheradhesive force of greater than about 20 N/mm, for example, greater thanabout 25 N/mm, greater than about 30 N/mm, greater than about 35 N/mm,greater than about 40 N/mm, greater than about 45 N/mm, greater thanabout 50 N/mm, greater than about 55 N/mm, greater than about 60 N/mm,greater than about 65 N/mm, greater than about 70 N/mm, greater thanabout 75 N/mm, or greater than about 80 N/mm, as determined by theleather adhesion test illustrated in Example 2. In one embodiment, theleather adhesive force is between about 50 and about 80 N/mm, asdetermined by the leather adhesion test illustrated in Example 2.

In some embodiments, the skin or body corrective film has a hysteresisof less than about 10% for example, least than about 9%, less than about8%, less than about 7%, less than about 6%, less than about 5%, lessthan about 4%, less than about 3%, less than about 2%, less than 1% orabout 0%.

In some embodiments, the skin or body corrective film is between about10 μm and about 1500 μm thick, for example, between about 50 μm andabout 500 μm thick. In some embodiments, the film is less than about 100μm thick. The film thickness may be measured by methods known to one ofskill in the art, for example, by the combination of calipers and acalibrated microscope. The thickness of the film may also be digitallymeasured from a micrograph of the film cross-section. The microscopecalibration allows for the conversion of measured pixelar distance intometric distance units.

In some embodiments, the skin or body corrective film shrinks by lessthan between about 1 and 30%, for example, between about 1 to about 15%.The amount of shrinking may be determined by methods known to one ofskill in the art, for example, by the Croll method (Croll, S. G. J.Coatings Tech. 52 (1980) 35, the teachings of which are incorporatedherein by reference). In this method the film is used to coat one sideof a thin flexible substrate. The amount of curve developed in thesubstrate due to the shrinking of the coating is used to calculate themagnitude of shrinking of the coating (Francis et al., J Mater Sci 2002;37:4717-31, the teachings of which are incorporated herein byreference.)

In some embodiments, the body corrective films are physiologicallystable. The language “physiologically stable” includes the durability ofthe film upon exposure to normal skin conditions, for example, humidity,tears, sweat or sebum. The physiological stability may be determined bymethods typically used by one of ordinary skill in the art, such as anuptake test, which measures the change in weight of the film afterexposure to a physiological factor. For example, the uptake test mayemploy a formulation of simulated sweat (e.g., 1× phosphate bufferedsaline solution) or simulated sebum (e.g., 25% wax monoesters, 41%triglycerides, 16% free fatty acids and 12% squalene). In someembodiments, the weight of the film increases by less than about 10%,for example, less than about 9%, less than about 8%, less than about 7%,less than about 6%, less than about 5%, less than 4%, less than 3%, lessthan 2%, less than 1% or exhibits no increase upon exposure to humidity,tears, sweat or sebum.

In some embodiments, the invention pertains, at least in part, tomethods for correcting body imperfections in a subject comprisingapplying to the subject a formulation comprising a) a first reactivereinforcing component; and a second cross-linking component; in whichthe cross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component, such that a film is formed on the skin,thereby correcting body imperfections. The language “correcting bodyimperfections” includes ameliorating (e.g., partially or completely) oneor more body imperfections, either permanently or temporarily (e.g., forthe duration that the film is left on the skin). One of skill in the artwould be able to determine whether the body imperfections are corrected,either partially or completely, upon application of the body correctiveformulation to the body by the techniques described in Example 6.

In some embodiments, the language “correcting body imperfections”includes reducing the appearance of body imperfections in a subjectcomprising applying to the subject a formulation comprising a) a firstreactive reinforcing component; and b) a second cross-linking component;in which the cross-linking component catalyzes an in situ cross-linkingof the reactive reinforcing component, such that a film is formed on theskin, thereby reducing the appearance of skin or body imperfections. Thelanguage “reducing the appearance of body imperfections” includes thediminishment of one or more outward aspects of one or more bodyimperfections. In some embodiments, the appearance of the bodyimperfections upon application of the body corrective formulation to thesubject are reduced by about 100%, by about 95%, by about 90%, by about85%, by about 80%, by about 75%, by about 70%, by about 65%, by about60%, by about 55%, by about 50%, by about 45%, by about 40%, by about35%, by about 30%, by about 25%, by about 20%, by about 10% or by about5% compared to the untreated subject.

In some embodiments, the language “correcting body imperfections”includes masking body imperfections in a subject comprising applying tosaid subject a formulation comprising a) a first reactive reinforcingcomponent; and b) a second cross-linking component; wherein saidcross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component; such that a film is formed on the skin,thereby masking the appearance of body imperfections. The language“masking body imperfections” includes concealing or obscuring from view,either partially or completely, one or more body imperfections. In someembodiments, the method provides for masking body imperfections on asubject following a cosmetic procedure, comprising applying to the skinwhere the cosmetic procedure was performed a formulation comprising a) afirst reactive reinforcing component; and b) a second cross-linkingcomponent; wherein said cross-linking component catalyzes an in situcross-linking of the reactive reinforcing component, such that a film isformed on the skin, thereby masking the appearance of bodyimperfections. Examples of cosmetic procedures include, for example,cosmetic surgery (e.g., eye lift, face lift, tummy tuck and the like) orBotox® injections. In some embodiments, skin imperfections are masked.In some embodiments, the body imperfections after application of thebody correcting formulation are masked by about 5%, by about 10%, byabout 15%, by about 20%, by about 25%, by about 30%, by about 35%, byabout 40%, by about 45%, by about 50%, by about 55%, by about 60%, byabout 65%, by about 70%, by about 75%, by about 80%, by about 85%, byabout 90%, by about 95% or by about 100% compared to the untreated bodyimperfections.

In some embodiments, the language “correcting body imperfections”includes improving the appearance of a subject's body, comprisingapplying to said subject a formulation comprising a) a first reactivereinforcing component; and b) a second cross-linking component; whereinsaid cross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component, such that a film is formed on the skin,thereby improving the appearance of the body. The language “improvingthe appearance of a subject' body” includes enhancing the outward aspectof the body. Examples of improving the appearance of the body includereducing or masking the appearance of port wine stain or nevus flammeus(e.g., nevus flammeus nuchae or midline nevus flammeus) melasma,wrinkles, scars, moles, acne, skin disfigurements, birth marks, burnwounds, blemishes or pores, evening skin tone, reducing or maskingshine, lifting sagging skin, or reducing or masking the appearance ofcellulite or stretch marks. In some embodiments, the appearance of thesubject's skin is improved.

In some embodiments, the language “correcting body imperfections”includes enhancing the body of a subject, comprising applying to thesubject's body a formulation comprising a) a first reactive reinforcingcompound; and b) a second cross-linking component, in which thecross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component, such that a film is formed on the skin,thereby enhancing the subject's body. The language “enhancing the body”includes augmenting or heightening the features of a subject's body suchthat the subject's appearance is more attractive. For example, asubject's body may be enhanced by the addition of colorants, glitter andthe like. In some embodiments, the appearance of the subject's skin isenhanced.

In some embodiments, the invention pertains, at least in part, tomethods of reducing the appearance of a subject's age comprisingapplying to the subject a formulation comprising a) a first reactivereinforcing component; and b) a second cross-linking component; in whichthe cross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component such that a film is formed on the skin,thereby reducing the appearance of a subject's age. The language“reducing the appearance of a subject's agent” includes the perceptionby the subject or those viewing the subject that the subject is youngerupon application of the body corrective film to the subject. In someembodiments, the subject appears about 1 year, about 2 years, about 3years, about 4 years, about 5 years, about 6 years, about 7 years, about8 years, about 9 years, about 10 years, about 11 years, about 12 years,about 13 years, about 14 years, about 15 years, about 16 years, about 17years, about 18 years, about 19 years or about 20 years younger uponapplication of the body corrective film.

In some embodiments, the invention pertains, at least in part, tomethods for protecting a subject's body comprising applying to thesubject a formulation comprising a) a first reactive reinforcingcomponent; and b) a second cross-linking component; in which thecross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component such that a film is formed on the skin,thereby protecting the body. The language “protecting a subject's body”includes preserving or shielding a subject's skin or body from damagingenvironmental elements, for example, damage by the sun, wind, rain orenvironmental toxins. In some embodiments, the subject's skin isprotected.

In some embodiments, the invention pertains, at least in part, tomethods for shaping a subject's body, comprising applying to the subjecta formulation comprising:

a) a first reactive reinforcing component; and b) a second cross-linkingcomponent; in which the cross-linking component catalyzes an in situcross-linking of the reactive reinforcing component such that a film isformed on the skin, thereby shaping or the body. The language “shaping asubject' body” includes altering the body of a subject, for example, byproviding support to soft body tissues and preventing sagging of softbody tissues. Examples of soft body tissues include the abdomen, thebuttocks, the thighs, the neck, the brow, the jowls, the breasts, theskin under the arms, and the skin surrounding the eyes. In someembodiments, the subject' skin is shaped.

In some embodiments, the language “shaping a subject's body” includesstructurally altering by, for example, redistributing a portion of thesubject's body, comprising applying to the subject a formulationcomprising a) a first reactive reinforcing component; and b) a secondcross-linking component; in which the cross-linking component catalyzesan in situ cross-linking of the reactive reinforcing component such thata film is formed on the skin, thereby shaping the body. In someembodiments, a portion of the subject's body is lifted, for example, thebreasts, the skin, the buttocks, and the like. The language “lifting asubject's body” includes raising the subject's body, for example, in amanner similar to a surgical cosmetic procedure (e.g., a face lift, aneye lift, a breast lift and the like). In some embodiments, thesubject's skin is lifted. In some embodiments, the skin is facial skin(e.g., the skin around the eyes, the skin on the brow or the skinsurrounding the lips) or neck skin. In some embodiments, uponapplication of the body corrective formulation, the body is lifted byabout 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about35%, about 40% or by about 50% compared to the Subject's untreated body.In some embodiments, the body is lifted by about 1 mm, about 2 mm, about3 mm, about 4 mm, about 5 mm, about 6 mm, about 7 mm, about 8 mm, about9 mm, about 1 cm, about 1.5 cm, about 2.0 cm, about 2.5 cm, about 3.0cm, about 3.5 cm, about 4.0 cm, about 4.5 cm, about 5.0 cm, about 5.5cm, about 6.0 cm, about 6.5 cm, about 7.0 cm, about 7.5 cm, about 8.0cm, about 8.5 cm, about 9.0 cm, about 9.5 cm or about 10 cm uponapplication of the body corrective film.

In some embodiments, the invention pertains, at least in part, to amethod for delivering an agent to a subject, comprising applying to thesubject's skin a formulation comprising a) a first reactive reinforcingcomponent optionally comprising one or more agents; and b) a secondcross-linking component optionally comprising one or more agents; inwhich the cross-linking component catalyzes an in situ cross-linking ofthe reactive reinforcing component such that a film is formed on theskin, thereby delivering the agent to the subject. The language“delivering an agent” includes releasing an agent (e.g., a cosmetic ortherapeutic agent) to the skin of subject upon formation of the film onthe subject's skin. In some embodiments, the agent is delivered in oneportion, or the agent is formulated to be delivered in a time-releasemanner. Examples of agents include cosmetic agents and therapeuticagents.

In some embodiments, the invention pertains, at least in part, to a bodycorrective formulation for application to a subject's body, comprisingat least one preselected function modulating component, wherein saidcomposition forms a body corrective film upon application to thesubject's body.

The term “preselected” includes components that are chosen prior to thepreparation of the formulation. For example, the components may bechosen during the manufacturing process to create a specificformulation. Alternatively, the components may be chosen by the subjectprior to application of the formulation.

The language “function modulating component” includes components thatallow

the body corrective formulations to, be selectively adjusted for aparticular use of the film (e.g., reducing the appearance of wrinkles,minimizing shine, masking pores, etc.). The function modulatingcomponent or components may be selected based on the physical propertiesof the film that are necessary to be effectively applied for aparticular use of the film. For example, if the formulation will be usedto minimize shine, the modulus should be low relative to the values ofthe other physical properties of the resulting film.

In some embodiments, the invention pertains, at least in part, to a bodycorrective formulation that targets a treatment area on a subject'sbody, comprising at least one preselected treatment specific component,wherein said composition forms a body corrective film upon applicationto the target treatment area on the subject's body.

The language “target treatment area” includes an area of the body wherethe formulation is meant to be applied.

The language “treatment specific component” includes components thatallow the body corrective formulations to be selectively adjusted for atarget treatment area on the body (e.g., under the eye, forehead, lips,buttocks, neck, etc. . . . ). The treatment specific component orcomponents may be selected based on the physical properties of the filmthat results from the formulations that are necessary to be effectivelyapplied to a target treatment area, as shown in Table 1. For example, ifthe target treatment area is under the eye, the modulus should be lowrelative to the values of the other physical properties of the resultingfilm.

TABLE 1 Target Treatment Elonga- Matte Tex- Area Modulus Elasticity tionAdhesion Finish ture Under the Low High Medium High High High eyeForehead High High Medium High High High Lips Medium High High High LowLow

Examples of function modulating components and treatment specificcomponents include a stiffness component, an elasticity component, anelongation component, an adhesive component, a matte component and atextural component.

The language “stiffness component” includes components that modulate theflexibility of the resulting film, which is determined by measuring theYoung's Modulus of the film (see Example 2). Examples of stiffnesscomponents include the reactive constituent (e.g., organopolysiloxaneand/or hydride functionalized polysiloxane) and the reinforcingconstituent.

The language “elasticity component” includes components that modulatethe recoil of the resulting film, which is determined by measuring thehysteresis, and includes, for example, the reinforcing constituent.

The language “elongation component” includes components that modulatethe stretch of the resulting film, which is determined by measuring thepercent elongation to yield. Examples of elongation components includethe reactive constituent (e.g., organopolysiloxane and/or hydridefunctionalized polysiloxane) and the reinforcing constituent.

The language “adhesion component” includes components that modulate theadherence of the resulting film to the skin, as measured by the leatheradhesive test (see Example 2). Examples of adhesion components includethe reactive constituent (e.g., organopolysiloxane and/or hydridefunctionalized polysiloxane) and the reinforcing constituent.

The language “matte component” includes components that modulate thegloss of the resulting film, as measured by determining the shine of theresulting film (see Example 3). Examples of matte components include thereinforcing constituent and light scattering particles.

The language “textural component” includes components that modulate thetexture of the film so that the resulting film has the look and feel ofnatural skin, and is measured by determining the friction of the film.One of skill in the art can readily determine methods to measure thefriction of the film, for example, by pressing in and dragging acantilever across the surface and recording the resisting force. Higherfriction corresponds to higher recorded force and rougher surfaces tendto have higher friction.

In some embodiments, the invention pertains, at least in part, to a filmremoving cleanser for use in removing a body corrective film, whereinsaid film is prepared by a process comprising the steps of a) applying areactive reinforcing component to skin; and b) applying a cross-linkingcomponent to said reactive reinforcing component, wherein saidcross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component.

In other embodiments, the invention pertains, at least in part, to afilm removing cleanser comprising a film wetting component, apenetration component, a film swelling component and a film releasecomponent.

The language “film removing cleanser” includes a cosmetic formulationthat, when applied to a body corrective film, breaks down the componentsof the film such that the film may be removed from the body. In someembodiments, the film cleanser removes the film by wetting the film,penetrating the film, swelling the film and releasing the film from theskin.

The language “film wetting component” includes those components of thecleanser that allow the film to absorb liquid. In some embodiments, thefilm wetting component comprises caprylyl methicone, ethyl trisiloxaneor a combination thereof.

The language “penetration component” includes those components of thecleanser that allow the cleanser to permeate the film. Examples ofpenetration components include siloxane emulsifiers, caprylyl methicone,ethyl trisiloxane or a combination thereof.

The language “film swelling component” includes components of thecleanser which cause the film to expand. Examples of film swellingcomponents include caprylyl methicone, ethyl trisiloxane, isododecane ora combination thereof.

The language “film releasing component” includes components of thecleanser that cause the film to not adhere to the skin or body of thesubject to which the film is applied. Examples of film releasingcomponents include glycols, water or a combination thereof.

In some embodiments, the cleanser disrupts the film's mechanicalintegrity. The language “disrupt the film's, mechanical integrity”includes the disturbance of the mechanical features that provide thefilm its unique properties (e.g., the stiffness, elasticity, elongation,adhesion and the like).

In some embodiments, the cleanser comprises a siloxane phase, anemulsifier phase and an aqueous phase. The language “siloxane phase”includes a component of the cleanser that comprises one or moresiloxanes, for example, caprylyl methicone and ethyl trisiloxane. Insome embodiments, the siloxane phase also includes isododecane andAerogel VM2270 (Dow Corning). The language “emulsifier phase” includes acomponent of the cleanser that comprises one or more emulsifiers, forexample, siloxane emulsifiers such as lauryl PEG-9polydiethylsiloxyethyl dimethicone, PEG-35 Castor oil, or isododecaneand lauryl dimethicone/polyglycerin 3 cross polymer. The language“aqueous phase” includes a component of the cleanser that is soluble inwater, for example, water, propylene glycol, butylenes diglycol,glycerol or combinations thereof. In some embodiments, the aqueous phaseincludes MPdiol glycol, preservatives (e.g., neolone PE), opticalparticles (e.g., silica and DMPA/isophthalic acid/SMDI copolymer & Green5) and structural particles (e.g., nylon-12).

In some embodiments, the siloxane phase is about 50% of the cleanser,the emulsifier phase is about 8% of the cleanser and the aqueous phaseis about 42% of the cleanser.

In some embodiments, the invention pertains, at least in part, to amethod of cleaning a body surface having a body corrective film,comprising applying an effective amount of a film dissolving cleanser tothe film, such that said film dissolves. In some embodiments, the bodysurface is the skin.

In some embodiments, the invention pertains, at least in part, to aformulation for repairing a body corrective skin applied to the skin inwhich the formulation comprises a) a first reactive reinforcingcomponent and b) a second cross-linking component; wherein thecross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component such that a film is formed on the skin.

The terms “repair” and “repairing” includes ameliorating imperfectionsin the body corrective film after formation of the film on the skin. Insome embodiments, the term “repair” includes mending or patching tears,gaps or breaks in the film. In some embodiments, the term “repair”includes replacing a portion of the film that may have been removed fromthe skin. In some embodiments, the term “repair” includes re-adhering orre-attaching a portion of the film that may have come loose from theskin (e.g. de-laminated from the skin). In some embodiments, the term“repair” includes swelling the edges of the tear, gap or break in thefilm to make the film more malleable, such that the film may be able tobe reshaped.

In some embodiment, the invention pertains, at least in part, to amethod for repairing a body corrective film applied to skin by a)identifying an area of the film in need of repair; b) optionallysmoothing the edges of the film; and c) applying a formulation forrepairing the film, wherein the formulation comprises a first reactivereinforcing component and a second cross-linking component; wherein thecross-linking component catalyzes an in situ cross-linking of thereactive reinforcing component such that a film is formed on the skin,thereby repairing the body corrective film.

The language “smoothing the edges of the film” includes removing,swabbing, swelling, brushing or grinding the edges of the film in thearea in need of repair to remove jagged or uneven portions of the film.

In some embodiments, the invention pertains to a kit comprising a firstreactive reinforcing component, and a second cross-linking component,wherein the cross-linking component catalyzes an in situ cross-linkingof the reactive reinforcing component such that a film is formed on theskin. In some embodiments, the invention pertains, at least in part, toa kit for repairing a body corrective film in which the kit comprises aformulation comprising a) a first reactive reinforcing component and b)a second cross-linking component wherein the cross-linking componentcatalyzes an in situ cross-linking of the reactive reinforcing componentsuch that a film is formed on the skin.

In some embodiments, the kit is a multi-compartment kit comprising atleast two compartments. In some embodiments, the reactive reinforcingcomponent is in one compartment and the cross-linking component is in asecond compartment. In some embodiments, the kit further comprises oneor more brushes, one or more swabs, a film removing cleanser,instructions for use or a mirror. In some embodiments, the kit furthercomprises a pigment dispersion formulation.

EXAMPLES Example 1 Cyclic and Extension Pull Test Sample Preparation:

For the purpose of bulk mechanical property determination, targetmaterials were cast inside dumbbell shaped molds. The dimensions of theneck of the mold were 20 mm in length, 5 mm in width and 1.5 mm indepth. The “handles” of the mold were 20 min by 15 mm and providedadequate area to insure secure slip-free grip during testing. The molddimensions are consistent with the ASTM D638 guidelines.

Once the poured specimens were fully cured and dried, the formed sampleswere extracted from their individual molds by means of a spatula and thegeometry of the finished pieces was measured with digital calipers todetermine precise dimensions.

Mechanical Testing:

Mechanical characterization of specimens was carried out on the Instron3342 (Instron, Norwood Mass.) equipped with 100N load-cell (Instron#2519-103). Dumbbell shaped samples were mounted onto the instrument viamodified Instron 2710-101 grips which insured sample didn't slip or failinside the grips during testing. Two types of tests were performedsequentially on each sample, first the Cyclic Test followed by theExtension Pull Test. It is noted that the first test (e.g., the cyclictest) had negligible effects on the result of the second test (e.g., theextension pull test). Each test was preprogrammed into Bluehill LiteSoftware used to operate the instrument. The parameters and dataanalysis associated with each of the two tests is described below.

Cyclic Test:

In order to determine the elasticity of the materials, a cyclic test wasdesigned. The cyclic test was used to determine the most elastic (e.g.,spring-like) material and an Instant Residual Strain (I.R.S.) wasobtained from this test, as described below. Generally, the more elasticthe material, the faster it returns to its original shape afterdeformation. For perfectly elastic materials, the I.R.S. and cycle testarea approach zero, and therefore, the lower the value the better.

Prior to starting the test, a sample was mounted onto the instrumentsuch that the rectangular handle portions of the specimen and none ofthe specimen neck were fixed within the instrument grips. The instrumentgrip distance was adjusted such that the sample was at neutral extensionas indicated by the instrument force being close to zero (±0.01N).Subsequently, cyclic extension was performed at 1 mm/s to a-maximumextension of 15% of initial sample length. A total of 15 cycles areexecuted and recorded. The stress strain data recorded by instrument wasexported into Excel where the reported mechanical properties werecalculated.

An Excel template was used to automatically extract a number ofparameters. The cyclic Young's Modulus as calculated as the straightline slope of the stress-strain curve of first cycle between 1% and 4%.The R squared value of the linear fit was above 0.99 or the Young'sModulus was discarded. The Instant Residual Strain (I.R.S.) wascalculated for each cycle as the strain difference between the loadingand unloading curves at half the maximum stress achieved during the 1stcycle. The I.R.S. for the first cycle as well as the average I.R.S. forthe 4th through 14th cycles were recorded. The area bound by the loadingand unloading curves of each cycle was also calculated. Good agreementwas observed between the I.R.S. and the calculated cycle area.

The majority of the materials evaluated were sufficiently flexible andelastic such that the Cyclic Test could be repeated on the same samplewithout a significant change in calculated properties. This suggeststhis test does not result in long lasting changes to the testedmaterial.

Extension Pull Test:

The Extension Pull test was used to determine the stiffness andstretchiness of a material by measuring the Young's Modulus and UltimateStrain. The Young's Modulus was utilized as a measure of materialstiffness, while the Ultimate Strain was used as a measure of materialflexibility. In order to develop a film with the appearance of skin, theYoung's Modulus should fall within a target range (e.g., 0.1-1.0 MPa),while the fracture strain (as measured by the Ultimate Strain) should besufficiently high (e.g., greater than about 150%) so that the film willnot break when being deformed by skin movement.

The sample was mounted onto the instrument such that the rectangularhandle portions of the specimen and none of the specimen neck were fixedwithin the instrument grips. The instrument grip distance was adjustedsuch that the sample was at neutral extension as indicated by theinstrument force being close to zero (±0.01N). Subsequently, extensionuntil sample failure was performed at 10 mm/s. The stress strain datarecorded by instrument during the extension was exported to Excel wherethe reported mechanical properties were calculated.

An Excel template was used to automatically extract a number ofparameters from the instrument generated data. The extension Young'sModulus (YM) as calculated as the straight line slope of thestress-strain curve between 6% and 11%. The R squared value of thelinear fit was above 0.99 or the Young's Modulus was calculated from amore linear 5% strain range on the stress strain curve. The ShearModulus (C) was determined from the same strain range as the YM. G wascalculated as the slope of the best line fit between recorded stress andα-α-2, where α is 1 plus the instantaneous strain. The Yield strain wasdetermined as the strain at which the measured stress differed by morethan 10% from the Neo-Hookean stress; the multiple of G and (α-α-2).Ultimate Stress was calculated as the maximum stress recorded during theexperiment. The mechanical property calculations presented here areconsistent with ASTM D412.

Example 2 Leather T-Peel Adhesion Test

To determine adhesiveness of the target materials, the materials werespread onto a piece of soft flexible leather 25.4 mm wide and 76.2 mmlong. The leather used as test substrate was light weight upholsteryleather (AD1100 from Leather Unlimited, Belgium Wis.). Immediately afterspreading the material onto the first piece of leather, a secondequivalent piece of leather was placed on top to sandwich a thin layerof material between the two pieces. The two pieces of leather werepressed together to leave a thin homogeneous layer of material at theinterface of the two leather substrates. The edges were wiped to removeaccess materials and the material was allowed to cure and dry to form atest specimen.

The adhesion test sample was partially pealed at one end by hand toseparate enough of the two leather substrates for effective grip byInstron 3342 mounts. Each leather substrate was secured in its owninstrument grip and an extension test was performed at a rate of 10 mm/sto peel the two substrates from each other. The force vs. time data wasrecorded by instrument during the extension and exported to Excel wherethe reported adhesive force was calculated.

An Excel template was used to automatically extract adhesive parametersfrom the instrument generated data. The sample average adhesive forcewas calculated by averaging the instantaneous force measured by theinstrument during the experiment normalized by the sample width (25.4mm). This test method was developed in accordance with ASTM D1876. Theminimum acceptable adhesion, which depends on the stiffness of thematerial and the area on which the film is placed, was approximatelygreater than 25 N/mm

Example 3 Image Analyses Measures Shine:

In order to measure shine, either in vitro or in viva, a light box witha light source placed at a 45° angle relative to the site being measuredwas used to create shine, and a camera, positioned such that the angleformed by a line drawn from the lens to the area being measured is 45°,was used to photograph the site. The white balance, F-stop and ISO ofthe camera were manually fixed at set values to give adequate exposureand good color temperature. One picture was taken without any diffusingelement between the light source and the site to capture the shine.Then, a diffusing surface was placed between the light source and siteand another photograph was taken (altering shutter speed such that theexposure is similar or equal to the first photograph). This photographcaptured the surface without any shine present while the firstphotograph captured the maximum amount of shine as a result of specularreflectance. These photographs were overlaid and cropped to the relevantsample area and then the diffused photograph was subtracted from themaximum shine photograph to create a photograph with only the shinehighlights present. The entire subtracted photograph was then summarizedby finding the average grey value along with the standard deviation.This average grey value was denoted as the shine value and was used tocompare the amount of specular reflectance present in each sample. Foreach sample, the camera settings for each situation (with and withoutthe diffuser) were identical.

Photo Set Up Capture:

To ensure maximum repeatability in panelist placement for everyphotograph taken for product performance evaluation, a Head PositioningSystem (HPS) was created. This HPS had two configurations: forehead-onlyevaluations and a whole face evaluation. In both configurations, a model819 series table clamped chin-rest from Applied Science Laboratories(ASL) was used as a base to mount the two different configurations to atable. Two cameras were used to capture the subject from two differentangles. The first camera (normal shot) was positioned face-on such thatline of the lens through the camera was positioned relative to the planeof the subject's face at an angle of approximately 90°. A second camera(45° shot) was positioned to the subject's left such that the line ofthe lens through the camera was positioned relative to the plane of thesubject's face at an angle of approximately 45° capturing primarily theleft side of the subject's face. The position of the cameras relative tothe chin-rest was kept fixed.

In the first configuration, an ASL cheek-rest (819-2155) was mounted tothe ASL chin-rest. In this setup, the panelist's head was positionedsuch that the line formed from the center of the camera lens to the areaof evaluation is normal to the area of evaluation on the forehead. Inthe second configuration, an ASL forehead-rest (819-2150) was attachedto the chin-rest. In this setup, the chin-rest cup was positioned suchthat the horizontal bar on the forehead-rest was situated at thepanelist's horizontal hairline, maximizing the area of evaluation inevery photograph.

Lighting for the photography consisted of two Calumet Quattrofluorescent lamps (CF0003) with four Calumet 35 Watt 5500K daylightcolor temperature fluorescent lights (OL2003) placed in front of and oneither side of the panelist, angled to point directly at the panelist. Aglare stop polarizing filter from Visual Pursuits, Inc. was also placedon the front of each lamp. The lights were allowed to warm up for atleast 10 minutes prior to taking any photographs. In addition to thelighting, a circular polarizing filter was used on each of the cameralenses to control the type of light in each photograph.

For each evaluation, two sets of pictures were taken for the normal shotcamera. In the first set, the camera's circular polarizing filter wasconfigured such that its polarization was parallel to the polarizationof the fluorescent lights, giving a picture that highlighted the shineas well as the fine wrinkles, pores and skin texture. In the second set,the circular polarizing filter was configured such that the polarizationwas perpendicular (or cross) to the polarization of the fluorescentlights yielding a result that eliminated all glare and shows theunderlying skin tone, discoloration, and deep wrinkles. The 45° shotcamera was configured for each evaluation such that the camera'scircular polarizing filter was configured so that its polarization wasparallel to the polarization of the fluorescent lights, giving a picturethat highlighted the shine as well as fine wrinkles, pores and skintexture.

Brow-Lift Measure of Photo:

To measure the brow height of a photograph, a photograph was obtainedusing the method of photo capture previously described above. A “canthusline” was then drawn on the photograph from the medial to the lateralcanthus on each eye. This canthus line was used as a base from which thebrow height was measured. The eyebrow was isolated from the image byapplying valley detection, edge detection and thresholding graphicaloperations on the image. Within one experiment, the parameters forvalley and edge detection and thresholding were constant so that thesame portions of the eyebrow from each image series was the same. Toaccurately isolate the eyebrow, these parameters were changed to accountfor differences in photographic exposure between experiments and skinand brow colors between panelists. From these methods, a binary mask wascreated which was then further manipulated in order to ensure only theeyebrows were isolated in the picture. For overall height changemeasurements, the center of mass of each eyebrow was then determinedfrom its binary mask. The parameters for the binary operations andcenter of mass determination were always kept constant. The height ofeach brow was the normal from its center of mass to its correspondingcanthus line. This method measured overall height change but did notcapture the magnitude of change for severe arching or angling whereportions were raised and portions were lowered. For such cases, insteadof measuring the brow's center of mass, the heights of the brow normalto the canthus line at its left and right edges and at its center weredetermined from the binary mask.

Redness Reduction Photo Measure:

Photographs are obtained of the panelist using the photographic setuppreviously described. Comparisons of redness are only done onphotographs taken within the same experiment because the exposure, andlight and face positioning are only constant within a single experiment.After the series of photographs in the experiment are taken, thecross-polarized pictures are overlaid such that the area to be evaluatedfor redness reduction remains as fixed as is possible between eachimage. Using graphical manipulation software, the L*a*b* channels in theCIELAB colorspace are created for each image in the series. The L* valuerepresents the degree of illumination, while a* and b* define thechromaticity. Specifically, a* represents the degree of redness (+values) or'greenness (− values). The intensity of the red color squareon the color card in the baseline photograph's a* channel is then usedto normalize the subsequent images by adjusting the intensity of thesubsequent image a* channels until the a* values within the red colorsquare on the color cards in those images equals the baseline value. Thearea of evaluation is then cropped out of the photographs. Rednessreduction is then determined by subtracting the a* values for the areain the ‘before’ photographs from the a* values in the ‘after’photographs. A negative value from this subtraction indicates areduction in redness while a positive value indicates an increase.

Example 4 Stress Testing Methods

The mechanical durability of the materials was evaluated by creating anartificial brow lift by applying one of the following methods ofpre-tensioning the skin during product application. These methods ofpre-tensioning were used to stress the skin surface and pull the browinto a lifted position:

-   -   “brow orthogonal push,” in which a stress was applied that        originated at the eyebrow and is vectored anteriorly away from        the eyebrow at an angle that was between 80° and 100° relative        to the line of the eyebrow,    -   “corner hairline diagonal pull,” in which a stress was applied        that originated at the most anterior and lateral point on the        panelist's hairline and was vectored anteriorly away from and at        an angle between 10° and 80° relative to the line of the        eyebrow,    -   “corner hairline orthogonal pull,” in which a stress was applied        that originated at the most anterior and lateral point on the        panelist's hairline and was vectored anteriorly away from and at        an angle between 80° and 100° relative to the line of the        eyebrow,    -   “lateral hairline orthogonal push” in which a stress was applied        that originated at the most lateral point of the hairline that        was at or above the level of the eyes and was vectored        anteriorly away from at an angle between 80° and 100° relative        to the line of the eyebrow.

While the brow was held lifted by one of these stresses, the product wasapplied to the area of skin over which the tension was being applied.Once the film cured, the stress was removed and the mechanicaldurability of the film's ability to hold the tensions in the skin wasevaluated. This evaluation was achieved by measuring the degree of browlift using the methods described before and after product application.Durability of the effect was measured by allowing time, normal andexaggerated facial expressions and environmental stresses such as water,sweat, heat, sebum production and surface contact to interact with thefilm. The amount of lift was tracked at regular intervals to determinehow quickly the film's ability to hold the mechanical benefit lasted. Afilm was determined to be mechanically durable if it could withstand thestresses previously mentioned and maintain the brow lift at the leveloriginally achieved immediately after application.

Example 5 Formulations

Examples of formulations illustrating the two-step application methodare provided below. The reactive reinforcing component first step (e.g.,the treatment) includes formulations 60-140-1, 60-140-1B, 60-140-HP2, SK87/2, 60-140-LX2, SK 87/1, 48-196, 48-199, 60-211, 60-200-1N, 60-208,66-166-F, 66-167-E, 66-166-C, 66-169-3, 66-170, 79-23, 79-24b, 79-45,79-46, 79-41, 88-30-1, 83-16, 79-55a, 79-55b, 79-55c, 79-55d, 79-55e,79-55f, 79-55g, 83-54, 79-55h, 81-18, 81-19, 81-20, 81-21, 79-74, 80-23,79-88, 79-88-3A, 79-74-RD, 79-90-B, 88-70, 88-72, 88-75-2, 88-75-3,88-80, 88-85-1, 88-85-2, 88-83-V2, 88-83-V3 and 83-54 shown below.

Components of the formulations are commercially available. The followingtable provides the generic name for any trade name used throughout thisapplication.

International Nomenclature Cosmetic Tradename Ingredient (INCI) nameAerogel VM2270 Silica Silylate Aerosil 8200 ™ or Fumed silica modifiedwith Aerosil R8200 ™ hexamethyldisilazane Andisil C1000 ™ Silicondioxide + Dimethylpolysiloxane Andisil C1300 ™ Silicon dioxide +Dimethylpolysiloxane Andisil CE-4 ™ Vinyl Dimethicone Andisil MV 2,000 ™or Vinyl Dimethicone MV2000 Andisil VS 1,000 ™ Vinyl Dimethicone AndisilVS 10,000 ™ Vinyl Dimethicone Andisil VS 165,000 ™ Vinyl Dimethicone orAndisil VS165K Andisil VS 20,000 ™ Vinyl Dimethicone Andisil VS 250 ™Vinyl Dimethicone Andisil VS 500 ™ or Vinyl Dimethicone VS500 Andisil VS65,000 ™ or Vinyl Dimethicone VS65,000 Andisil XL-11 ™ HydrogenDimethicone, SiH Functional Andisil XL-1B ™ or XL- Hydrogen Dimethicone,SiH Functional 1B Aquadispersable Rutile Titanium dioxide TitaniumDioxide ™ Barium Sulfate HL Barium Sulfate Beaver UV/FluorescentAROMATIC HETEROCYCLE Pigment Cabosperse 1030K CAB-O-SPERSE ® 1030K is anaqueous dispersion of CAB-O-SIL ® L-90, a very low surface area, fumedsilica. It is electrostatically stabilized with Potassium Hydroxide andhas an alkaline pH. Carbopol Ultrez 21 Acrylates/C10-30 Alkyl AcrylateCrosspolymer Cetiol OE Dicapryl Ether Chronosphere Optical Silica andpolyurethane-40/silica and Brite or Chronosphere polyurethane-40 andgreen 5 Opticals/Opticals Brite cremaphor EL PEG-35 Castor Oil CrodamolSTS PPG 3 Benzyl Ether Myristate DC 200 Fluid (1 cSt) Dimethicone DC2-1184 fluid (DOW Trisiloxane (and) Dimethicone CORNING ® 2-1184 FLUID)DC 556 Phenyl Trimethicone DMF5 CS dimethicone DMS-V41Poly(Dimethylsiloxane), Vinyl Terminated Dow 245 Fluid (DowCyclopentasiloxane CORNING 245 Fluid) Dow 246 Fluid (DowCyclohexasiloxane CORNING 246 Fluid) Dow 9011 ElastomerCyclopentasiloxane (and) PEG-12 Dimethicone Blend (Dow CorningCrosspolymer 9011 Elastomer Blend) Dow Corning 9011 Cyclopentasiloxane(and) PEG-12 Dimethicone Silicone Elastomer Crosspolymer B1end ™ or DowElastomer Blend 9011 Dow 9045 Elastomer Cyclopentasiloxane (and)Dimethicone Blend or Dow Corning Crosspolymer 9045 Silicone ElastomerBlend ™ Dow Corning 200 Fluid Hexamethyldisiloxane 0.65 cSt ™ DowCorning 245 Decamethylcyclopentasiloxane F1uid ™ Dow Corning 5329 PEG-12Dimethicone Dow Elastomer Blend Dimethicone (and) DimethiconeCrosspolymer 9041 or DOW CORNING ® 9041 SILICONE ELASTOMER BLEND dowanolDPM Dipropylene Glycol Methyl Ether Dri-Flow Elite BN or Aluminum StarchOctenylsuccinate (and) Boron DRY-FLO Elite BN Nitride Flo-BeadsSE-3207B ™ Ethylene-methyl methacrylate copolymer Dow Corning FZ-3196Caprylyl Methicone Ganzpearl GMP-0830 ™ Acrylates CrosspolymerGranhydrogel O ™ Water (and) Glyceryl Polyacrylate (and) 1,3- ButyleneGlycol (and) PVM/MA (and) Propylparaben (and) Methylparaben GranpowderNylon ™ Nylon-12 Gransil EP-LS ™ Polysilicone-11 (and) Laureth-12Gransurf 90 Cetyl PEG/PPG-10/1 Dimethicone Iris C12-17 Alkanes IronOxide Tint or Iron Iron Oxides Oxide Tint Mixture Isododecane mixture ofhighly branched C12 isoparaffins, mainly the2,2,4,6,6-pentamethylheptane isomer (typically c.a. 85%). Jeechem BUGL ™or Butylene Glycol Jeen BUGL Jeecide cap 5 Phenoxyethanol, CaprylylGlycol, Potassium Sorbate, Aqua, Hexylene Glycol Jeensilc CPS-312 ™Cyclomethicone Kaolin USP BC2747 Kaolin KF6013 PEG-9 Dimethicone KTZXian Vistas ™ Titanium Dioxide (And) Mica (And) Iron Oxide (C.I. 77491);chemical name: Mica (and) Titanium Dioxide (and) Ferrous Oxide LabrafacCC ™ Caprylic/Capric Triglyceride LILAC ™ (Sonneborn) C14-22 AlkaneMPDiol Methyl Propanediol Neolone PE ™ Phenoxyethanol,Methylisothiazolinone Nylon Nylon 12 Nylon 10-12 ™ Nylon 12 (And)Isopropyl Titanium Triisostearate PC 075.3 Hydrogen Dimethicone Pinktint mix Iron Oxides Plantacare 818 UP ™ Coco-Glucoside; ChemicalDescription is “C8- 16 fatty alcohol glucoside” Platinum divinyl UPACname “1,3-Diethenyl-1,1,3,3- complex (for exampletetramethyldisiloxane - platinum (1:1)”; Trade PT-50175F) name:“Platinum-divinyltetramethyldisiloxane complex”; Synonyms:Platinum(0)-1,3-divinyl- 1,1,3,3-tetramethyldisiloxane complex solution;pt(0)-1,3-divinyl-tetrame-disiloxane compl 0.100;1,3-Divinyl-1,1,3,3-tetramethyl- disiloxane-platinum (0) PMX-1184 orDimethicone and trisiloxane XIAMETER ® PMX- 1184 Silicone FluidPolyglycol P425 PPG-9 prestige pearlescent mixture of titanium and ironoxides of a beige beige color PS123-KG Hydrogen Dimethicone RM 2051 orRM 2051 Sodium Polyacrylate (and) Dimethicone (and) Thickening AgentCyclopentasiloxane (and) Trideceth-6 (and) PEG/PPG 18/18 Schercemol ™318 Ester Isopropyl Isostearate Sepiplus 400 ™ Polyacrylate 13 (and)Polyisobutene (and) Polysorbate 20 Shin Etsu KF 6038 Lauryl PEG-9Polymethylsiloxyethyl Dimethicone Shin Etsu KSG 820 LaurylDimethicone/Polyglycerin-3 Crosspolymer Silsoft 034 caprylyl methiconesilsoft ETS ethyl trisiloxane Simulgel EG ™ Sodiumacrylate/acryloyldimethyl taurate copolymer & Isohexadecane &Polysorbate 80 SIMULGEL NS Hydroxyethylacrylate/sodium acryloyldimethyltaurate copolymer & squalane & polysorbate 60 Soft Bead B or SoftEthylene/Methacrylate Copolymer Beads B Solagum AX Acacia senegal gumand xanthan gum SR 1000 Resin Trimethylsiloxysilicate Tint Iron OxidesTMF 1.5 Methyl Trimethicone Tween 20 Polysorbate 20 UCT-PS448.5Polydimethylsiloxane, Vinyldimethyl Terminated USG 102 Dimethicone/VinylDimethicone Crosspolymer Veegum Pro Tromethamine Magnesium AluminumSilicate Veegum Ultra Granules Magnesium Aluminum Silicate Velvesil125 ™ Cyclopentasiloxane (and) C30-45 Alkyl Cetearyl DimethiconeCrosspolymer Velvet Veil 310 ™ Mica (and) Silica Vitamin-A complexretinol Vitamin-C complex ascorbic acid Vitamin-E complex TocopherolXirona caribbean blue Mica, Titanium Dioxide, Silica, Tin Oxide

Formulation 60-140-1

Component Percent of No Component Formulation (%) 1 DMS-V41 23.80 2Aerosil 8200 9.45 3 PS123-KG 12.00 4 UCT-PS448.5 5.55 5 Velvesil 1253.60 6 Gransil EP-LS 3.60 7 Soft Beads B 1.20 8 Sepiplus 400 1.20 9Water 27.00 10 Granhydrogel O 6.70 11 Granpowder 5.90 Nylon

Procedure:

Components 1-4 were hand mixed in a graduated 4-oz until mixture wasfree of white particulates. Subsequently, components 5-8 were added andthe mixture was confirmed as homogenous (Mixture A). In a separatevessel, components 9 and 10 were hand mixed until homogenous (MixtureB). Mixture B was added to Mixture A under strong agitation, provided bya 4-blade, 40 mm propeller at 550 rpm, then component 11 was added andthe mixing speed was to 1000 rpm and mix for 5 minutes. The mixture wasconfirmed as homogenous.

Formulation 60-140-1B

Component Percent of No. Component Formulation (%) 1 DMS-V41 22.60 2Aerosil 8200 8.94 3 PS123-KG 11.30 4 UCT-PS448.5 5.30 5 Velvesil 1253.42 6 Gransil EP-LS 3.42 7 Soft Beads B 1.20 8 Sepiplus 400 1.20 9Water 25.66 10 Granhydrogel O 6.36 11 Granpowder 5.60 Nylon 12 Cetiol OE5.00

Procedure:

Components 1-4 were hand mixed in a graduated 4-oz and the mixture wasconfirmed as free of white particulates. Subsequently, components 5-8were added and the mixture was confirmed homogenous (Mixture A). In aseparate vessel, components 9 and 10 were hand mixed until homogenous(Mixture B). Mixture B to was added Mixture A under strong agitation,provided by a 4-blade, 40 mm propeller at 550 rpm, then components 11and 12 were added and the mixing speed was increased to 1000 rpm and mixfor 5 minutes. The mixture was confirmed as homogenous.

Formulation 60-140-HP2

Component Percent of No. Component Formulation (%) 1 UCT-PS448.5 32.97 2Aerosil 8200 12.82 3 PS123-KG 14.65 4 Velvesil 125 4.40 5 Gransil EP-LS4.40 6 Soft Beads B 1.47 7 Sepiplus 400 1.47 8 Granhydrogel O 20.63 9Granpowder 7.20 Nylon

Procedure:

Components 1-3 were hand mixed in a graduated 4-oz and the mixture wasconfirmed as free of white particulates. Subsequently, components 4-7were added the mixture was confirmed homogenous (Mixture A). In aseparate vessel, component 8 was mixed until homogenous (Mixture B).Mixture B to was added Mixture A under strong agitation, provided by a4-blade, 40 mm propeller at 550 rpm, then component 9 was added and themixing speed was increased to 1000 rpm and mix for 5 minutes. Themixture was confirmed as homogeneous.

Formulation SK 87/2

Component Percent of No. Component Formulation (%) 1 DMS V41 35.00 2Aerosil 8200 11.60 3 PS123-KG 5.20 4 Velvesil 125 11.20 5 Gransil EP-LS8.70 6 Water 6.70 7 Polyvinyl alcohol 2.00 8 Granhydrogel O 8.70 9Granpowder 6.10 Nylon 10 Silsoft 034 4.80

Procedure:

Components 1-3 were hand mixed in a graduated 4-oz and the mixture wasconfirmed as free of white particulates. Subsequently, components 4 and5 were added and the mixture was confirmed as homogenous (Mixture A). Ina separate vessel, components 6 and 7 were hand mixed until homogenous(Mixture B). Mixture B was added to Mixture A under strong agitation,provided by a 4-blade, 40 mm propeller at 550 rpm, then components 8-10were added and the mixing speed was increased to 1000 rpm and mix for 5minutes. The mixture was confirmed as homogeneous.

Formulation 60-140-LX2

Component Percent of No. Component Formulation (%) 1 DMS V41 27.51 2Aerosil 8200 10.87 3 PS123-KG 3.47 4 UCT-PS448.5 13.41 5 Velvesil 1254.16 6 Gransil EP-LS 4.16 7 Soft Bead B 1.39 8 Sepiplus 400 1.39 9 Water21.45 10 Granhydrogel O 5.38 11 Granpowder 6.82 Nylon

Procedure:

Components were hand mixed 1-4 in a graduated 4-oz and the mixture wasconfirmed as free of white particulates. Subsequently, components 5-8were added and mixture was confirmed as homogenous (Mixture A). In aseparate vessel, components 9 and 10 were hand mixed until homogenous(Mixture B). Mixture B was added to Mixture A under strong agitation,provided by a 4-blade, 40 mm propeller at 550 rpm, then component 11 wasadded and the mixing speed was increased to 1000 rpm and mixed for 5minutes. The mixture was confirmed as homogeneous.

Formulation SK 87/1

Component Percent of No. Component Formulation (%) 1 DMS V41 36.90 2Aerosil 8200 12.30 3 PS123-KG 5.50 4 Velvesil 125 11.60 5 Gransil EP-LS9.10 6 Water 7.10 7 Polyvinyl alcohol 2.00 8 Granhydrogel O 9.10 9Granpowder 6.40 Nylon

Procedure:

Components 1-3 were hand mixed in a graduated 4-oz and the mixture wasconfirmed as free of white particulates. Subsequently, components 4 and5 were added and the mixture was confirmed as homogenous (Mixture A). Ina separate vessel, components 6 and 7 were hand mixed until homogenous(Mixture B). Mixture B was added to Mixture A under strong agitation,provided by a 4-blade, 40 mm propeller at 550 rpm, then components 8 and9 were added and the mixing speed was increased to 1000 rpm and mixedfor 5 minutes. The mixture was confirmed as homogeneous.

Formulation 48-196

Component Percent of No. Component Formulation (%) 1 Andisil VS10,00024.46 2 Andisil VS165K 3.66 3 Aerosil 8200 9.72 4 Andisil XL-11 12.33 5Velvesil 125 3.70 6 Gransil EP-LS 3.70 7 Soft Beads B 1.23 8 Sepiplus400 1.23 9 Water 27.75 10 Granhydrogel O 6.87 11 Neolone PE 0.21 12Granpowder 4.11 Nylon 13 Tint 1.03

Procedure:

Components 1-3 were mixed in a graduated 4-oz with a 4-blade propellerat 1000 RPM until homogenous (Mixture A) and the mixture was confirmedas homogenous. In a separate container components 4-8 were mixed with a4-blade propeller at 750 RPM until homogenous (Mixture B). In anothercontainer, components 9-11 were mixed with a 4-blade propeller at 750RPM until homogenous (Mixture C). Mixture B was added to Mixture C understrong agitation, provided by a 4-blade, 40 mm propeller at 750 rpm,then Mixture A was added to combined Mixtures B and C drop by drop.Finally, components 12 and 13 were added and the mixing speed increasedto 1000 RPM and mix for 10 minutes. The mixture was confirmed ashomogeneous.

Formulation 48-199

Component Percent of No. Component Formulation (%) 1 Andisil VS10,00022.11 2 Andisil VS165K 3.31 3 Aerosil 8200 8.79 4 Andisil XL-11 11.15 5Velvesil 125 3.35 6 Gransil EP-LS 3.35 7 Soft Beads B 1.12 8 Sepiplus400 1.12 9 Water 25.09 10 Granhydrogel O 6.21 11 Neolone PE 0.19 12Granpowder 4.94 Nylon 13 Silsoft 034 9.29

Procedure:

Components 1-3 were mixed in a graduated 4-oz with a 4-blade propellerat 1000 RPM until homogenous (Mixture A). In a separate container,components 4-8 were mixed with a 4-blade propeller at 750 RPM untilhomogenous (Mixture B). In another container, components 9-11 were mixedwith a 4-blade propeller at 750 RPM until homogenous (Mixture C).Mixture B to Mixture C was added under strong agitation, provided by a4-blade, 40 mm propeller at 750 rpm, then Mixture A was added tocombined Mixtures B and C drop by drop. Finally, components 12 and 13were added and the mixing speed was added to 1000 RPM and mixed for 10minutes. The mixture was confirmed as homogeneous.

Formulation 60-211

Component Percent of No. Component Formulation (%) 1 Andisil C1000 33.662 Andisil C1300 6.73 3 Andisil XL-1 1 9.62 4 Velvesil 125 3.46 5 GransilEP-LS 3.46 6 Soft Beads B 1.15 7 Sepiplus 400 1.15 8 Water 25.97 9Granhydrogel O 6.42 10 Jeechem BUGL 3.85 11 Neolone PE 0.19 12Granpowder 3.85 Nylon 13 Tint 0.49

Procedure:

Components 1-7 were mixed in a graduated 4-oz with a 4-blade propellerat 2000 RPM until homogenous (Mixture A). In a separate container,components 8-11 were mixed with a 4-blade propeller at 750 RPM untilhomogenous (Mixture B). Mixture B was slowly added to Mixture A understrong agitation provided by a 4-blade propeller at 2000 RPM. Components12 and 13 were added and the mixing speed was increased to 2000 RPM for5 minutes. The mixture was confirmed as homogeneous.

Formulation 60-200-1N

Component Percent of No. Component Formulation (%) 1 Andisil C1000 33.882 Andisil C1300 7.65 3 Andisil XL-11 18.03 4 SR 1000 Resin 10.93 5 Iris2.19 6 Dri-Flow Elite BN 10.93 7 Barium Sulfate HL 4.37 8 Gransil EP-LS8.74 9 Sepiplus 400 2.19 10 Neolone PE 0.55 11 Tint 0.54

Procedure:

Components 1-5 were mixed in a graduated 4-oz with a 4-blade propellerat 2000 RPM until homogenous (Mixture A). Components 6-9 were then addedand mixed with a 4-blade propeller at 2000 RPM until homogenous.Components 10 and 11 were added and the mixing speed was mixed at 2000RPM until homogeneous.

Formulation 60-208

Component Percent of No. Component Formulation (%) 1 Andisil C1000 30.052 Andisil C1300 6.56 3 Andisil XL-11 22.95 4 SR 1000 Resin 10.93 5 Iris2.19 6 Dri-Flow Elite BN 10.93 7 Barium Sulfate HL 4.37 8 Gransil EP-LS8.74 9 Sepiplus 400 2.19 10 Neolone PE 0.55 11 Tint 0.54

Procedure:

Components 1-5 were mixed in a graduated 4-oz with a 4-blade propellerat 2000 RPM until homogenous (Mixture A). Components 6-9 were then addedand mixed with a 4-blade propeller at 2000 RPM until homogenous.Components 10 and 11 were added and the mixing speed was mixed at 2000RPM until homogeneous.

Formulation 66-166-F

Percent of Component Formulation No. Component (%) 1 Aerosil 8200 ™ 8.43% 2 Andisil VS 10,000 ™ 21.22% 3 Andisil VS 165,000 ™  3.17% 4Andisil XL11 ™ 10.34% 5 Velvesil 125 ™  3.10% 6 Gransil EP-LS ™  3.10% 7Flo-Beads SE-3207B ™  1.03% 8 Sepiplus 400 ™  1.03% 9 Water 23.28% 10Granhydrogel O ™  5.75% 11 Neolone PE ™  0.17% 12 Granpowder Nylon ™ 4.23% 13 Ganzpearl GMP-0830 ™  0.31% 14 Velvet Veil 310 ™  0.21% 15Aquadispersable Rutile  0.21% Titanium Dioxide ™ 16 Yellow Iron Oxide 0.09% 17 Red Iron Oxide  0.04% 18 Black Iron Oxide  0.01% 19 DowCorning 200 Fluid 14.29% 0.65 cSt ™

Procedure:

Components 1-3 were mixed together as siloxane phase A. Into siloxanephase B, components 4-8 were mixed. Components 9-11 were combined as thewater phase. The water phase was slowly added to siloxane phase B andmixed until homogenous. Into this new phase, phase A was added veryslowly drop by drop. Once all of siloxane phase A was added, components12-19 were added to the formula and mix until homogenous.

Formulation 66-167-E

Component Percent of No. Component Formulation(%) 1 Aerosil 8200 ™ 8.36% 2 Andisil VS 10,000 ™ 21.05% 3 Andisil VS 165,000 ™  3.15% 4Andisil XL11 ™ 10.25% 5 Velvesil 125 ™  3.08% 6 GransilEP-LS ™  3.08% 7Flo-Beads SE-3207B ™  1.02% 8 Sepiplus 400 ™  1.02% 9 Water 23.09% 10Granhydrogel O ™  5.70% 11 Neolone PE ™  0.17% 12 Granpowder Nylon ™ 4.20% 13 Ganzpearl GMP-0830 ™  0.31% 14 Velvet Veil 310 ™  0.20% 15Aquadispersable Rutile  0.20% Titanium Dioxide ™ 16 Yellow Iron Oxide 0.09% 17 Red Iron Oxide  0.04% 18 Black Iron Oxide  0.01% 19 LILAC ™(Sonneborn)    2% 20 Cetyl Dimethicone    5% 21 Granhydrogel O ™    8%

Procedure:

Components 1-3 were mixed together as siloxane phase A. Into siloxanephase B components 4-8 were added. Components 9-11 were combined as thewater phase. The water phase was slowly added to siloxane phase B andmixed until homogenous. Into this new phase, phase A was added veryslowly drop by drop. Once all of siloxane phase A was added, components12-21 were added to the formula and mixed until homogenous.

Formulation 66-166-C

Component Percent of No. Component Formulation (%) 1 Aerosil 8200 ™ 8.43% 2 Andisil VS 10,000 ™ 21.22% 3 Andisil VS 165,000 ™  3.17% 4Andisil XL11 ™ 10.34% 5 Velvesil 125 ™  3.10% 6 Gransil EP-LS ™  3.10% 7Flo-Beads SE-3207B ™  1.03% 8 Sepiplus 400 ™  1.03% 9 Water 23.28% 10Granhydrogel O ™  5.75% 11 Neolone PE ™  0.17% 12 Granpowder Nylon ™ 4.23% 13 Ganzpearl GMP-0830 ™  0.31% 14 Velvet Veil 310 ™  0.21% 15Aquadispersable Rutile  0.21% Titanium Dioxide ™ 16 Yellow Iron Oxide 0.09% 17 Red Iron Oxide  0.04% 18 Black Iron Oxide  0.01% 19Granhydrogel O ™ 14.29%

Procedure:

Components 1-3 were mixed together as siloxane phase A. Into siloxanephase B components 4-8 were added. Components 9-11 were combined as thewater phase. The water phase was slowly added to siloxane phase B andmixed until homogenous. Into this new phase, phase A was very slowlyadded drop by drop. Once all of siloxane phase A was added, components12-19 was added to the formula and mixed until homogenous.

Formulation 66-169-3

Component Percent of No. Component Formulation (%) 1 Ganzpearl GMP- 0.16% 0830 ™ 2 Velvet Veil 310 ™  0.10% Aquadispersable 3 RutileTitanium  0.10% Dioxide ™ 4 Yellow Iron Oxide  0.04% 5 Red Iron Oxide 0.02% 6 Black Iron Oxide  0.01% 7 Gransil EP-LS ™  0.76% 8 AndisilXL-11 ™  8.61% 9 Gransil EP-LS ™  2.34% 10 Andisil C1000 ™ 33.51% 11Andisil C1300 ™  6.67% 12 Andisil XL-11 ™  1.59% 13 Velvesil 125 ™ 3.48% 14 Flo-Beads SE-  1.15% 3207B ™ 15 Sepiplus 400 ™  1.27% 16 Water25.18% 17 Granhydrogel O ™  6.22% 18 Jeechem BUGL ™  3.75% 19 NeolonePE ™  0.21% 20 Granpowder  3.83% Nylon ™ 21 KTZ Xian Vistas ™  1.00%

Procedure:

Components 1-8 were mixed together and homogenized at 26,000 RPM for 10minutes. After 10 minutes, component 9 was added and homogenized againfor 10 minutes at 26,000 RPM. To this homogenized mixture, components10-15 were added and mixed with an overhead stirrer at 2,000 RPM untilhomogenous in appearance (this is the siloxane phase). In a separatecontainer, components 16-19 were mixed until homogenous to form thewater phase. The water phase was added to the siloxane phase veryslowly, with continuous stirring at 2,000 RPM. Once the water phase wascompletely mixed in, components 20 and 21 were added to the formula andmixed at 2,000 RPM until homogenous.

Formulation 66-170

Component Percent of No. Component Formulation (%) 1 Andisil C1300 ™ 8.92% 2 Andisil C1000 ™ 44.21% 3 Andisil XL11 ™ 12.67% 4 Sepiplus 400 ™ 1.30% 5 Ganzpearl GMP-0830 ™  0.18% 6 Velvet Veil 310 ™  0.12% 7Aquadispersable Rutile  0.12% Titanium Dioxide ™ 8 Yellow Iron Oxide 0.05% 9 Red Iron Oxide  0.02% 10 Black Iron Oxide  0.01% Dow Corning9011 11 Silicone Elastomer  3.25% Blend ™ Dow Corning 9045 12 SiliconeElastomer  3.25% Blend 13 Dow Corning 245  2.62% Fluid ™ 14 JeensilcCPS312 ™  0.65% 15 Water  9.49% 16 Plantacare 818 UP ™  0.16% 17Propylene Glycol  6.60% 18 Glycerin  1.29% 19 Jeechem BUGL ™  3.22% 20Sodium Chloride  0.32% 21 Nylon 10-I2 ™  1.53%

Procedure:

Components 1-10 were mixed together to create the siloxane phase A.Next, components 11-14 were mixed to create siloxane phase B. A waterphase was created by mixing components 15-20. The water phase was slowlyadded into siloxane phase B while mixing at 2,000 RPM to create phase C.Finally, phase C was mixed into siloxane phase A until homogenous.

Formulation 79-23

Component Percent of No. Component Formulation (%) 1 Andisil VS 500 ™0.72 2 Andisil MV 2000 ™ 1.02 3 Andisil VS 65,000 ™ 17.20 4 AndisilXL-1B ™ 22.52 5 Aerosil R8200 ™ 11.77 6 Ganzpeari GMP- 0.19 0830 ™ 7Velvet Veil 310 ™ 0.13 8 Aquadispersable Rutile 0.13 Titanium Dioxide ™9 Yellow Iron Oxide 0.05 10 Red Iron Oxide 0.03 11 Black Iron Oxide 0.0112 Gransil EP-LS ™ 3.59 13 Velvesil 125 ™ 3.58 14 Flo-Beads SE- 1.023207B ™ 15 Sepiplus 400 ™ 1.10 16 Water 23.72 17 Granhydrogel O ™ 6.9918 Jeechem BUGL ™ 3.50 19 Sodium Chloride 0.35 20 Neolone PE ™ 0.35 21Granpowder Nylon ™ 2.05

Procedure:

Components 1-5 were combined and mixed (Mixture A) in a dual asymmetriccentrifugal mixer at 2500 RPM while confirming that the mixture was freeof white particulates. Components 6-15 were mixed into Mixture A andmixed in a dual asymmetric centrifugal mixer. Mixture A was confirmed ashomogenous. In a separate vessel, components 16 and 20 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture B).Mixture B was added to Mixture A dropwise while mixing with a 4-blade 40mm propeller at 2000 rpm and the mixture was confirmed as homogenous.Component 21 was added to the product of Mixture A and Mixture B andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-24b

Component Percent of No. Component Formulation ( % ) 1 Andisil VS 500 ™0.72 2 Andisil MV 2000 ™ 1.07 3 Andisil VS 65,000 ™ 17.91 4 AndisilXL-1B ™ 23.15 5 Aerosil R8200 ™ 12.12 6 Ganzpearl GMP- 0.19 0830 ™ 7Velvet Veil 310™  0.13 8 Iron Oxide Tint 0.22 9 Gransil EP-LS ™ 3.70 10Velvesil 125 ™ 3.70 11 Flo-Beads SE- 1.06 3207B ™ 12 Sepiplus 400 ™ 1.1113 Water 22.31 14 Granhydrogel O ™ 6.56 15 Jeechem BUGL ™ 3.28 16 SodiumChloride 0.33 17 Neolone PE ™ 0.33 18 Granpowder Nylon ™ 2.12

Procedure:

Components 4, 8 and 9 were combined and homogenized until smooth at20000 RPM. Components 1-3, 6-7, 10-12 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates were no longer visible (Mixture A). In a separate vessel,components 13-17 were mixed with a 4-blade, 40 mm propeller at 550 rpmuntil homogenous (Mixture B). Mixture B was added to Mixture A dropwisewhile mixing with a 4-blade 40 mm propeller at 2000 rpm and the mixturewas confirmed as homogenous. Component 18 was added to the product ofMixture A and Mixture B and mixed with 4-blade 40 mm propeller at 1000rpm until homogenous.

Formulation 79-45

A 2:1 blend of Formulations 60-211 and 79-24b was mixed together with a4-blade 40 mm propeller at 2000 rpm for 2 minutes.

Formulation 79-46

A 1:2 blend of Formulations 60-211 and 79-24b was mixed together with a4-blade 40 mm propeller at 2000 rpm for 2 minutes.

Formulation 79-41

A 1:5 blend of Formulations 60-211 and 79-24b was mixed together with a4-blade 40 mm propeller at 2000 rpm for 2 minutes.

Formulation 88-30-1

Component Percent of No. Component Formulation (%) 1 VS500 0.68 2 MV20001.02 3 VS65,000 17.00 4 XL-1B 21.96 5 Aerosil R 8200 11.51 6 Dow 246Fluid 10.43 7 Crodamol STS 1.15 8 83-49 12.00 9 83-50 3.39 10 Cabosperse1030K 20.87

Procedure:

Ingredients 1 through 7 were mixed using a propeller blade at 275 RPM toprepare phase A. In a separate vessel components 8 through 10 weremixed, using a propeller blade at 275 RPM, to prepare phase B. Phase Bwas mixed into phase A at 275 RPM until the emulsion is uniform. Anamount of 0.01% iron oxides was added to the final formulation to impartcolor. Formulation 83-49 and 83-50 are emulsions of VS 165,000 vinylsiloxane and XL-11 hydride functionalized siloxane, respectively,containing 65% siloxanes, 8% oleth-10 surfactant, and the balance water.

Formulation 83-16

Component Percent of No. Component Formulation (%) 1 Gransil EP-LS ™ 3.52 Andisil XL-11 ™ 9.76 3 Andisil VS 1,000 ™ 25.53 4 Andisil VS 165,000 ™5.12 5 Aerosil R8200 ™ 10.23 6 Velvesil 125 ™ 3.51 7 Flo-BeadsSE-3207B ™ 1.17 8 Sepiplus 400 ™ 1.22 9 Granpowder Nylon ™ 3.9 10 Water25.47 11 Granhydrogel O ™ 6.32 12 Jeechem BUGL ™ 3.97 13 Neolone PE ™0.22 14 Iron Oxide Tint 0.08 Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 9 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates were no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 10 to 13 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 14 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55a

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-11 ™ 8.17 3 Andisil VS 1,000 ™ 32.59 4 Andisil VS165,000 ™ 6.52 5 Andisil XL-11 ™ 3.04 6 Aerosil R8200 ™ 13.04 7 Sepiplus400 ™ 1.14 8 Water 21.76 9 Granhydrogel O ™ 6.40 10 Jeechem BUGL ™ 3.2011 Sodium Chloride 0.32 12 Neolone PE ™ 0.32 13 Iron Oxide Tint 0.01Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 7 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 8 to 12 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 0.13 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55b

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-11 ™ 8.17 3 Andisil VS 10,000 ™ 30.33 4 Andisil VS165,000 ™ 7.10 5 Andisil XL-11 ™ 5.49 6 Aerosil R8200 ™ 12.26 7 Sepiplus400 ™ 1.14 8 Water 21.76 9 Granhydrogel O ™ 6.40 10 Jeechem BUGL ™ 3.2011 Sodium Chloride 0.32 12 Neolone PE ™ 0.32 Iron Oxide Tint 13 Mixture0.01

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 7 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 8 to 12 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 13 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55c

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.17 3 Andisil VS 500 ™ 0.84 4 Andisil MV 2,000 ™1.29 5 Andisil VS 65,000 ™ 21.04 6 Andisil XL-1B ™ 17.82 7 AerosilR8200 ™ 14.20 8 Sepiplus 400 ™ 1.14 9 Water 21.76 10 Granhydrogel O ™6.40 11 Jeechem BUGL ™ 3.20 12 Sodium Chloride 0.32 13 Neolone PE ™ 0.3214 Iron Oxide Tint 0.01 Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 8 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 9 to 13 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 14 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55d

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.17 3 Andisil VS 250 ™ 1.29 4 Andisil MV 2,000 ™1.94 5 Andisil VS 20,000 ™ 24.52 6 Andisil CE-4 ™ 1.94 7 Andisil XL-1B ™0.33 8 Andisil XL-11 ™ 10.97 9 Aerosil R8200 ™ 14.20 10 Sepiplus 400 ™1.14 11 Water 21.76 12 Granhydrogel O ™ 6.40 13 Jeechem BUGL ™ 3.20 14Sodium Chloride 0.32 15 Neolone PE ™ 0.32 16 Iron Oxide Tint 0.01Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 10 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 11 to 15 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 16 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 ram propeller at 1000 rpm until homogenous.

Formulation 79-55e

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.17 3 Andisil VS 250 ™ 1.29 4 Andisil MV 2,000 ™1.94 5 Andisil VS 65,000 ™ 22.91 6 Andisil XL-1B ™ 6.78 7 AndisilXL-11 ™ 8.07 8 Aerosil R8200 ™ 14.20 9 Sepiplus 400 ™ 1.14 10 Water21.76 11 Granhydrogel O ™ 6.40 12 Jeechem BUGL ™ 3.20 13 Sodium Chloride0.32 14 Neolone PE ™ 0.32 15 Iron Oxide Tint 0.01 Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 9 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 10 to 14 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 15 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55f

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.17 3 Andisil VS 250 ™ 1.34 4 Andisil VS65,000 ™ 23.74 5 Andisil XL-1B ™ 7.03 6 Andisil XL-11 ™ 8.36 7 AerosilR8200 ™ 14.71 8 Sepiplus 400 ™ 1.14 9 Water 21.76 10 Granhydrogel O ™6.40 11 Jeechem BUGL ™ 3.20 12 Sodium Chloride 0.32 13 Neolone PE ™ 0.3214 Iron Oxide Tint 0.01 Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 8 were added and mixed with a dual,asymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 9 to 13 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 14 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 79-55g

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.17 3 Andisil VS 250 ™ 1.29 4 Andisil MV 2,000 ™1.94 5 Andisil VS 20,000 ™ 22.91 6 Andisil XL-1B ™ 6.78 7 AndisilXL-11 ™ 8.07 8 Aerosil R8200 ™ 14.20 9 Sepiplus 400 ™ 1.14 10 Water21.76 11 Granhydrogel O ™ 6.40 12 Jeechem BUGL ™ 3.20 13 Sodium Chloride0.32 14 Neolone PE ™ 0.32 15 Iron Oxide Tint 0.01 Mixture

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 9 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 10 to 14 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 15 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 83-54

Percent of Component Formulation No. Component (%) 1 Andisil VS 10,000 ™27.58 2 Andisil VS 165,000 ™ 6.46 5 Andisil XL-11 ™ 13.50 6 AerosilR8200 ™ 17.50 7 Labrafac CC ™ 3.00 7 Sepiplus 400 ™ 1.44 8 Water 29.29 9Plantacare 818UP ™ 0.50 11 Sodium Chloride 0.36 12 Neolone PE ™ 0.36 13Iron Oxide Tint 0.01 Mixture

Procedure:

Components 1 to 7 were added and mixed with a dual asymmetriccentrifugal mixer at 2500 RPM for 6 minutes until particulates are nolonger visible (Mixture A). In a separate vessel, components 8 to 12were mixed with a 4-blade, 40 mm propeller at 550 rpm until homogenous(Mixture B). Mixture B was added to Mixture A dropwise while mixing witha 4-blade 40 mm propeller at 400 rpm and the mixture was confirmed ashomogenous. Component 13 was added to the product of Mixture A andMixture B and mixed with 4-blade 40 mm propeller at 1000 rpm untilhomogenous.

Formulation 79-55h

Percent of Component Formulation No. Component (%) 1 Gransil EP-LS ™3.50 2 Andisil XL-1B ™ 8.15 3 Andisil VS 250 ™ 1.25 4 Andisil MV 2,000 ™1.85 5 Andisil VS 20,000 ™ 24.40 6 Andisil CE-4 ™ 1.85 7 Andisil XL-1B ™0.30 8 Andisil XL-11 ™ 10.80 9 Aerosil R8200 ™ 14.20 10 Sepiplus 400 ™1.14 11 Water 21.50 12 Granhydrogel O ™ 6.30 13 Jeechem BUGL ™ 3.15 14Sodium Chloride 0.30 15 Neolone PE ™ 0.30 16 Beaver UV/Fluorescent 1.00Pigment

Procedure:

Components 1 and 2 were combined and homogenized until smooth at 20000RPM (Mixture A). Components 3 to 10 were added and mixed with a dualasymmetric centrifugal mixer at 2500 RPM for 6 minutes untilparticulates are no longer visible (Mixture B). Mixture A and Mixture Bwere combined and centrifuge mixed for 6 minutes at 2500 RPM (MixtureA+B). In a separate vessel, components 11 to 15 were mixed with a4-blade, 40 mm propeller at 550 rpm until homogenous (Mixture C).Mixture C was added to Mixture A+B dropwise while mixing with a 4-blade40 mm propeller at 400 rpm and the mixture was confirmed as homogenous.Component 15 was added to the product of Mixture A+B and Mixture C andmixed with 4-blade 40 mm propeller at 1000 rpm until homogenous.

Formulation 81-18

Component Percent of No. Component Formulation (%) 1 Dow 9011 Elastomer10.45 Blend 2 Dow 9045 Elastomer 10.45 Blend 3 Dow 245 Fluid 8.4 4Jeensilc CPS-312 2.09 5 PT-50175F 1.00 6 Water 30.33 7 Plantacare 818 UP0.55 8 Neolone PE 0.21 9 Propylene Glycol 20.87 10 Glycerin 4.16 11Jeechem BUGL 10.44 12 Sodium Chloride 1.05

Procedure:

Components 1-5 were mixed in a glass beaker at 2000 rpm with 4-blade 40mm propeller for 2 minutes until mixture was homogeneous (Mixture A).Separately, components 6-12 were mixed until homogenous (Mixture B).Mixture B was added to Mixture A under strong agitation provided by a4-blade, 40 mm propeller at 2000 rpm until homogeneous. The finalformulation was further homogenized for 2 minutes.

Formulation 81-19

Component Percent of No. Component Formulation (%) 1 Dow 9011 Elastomer10.45 Blend 2 Dow 9045 Elastomer 10.45 Blend 3 Dow 245 Fluid 8.4 4Jeensilc CPS-312 2.09 5 PT-50175F 1.00 6 Water 29.83 7 Plantacare 818 UP0.55 8 Neolone PE 0.21 9 Propylene Glycol 20.87 10 Glycerin 4.16 11Jeechem BUGL 10.44 12 Sodium Chloride 1.05 13 Nylon 10-12 0.5

Procedure:

Components 1-5 were mixed in a glass beaker at 2000 rpm with 4-blade 40mm propeller for 2 minutes until mixture was homogeneous (Mixture A).Separately, components 6-12 were mixed until homogenous (Mixture B).Mixture B was added to Mixture A under strong agitation provided by a4-blade, 40 mm propeller at 2000 rpm until homogeneous. Component 13 wasthen added and the resulting mixture was homogenized for 2 minutes.

Formulation 81-20

Component Percent of No. Component Formulation (%) 1 Dow 9011 Elastomer10.45 Blend 2 Dow 9045 Elastomer 10.45 Blend 3 Dow 245 Fluid 8.4 4Jeensilc CPS-312 2.09 5 PT-50175F 1.00 6 Water 29.33 7 Plantacare 818 UP0.55 8 Neolone PE 0.21 9 Propylene Glycol 20.87 10 Glycerin 4.16 11Jeechem BUGL 10.44 12 Sodium Chloride 1.05 13 Nylon 10-12 1.0

Procedure:

Components 1-5 were mixed in a glass beaker at 2000 rpm with 4-blade 40mm propeller for 2 minutes until mixture was homogeneous (Mixture A).Separately, components 6-12 were mixed until homogenous (Mixture B).Mixture B was added to Mixture A under strong agitation provided by a4-blade, 40 mm propeller at 2000 rpm until homogeneous. Component 13 wasthen added and the resulting mixture was homogenized for 2 minutes.

Formulation 81-21

Component Percent of No. Component Formulation (%) 1 Dow 9011 Elastomer10.45 Blend 2 Dow 9045 Elastomer 10.45 Blend 3 Dow 245 Fluid 8.4 4Jeensilc CPS-312 2.09 5 PT-50175F 1.00 6 Water 27.33 7 Plantacare 818 UP0.55 8 Neolone PE 0.21 9 Propylene Glycol 20.87 10 Glycerin 4.16 11Jeechem BUGL 10.44 12 Sodium Chloride 1.05 13 Nylon 10-12 3.0

Procedure:

Components 1-5 were mixed in a glass beaker at 2000 rpm with 4-blade 40mm propeller for 2 minutes until mixture was homogeneous (Mixture A).Separately, components 6-12 were mixed until homogenous (Mixture B).Mixture B was added to Mixture A under strong agitation provided by a4-blade, 40 mm propeller at 2000 rpm until homogeneous. Component 13 wasthen added and the resulting mixture was homogenized for 2 minutes.

Formulation 79-74

Percent of Component Formulation No. Component (%) 1 Andisil VS 10,000 ™27.58 2 Andisil VS 165,000 ™ 6.46 5 Andisil XL-11 ™ 13.50 6 AerosilR8200 ™ 17.50 7 Schercemol ™ 318 Ester 3.00 7 Sepiplus 400 ™ 1.44 8Water 29.29 9 Plantacare 818UP ™ 0.50 11 Sodium Chloride 0.36 12 NeolonePE ™ 0.36 13 Iron Oxide Tint Mixture 0.01

Procedure:

Components 1 to 7 were added and mixed with a dual asymmetriccentrifugal mixer at 2500 RPM for 6 minutes until particulates are nolonger visible (Mixture A). In a separate vessel, components 8 to 12were mixed with a 4-blade, 40 mm propeller at 550 rpm until homogenous(Mixture B). Mixture B was added to Mixture A dropwise while mixing witha 4-blade 40 mm propeller at 400 rpm and the mixture was confirmed ashomogenous. Component 13 was added to the product of Mixture A andMixture B and mixed with 4-blade 40 mm propeller at 1000 rpm untilhomogenous.

Pigment Dispersion Formulation 80-23

Component Percent of No. Component Formulation (%) 1 Dow 9011 Elastomer10 Blend 2 Dow 9045 Elastomer 10 Blend 3 Dow 245 Fluid 10 4 Water 27 5Plantacare 818 UP 0.5 6 Neolone PE 0.5 7 Propylene Glycol 20 8 Glycerin4 9 Jeechem BUGL 10 10 Sodium Chloride 1 11 Nylon 4.5 12 Tint 2.5

Procedure:

Components 1-3 were mixed in a glass beaker at 2000 rpm with 4-blade 40mm propeller for 2 minutes until homogenous (Mixture A). Separately,components 5-10 were mixed until homogenous (Mixture B). Mixture wasadded B to Mixture A under strong agitation, provided by a 4-blade, 40mm propeller at 2000 rpm until homogeneous. Components 11 and 12 werethen added and mix at 200 rpm and until homogeneous. The final mixturewas then homogenized for 2 minutes.

Formulation 79-88

Percent of Component Formulation No. Component (%) 1 Andisil VS 10,000 ™27.59 2 Andisil VS 165,000 ™ 6.46 3 Andisil XL-11 ™ 13.50 4 AerosilR8200 ™ 17.50 5 Labrafac CC ™ 3.00 6 Sepiplus 400 ™ 1.44 7 Water 29.29 8Plantacare 818UP ™ 0.50 9 Sodium Chloride 0.36 10 Neolone PE ™ 0.36

Procedure:

Components 1 to 4 were combined and mixed with KitchenAid mixer for 5hours. Subsequently the mixture was vacuumed overnight. Components 5 and6 were then added and the mixture was homogenized in a dual asymmetriccentrifugal mixer at 2500 RPM. In a separate vessel, components 7 to 10were mixed with a 4-blade, 40 mm propeller at 550 rpm until homogenous(Mixture B). Mixture B was added to Mixture A dropwise while mixing witha 4-blade 40 mm propeller at 500 rpm and the mixture was confirmed ashomogenous.

Formulation 79-88-3A.

Percent of Component Formulation No. Component (%) 1 Andisil VS 10,000 ™27.59 2 Andisil VS 165,000 ™ 6.46 3 Andisil XL-11 ™ 13.50 4 AerosilR8200 ™ 17.50 5 Labrafac CC ™ 3.00 6 Simulgel EG ™ 1.44 7 Water 29.29 8Plantacare 818UP ™ 0.50 9 Sodium Chloride 0.36 10 Neolone PE ™ 0.36

Procedure:

Components 1 to 4 were combined and mixed with KitchenAid mixer for 5hours. Subsequently the mixture was vacuumed overnight. Components 5 and6 were then added and the mixture was homogenized in a dual asymmetriccentrifugal mixer at 2500 RPM. In a separate vessel, components 7 to 10were mixed with a 4-blade, 40 mm propeller at 550 rpm until homogenous(Mixture B). Mixture B was added to Mixture A dropwise while mixing witha 4-blade 40 mm propeller at 500 rpm and the mixture was confirmed ashomogenous.

Formulation 79-74-RD

Percent of Component Formulation No. Component (%) 1 Andisil VS 500 ™0.52 2 Andisil MV 2000 ™ 0.80 3 Andisil VS 65,000 ™ 13.04 4 AndisilXL-1B ™ 16.84 5 Aerosil R8200 ™ 8.80 6 Water 50.00 7 Veegum Pro 4.00 8Solagum AX 1.00 9 Dow Corning 5329 5.00

Procedure:

Components 1 to 5 were combined and mixed under vacuum (Mixture A). In aseparate vessel, components 6 to 7 were mixed with a 4-blade, 40 mmpropeller at 550 rpm until the mixture was homogenous and theparticulates were fully wetted (Mixture B). Component 8 was added toMixture B and mixed in with a 4-blade 40 mm propeller at 500 rpm untilthe mixture thickened and became homogenous. Component 9 was added toMixture B and mixed in with a 4-blade 40 mm propeller at 500 rpm for 10minutes. Mixture A was added slowly to Mixture B under continuous mixingat 500 rpm. The product was homogenized for 5 minutes at 10,000 rpm.

Formulation 79-90-B

Percent of Component Formulation No. Component (%) 1 Andisil VS 500 ™0.68 2 Andisil MV 2000 ™ 1.04 3 Andisil VS 65,000 ™ 16.95 4 AndisilXL-1B ™ 21.89 5 Aerosil R8200 ™ 11.44 6 Water 40.00 7 Veegum Pro 4.00 8Solagum AX 1.00 9 Dow Corning 5329 3.00

Procedure:

Components 1 to 5 were combined and mixed under vacuum (Mixture A). In aseparate vessel, components 6 to 7 were mixed with a 4-blade, 40 mmpropeller at 550 rpm until the mixture was homogenous and theparticulates were fully wetted (Mixture B). Component 8 was added toMixture B and mixed in with a 4-blade 40 mm propeller at 500 rpm untilthe mixture thickened and became homogenous. Component 9 was added toMixture B and mixed in with a 4-blade 40 mm propeller at 500 rpm for 10minutes. Mixture A was added slowly to Mixture B under continuous mixingat 500 rpm. The product was homogenized for 5 minutes at 10,000 rpm.

Formulation 88-70

Component Percent of No. Component Formulation (%) 1 Andisil VS10,00028.7% 2 Andisil  6.7% VS165,000 3 Andisil XL-11 14.0% 5 Aerosil R820018.2% 6 KF6013  2.1% 7 TMF 1.5  2.3% 8 USG 102  2.3% 9 DI water 22.3% 10Glycerin  1.1% 11 Jeen BUGL  1.2% 12 Jeecide Cap-5  1.0%

Procedure:

Components 1-8 (part A) and components 9-11 (part B). Part B wasintroduced to part A while mixing part A with a flat propeller blade at500 RPM. The resulting solution was mixed until a uniform emulsionformed. Component 12 was subsequently added to the emulsion.

Formulation 88-72

Component Percent of No. Component Formulation (%) 1 Andisil VS10,00028.60% 2 Andisil  6.69% VS165,000 3 Andisil XL-11 13.99% 5 Aerosil R820018.16% 6 KF6013  2.08% 7 TMF 1.5  2.25% 8 USG 102  2.35% 9 Pink tint mix 0.02% 10 DI water 22.25% 11 Glycerin  1.16% 12 Jeen BUGL  1.24% 13Veegum Ultra  0.11% Granules 14 Kaolin USP  0.10% BC2747 15 JeecideCap-5  1.00%

Procedure:

Components 1-9 (Phase A) were mixed separately from components 10-14(Phase B). Phase B was added to Phase A while mixing at 500 RPM using a4 paddle mixing blade, followed by homogenization using a Silversonhomogenizer for 1 hour at 3000 to 5000 RPM. Subsequently, component 15was added using mixing blade at 200 rpm.

Formulation 88-75-2

Percent of Component Formulation No. Component (%) 1 Andisil VS10,00021.39% 2 Andisil  5.00% VS165,000 3 Andisil XL-11 10.47% 4 Aerosil R820013.58% 5 RM2051  1.95% 6 DC 556  3.12% 7 FZ3196  3.11% 8 Squalane  1.85%9 USG 102  6.90% 10 Jeechem BUGL  1.85% 11 DI water 29.03% 12 PolyglycolP425  1.22% 13 Jeecide Cap-5  0.52%

Procedure:

Components 1-4 (Phase A) were mixed. Separately, components 5-9 werealso mixed (Phase B) until a uniform dispersion was formed. Components10-12 (Phase C) were also mixed separately. Phase C was slowlyintroduced into Phase B, while mixing at 700 RPM with 4 blade propellerrod to create a uniform emulsion (Phase D). Phase D was slowlyintroduced into Phase A at 700 RPM until uniform, and the resultingformulation was mixed for 5 minutes. Component 13 was added and mixedfor 2 minutes.

Formulation 88-75-3

Percent of Component Formulation No. Component (%) 1 Andisil VS10,00018.64% 2 Andisil  4.36% VS165,000 3 Andisil XL-11  9.12% 4 Aerosil R820011.84% 5 RM2051  2.21% 6 DC 556  3.53% 7 FZ3196  3.52% 8 Squalane  2.10%9 USG 102  7.81% 10 Jeechem BUGL  2.10% 11 DI water 32.85% 12 PolyglycolP425  1.38% 13 Jeecide Cap-5  0.54%

Procedure:

Components 1-4 (Phase A) were mixed. Components 5-9 (Phase B) were mixedseparately from Phase A until a uniform dispersion was formed.Components 10-12 (Phase C) were also mixed separately from Phase A andPhase B. Phase C was slowly introduced into Phase B, while mixing at 700RPM with 4 blade propeller rod to create a uniform emulsion (Phase D).Phase D was Slowly introduced to Phase A at 700 RPM until uniform, andmixed for 5 minutes. Component 13 was then introduced to the resultingformulation and mixed for 2 minutes, followed by homogenization at 5000RPM for 15 minutes.

Formulation 88-80

Percent of Component Formulation No. Component (%) 1 Andisil VS10,00012.72% 2 Andisil  2.98% VS165,000 3 Andisil XL-11  6.23% 4 Aerosil R8200 8.08% 5 RM2051  2.79% 6 DC 556  4.45% 7 FZ3196  4.44% 8 Squalane  2.64%9 USG 102  9.85% 10 Jeechem BUGL  2.64% 11 DI water 41.44% 12 PolyglycolP425  1.74% 13 Jeecide Cap-5 0.005%

Procedure:

Components 1-4 (Phase A) were mixed. Components 5-9 (Phase B) were mixedseparately from Phase A until a uniform dispersion was formed.Components 10-12 (Phase C) were also mixed separately from Phase A andPhase B. Phase C was slowly introduced into Phase B, while mixing at 700RPM with 4 blade propeller rod to create a uniform emulsion (Phase D).Component 13 was added to Phase D and mixed for 2 minutes. The resultingemulsion was lowly introduced into Phase A at 700 RPM until uniform, andmixed for 5 minutes, followed by homogenization at 9000 RPM for 7minutes.

Formulation 88-85-1

Percent of Component Formulation No. Component (%) 1 RM 2051  3.28% 2 FZ3196  4.92% 3 USG 102 12.11% 4 water 48.83% 5 Jeecide CAP-5  0.87% 6Andisil VS10,000 12.72% 7 Andisil  2.98% VS165,000 8 Andisil XL-11 6.23% 9 Aerosil R8200  8.08%

Procedure:

Components 1-3 (Phase A) were mixed. Component 4 was added while mixingPhase A, until a white emulsion formed. Components 6-9 (Phase B) weremixed and Phase B was subsequently added to the emulsion and mixed for 5minutes at 1300 RPM. The resulting formulation was homogenized(Silverson) for 5 minutes and component 5 was added, followed by mixingfor 2 minutes at 700 RPM with a propeller blade.

Formulation 88-85-2

Percent of Component Formulation No. Component (%) 1 RM 2051  2.62% 2 FZ3196  3.93% 3 USG 102  9.68% 4 water 39.03% 5 Jeecide CAP-5  0.78% 6Andisil VS10,000  18.6% 7 Andisil  4.4% VS165,000 8 Andisil XL-11  9.1%9 Aerosil R8200  11.8%

Procedure:

Components 1-3 (Phase A) were mixed. Component 4 was added while mixingphase A until a white emulsion formed. Components, 6-9 (Phase B) weremixed separately and subsequently added to the emulsion while mixing at1300 RPM for 5 minutes. The mixture was homogenized (Silverson) for 5minutes. Component 5 was added and the resulting formulation was mixedfor 2 minutes at 700 RPM with a propeller blade.

Formulation 88-83-V2

Percent of Component Formulation No. Component (%) 1 RM 2051  3.3% 2 FZ3196  3.3% 3 DC 2-1184 fluid 10.0% 4 USG 102  3.3% 5 water 46.3% 6Jeecide CAP-5  0.3% 7 Andisil VS10,000 14.1% 8 Andisil  3.3% VS165,000 9Andisil XL-11  6.9% 10 Aerosil R8200  9.0%

Procedure:

Components 1-4 were mixed (Phase A), followed by addition of component5, until a white emulsion formed. Component 6 was added to the emulsionand mixed for 5 minutes (emulsion base). Components 7-10 (Phase B) weremixed separately and added to the emulsion base at 1300 RPM, followed bymixing for 5 minutes and homogenization (Silverson) for 10 minutes.

Formulation 88-83-V3

Percent of Component Formulation No. Component (%) 1 RM 2051  3.3% 2 DC2-1184 fluid 13.3% 3 water 49.7% 4 Jeecide CAP-5  0.3% 5 AndisilVS10,000 14.1% 6 Andisil VS165,000  3.3% 7 Andisil XL-11  6.9% 8 AerosilR8200  9.0%

Procedure:

Components 1 and 2 were mixed (Phase A), followed by addition ofcomponent 3, until a white emulsion formed. Component 4 was added to theemulsion and mixed for 5 minutes (emulsion base). Components 5-8 (PhaseB) were mixed separately and added to the emulsion base at 1300 RPM,followed by mixing for 5 minutes and homogenization (Silverson) for 10minutes.

Formulation 83-54

Reactive constituent and Reinforcing constituent composition (Vinyl,hydride, fumed silica) weight ranges Tradename Description percent lowerupper Andisil VS10,000  0.05 mmol/g vinyl, 10,000 cSt  42.40% 30 50Andisil VS165,000 0.015 mmol/g vinyl, 165,000 cSt  9.92% 5 15 AndisilXL-11  4.35 mmol/g. 45 cSt  20.75% 10 30 Aerosil R8200 Silica Silylate 26.93% 20 34 total 100.00% Reactive Reinforcing Component RM 2051Thickening Sodium Polyacrylate (and)  3.63%  3.00%  5.00% AgentDimethicone (and) Cyclopentasiloxane (and) Trideceth-6 (and) PEG/PPG-18/18 Dimethicone Gransurf 90 Cetyl PEG/PPG-10/1  0.50%  0.20%  2.00%Dimethicone PMX-1184 dimethicone and trisiloxane  13.63% 10.00% 40.00%Water N/A  46.00% 20.00% 60.00% Vitamin-C complex Ascorbic Acid  0.08% 0.05%  0.50% Jeecide CAP-5 Phenoxyethanol, Caprylyl  0.33%  1.00%Glycol, Potassium Sorbate, Aqua, Hexylene Glycol Tween 20 Polysorbate 20 0.33%  5.00% Vitamin-A complex Vitamin A Palmitate 1.7  0.40%  5.00%MIU/g Vitamin-E complex Vitamin E Acetate  0.10%  5.00% Reactiveconstituent and N/A  35.00% 30.00% 60.00% Reinforcing constituentcomposition (Vinyl, hydride, fumed silica) from above total 100.00%

Procedure:

Formulation 83-54 was prepared by a procedure similar to 88-83-V3.Andisil VS10,000, Andisil VS165,000, Andisil XL-11 were obtained fromAnderson and Associates, Aerosil R8200 was obtained from Evonik, and thefour components were mixed by Crisil. RM 2051 Thickening Agent andPMX-1184 were obtained from Dow. Gransurf 90 was obtained from Grant.Vitamin-C complex and Vitamin A comples were obtained from DSM. JeecideCAP-5 was obtained from Jeen. Tween 20 was obtained from Croda.Vitamin-E complex was obtained from TRI-K.The cross-linking component second step includes formulations 60-148-99,60-144-San 86-114, and 86-141c shown below.

Formulation 60-148-99

Component Percent of No. Component Formulation (%) 1 Water 28.60 2Plantacare 818UP 0.49 3 Propylene Glycol 19.72 4 Glycerin 3.94 5 JeechemBUGL 9.86 6 Sodium Chloride 0.99 7 Dow Elastomer 9.86 Blend 9011 8 DowElastomer 9.86 Blend 9041 9 Dow 245 Fluid 7.89 10 Jeensilc CPS-312 1.9711 Nylon 10-12 4.64 12 Chronosphere 0.18 Optical Brite 13 Platinumdivinyl 1.00 complex PC 075.3

Procedure:

Components 1-6 were combined and mixed at 750 RPM for two minutes with a4-blade 40 mm propeller until homogenous to create an aqueous phase. Ina separate container components 7-10 were mixed at 750 RPM for twominutes with a 4-blade 40 mm propeller until homogenous to create aSilicon Mixture A. To the aqueous phase, components 11 and 12 were addedand mixed at 750 RPM with a 4-blade 40 mm propeller. The mixing speedwas increased to 1000 RPM and the mixture was mixed until homogenous andthickened. Component 13 was added and stirred at 1000 RPM for 1 minute,then homogenized at 25,000 RPM for 5 minutes.

Formulation 60-144-San

Component Percent of No. Component Formulation (%) 1 Water 67.47 2Carbopol Ultrez 1.01 21 3 Denatured Ethanol 29.35 190 Proof 4 Glycerin2.02 5 2% Sodium 0.20 Hydroxide 6 Platinum divinyl 1.99 complex 3% PC075.3

Procedure:

Components 1 and 2 were gently blended with a 4-blade 40 mm propellerblade at 250 RPM until the Carbopol was completely wetted and themixture was free of white particulates. Components 3 and 4 were addedunder moderate agitation provided by a 4-blade 40 mm propeller at 500RPM. Component 5 was added dropwise under moderate agitation provided bya 4-blade 40 mm propeller at 550 RPM until the mixture was homogenousand thickened. Component 6 was added under moderate agitation providedby a 4-blade 40 mm propeller at 550 RPM, followed by mixing at 1000 RPMfor 5 minutes until the mixture was homogoneous.

Formulation 86-114 and 86-141c

weight Tradename Description percent Supplier lower upper PlatinumDivinyl Karstedt's catalyst in  1.00% Umicore 0.50%  2.50% Complex 2%PT- stabilizing vinyl- 50175F (CAS# dimethicone 68478-92-2, 2627- 95-4,68083-19-2)  1.00% total 86-114 Crosslinking Component # 1 Dow 9011Cyclopentasiloxane (and)  10.00% Dow 5.00% 20.00% Elastomer Blend PEG-12Dimethicone Corning CrossPolymer Dow 9045 Cyclopentasiloxane and  10.00%Dow 5.00% 20.00% Elastomer Blend Dimethicone Corning Crosspolymer PMX-0245 Cyclopentasiloxane  10.00% Dow 5.00% 25.00% Corning Water  28.50%NA — 90.00% Sodium Chloride Sodium Chloride  1.00% Spectrum —  5.00%Plantacare 818 UP Coco-Glucoside  0.50% Cognis —  4.00% Tween 20Polysorbate 20  0.00% Cognis —  2.00% Propylene Glycol Propylene Glycol 20.00% Ruger — 40.00% Chemical Co Lipo Polyglycol ® PEG-4  0.00% Lipo —40.00% 200 Chemicals Inc Glycerin Glycerin  4.00% Ruger — 10.00%Chemical Co Jeechem BUGL 1,3-Butylene Glycol  10.00% Jeen — 50.00% Nylon10-12 Nylon 12 and Isopropyl  4.50% KOBO — 15.00% TitabiumTriisostearate Jeecide CAP-5 Phenoxyethanol,  0.50% Jeen —  2.00%Caprylyl Glycol, Potassium Sorbate, Aqua, Hexylene Glycol PT-50175FPlatinum  1.00% Umicore 0.50%  2.50% Divinyldisiloxane total 100.00%total 86-141c Crosslinking Component #2 KSG-240 Dimethicone/PEG-10/15 10.00% Shin Etsu 3.00% 20.00% Crosspolymer DC 9045 Cyclopentasiloxaneand  7.50% Dow 25.00% Dimethicone Corning Crosspolymer KF-995Cyclopentasiloxane  11.50% Shin Etsu 25.00% KF-6028 PEG-9  1.00% ShinEtsu 4.00% Polydimethylsiloxyethyl Dimethicone Water  28.25% NA 90.00%Sodium Chloride Sodium Chloride  1.00% Spectrum  5.00% Plantacare 818 UPCoco-Glucoside  0.50% Cognis  4.00% Tween 20 Polysorbate 20  0.00%Cognis  2.00% Propylene Glycol Propylene Glycol  20.00% Ruger 40.00%Chemical Co Lipo Polyglycol ® PEG-4  0.00% Lipo — 40.00% 200 ChemicalsInc Glycerin Glycerin  4.00% Ruger 10.00% Chemical Co Jeechem BUGL1,3-Butylene Glycol  10.00% Jeen 50.00% Nylon 10-12 Nylon 12 andIsopropyl  4.50% KOBO 15.00% Titabium Triisostearate Jeecide CAP-5Phenoxyethanol,  0.50% Jeen  2.00% Caprylyl Glycol, Potassium Sorbate,Aqua, Hexylene Glycol PT-50175F Platinum  1.25% Umicore  2.50%Divinyldisiloxane 100.00% total

Procedure for 86-114:

Components 1-3 were combined and mixed at 750 RPM for two minutes withuntil homogenous to create an silicone phase. In a separate containercomponents 4-11 and 13 were mixed at 750 RPM for 15 minutes with a untilhomogenous to create a water phase. The water phase was added slowly tothe silicone phase and mixed at 750 RPM. The mixing speed was increasedto 2000 RPM and the mixture was mixed until homogenous and thickened.Component 12 was added and stirred at 1000 RPM for 5 minutes. Component14 was added and stirred at 1000 RPM for 5 minutes.

Procedure for 86-141c:

Components 1-4 were combined and mixed at 750 RPM for two minutes withuntil homogenous to create an silicone phase. In a separate containercomponents 5-12 and 14 were mixed at 750 RPM for 15 minutes with a untilhomogenous to create a water phase. The water phase was added slowly tothe silicone phase and mixed at 750 RPM. The mixing speed was increasedto 2000 RPM and the mixture was mixed until homogenous and thickened.Component 13 was added and stirred at 1000 RPM for 5 minutes. Component15 was added and stirred at 1000 RPM for 5 minutes.

Example 6 A 2 Day, Double-Blinded Study Evaluating 2 DifferentFormulations to Achieve a Cosmetic Benefit on Aged Skin Purpose:

The goal of the study was to identify the lead candidates, of 2different formulation candidates, to advance to a subsequentconfirmatory clinical study. Selection criteria was based on theimmediately visualizable improvements in the appearance of fine lines,evenness in skin tone, skin texture and pores, as well as the durationof the effect over a six hour period. An additional goal was todetermine the ease of application of each formulation for a typical userwhen self-applying.

Background:

This trial was an early stage development project focused on bringingpolysiloxane based reactive systems to topical human use studies.Currently, the performance evaluation studies have been restricted tosupervised, limited-use applications. The systems evaluated consisted ofvinyl terminated polysiloxanes, silicon hydride functionalizedpolysiloxanes, fumed silica particles, and a platinum catalyst. In thesestudies, the polysiloxane systems were applied to the skin surface andcured by the addition of the platinum catalyst.

Test Material Composition:

The formulation compositions under consideration generally consisted ofthe following ingredients:

-   -   vinyl terminated polysiloxane,    -   hydride functional polysiloxane,    -   fumed silica particles,    -   platinum catalyst, and    -   Commercially available cosmetic ingredients.

The polysiloxanes under consideration all exceeded a molecular weight of600 Daltons. The percent compositions of the polysiloxanes evaluated aresummarized in the table below. These represent the upper concentrationranges of the siloxane and fumed silica materials present in the totalformulation. For example, the addition of cosmetic ingredients at alevel of 50% would lead to a dilution of each ingredient by a factor of2, such that composition number 1 was a 35% vinyl terminatedpolysiloxane, 15% hydride functional polysiloxane, 0% fumed silica, and50% commercially available cosmetic ingredients. The platinum catalystin the final formulation was always present at concentrations less than500 ppm. The two treatments tested were formulations 60-140-1 and60-140-LX2 and the cross-linking component used was 60-148-99.

Subject Enrollment:

Number of subjects: Approximately 25 subjects were screened in order toenroll a total of 20 subjects to ensure that at least 15 subjectscompleted the study.

Informed Consent and Release Form: Two copies of a statement of informedconsent were given to each subject before the start of this study. Thesubject was given the opportunity to have her questions answered to hersatisfaction. However, if further questions existed, the subject wasgiven sufficient time on the first visit to clarify open questions andconcerns regarding the study and/or the informed consent with theinvestigator prior to signing.

Subject Identification: Subjects were assigned a three-digit numberwhich, when used in conjunction with the clinical study number, uniquelyidentified every subject in the study. This number remained with thesubject throughout the study.

Eligibility Criteria:

The Fitzpatrick skin classification is based on the unprotectedappearance response of the skin to the first 30 to 45 minutes of sunexposure after a winter season without sun exposure. The categories ofskin types are as follows:

-   -   I Always burns easily; never tans    -   II Always burns easily; tans minimally    -   III Burns moderately, tans gradually    -   IV Burns minimally; always tans well    -   V Rarely burns; tans profusely    -   VI Never burns; deeply pigmented

Inclusion:

-   1. 30-65 years old-   2. Female-   3. Fitzpatrick skin types I-IV-   4. Shows some visible sign of aging on the face including but not    limited to: large pores, fine lines and wrinkles, or poor skin    tone/texture-   5. Willingness to cooperate and participate by following study    requirements for the duration of the study and to report any adverse    symptoms immediately-   6. Little or no erythema due to sun exposure at the treatment site    at the time of treatment-   7. Able to refrain from using topical skin care products not    included in the study on the treatment areas during the course of    the study.

Exclusion:

-   1. Fitzpatrick skin types V-VI-   2. Individuals with a known history of allergy or sensitivity to the    cosmetic study cream ingredients-   3. Individuals with known atopic skin diseases or neurodermatitis-   4. Women known to be pregnant, nursing, or planning to become    pregnant within 6 months-   5. Individuals known to be treated for cancer or have a history of    cancer-   6. Individuals with observable sunburn, suntan, scars, uneven    tone/pigmentation, or other dermal conditions on the test areas that    might influence the test results-   7. Any active dermatologic condition(s) that might interfere with    clinical assessments (e.g., tattoos, eczema, psoriasis, rosacea,    acne, etc)

Study Procedure:

Table 2 below outlines the procedures performed each visit of the study:

TABLE 2 Day 1 Day 8 Day 1 time Day 8 time Order of Events on Each Day:time o 6+ hrs time o 6+ hrs Informed consent. qualify x Cosmetic productapplication history taken x Sensitivity to formulations test on arm xPanelist's face cleaned x x Baseline photograph taken x x Formulationsapplied x x After application photgraph taken x x After application liveevaluation taken x x After duration photograph taken x x After durationlive evaluations taken x x Test articles removed x x Moisturizer appliedx x

Preparation:

Prior to any panelist's arrival, the 2 formulations were randomized suchthat the investigator and photographer are not aware of the identity ofeach formulation.

Photography:

Panelists were photographed under two different lighting conditions(parallel polarized lighting and cross polarized lighting) and at twodifferent camera angles relative to the plane of the face (90°, 45°).Panelists were positioned in a facial positing system to reducedorsal-ventral rotation and to position the face in approximately thesame location relative to the camera each time. Refer to “Photo set upcapture” example in “Image analyses measures” section

Visit 1:

-   1. Upon arrival, individuals were evaluated against the    exclusion/inclusion criteria and were recruited for the study if    they met the requirements-   2. After recruitment, subjects were given a brief description of the    study and an informed consent form and signed (along with a witness)    after all questions about the study had been adequately answered-   3. After signing all the paperwork, subjects were assigned the next    available subject number-   4. The two formulations that were tested on that subject according    to the randomization scheme were then be applied by the investigator    in a small area on the subject's arm and allowed to remain for 5    minutes to determine any sensitivity to the products-   5. If the panelist was not sensitive to the product then they had    their face cleaned with a gentle facial cleanser-   6. After washing the face, a baseline photograph was taken of the    subject's whole face-   7. After the baseline photograph, the subject was asked to apply the    test materials to the entire upper half of her face (below eyes to    hairline, avoiding area below cheek bones), using the finger to    apply, under supervision-   8. The panelist was then photographed after 2-5 min to obtain the    after application photograph-   9. The panelist was then asked to complete a questionnaire about the    test products applied-   10. The investigator completed a live-evaluation of the panelist for    efficacy against baseline-   11. The panelist was then be allowed to leave for 6-8 hours and    given the following instructions:    -   a. Do not rub or scratch the face    -   b. Do not shower or get the face wet    -   c. Do not apply additional products to the face    -   d. If any adverse event occurs in the area of application, the        panelist should call the investigator and come in for evaluation        and removal of the film.-   12. Once the panelist returned they were photographed and the    panelist and investigator completed evaluation forms-   13, If an expert live assessor was scheduled for that evening then    the panelist was instructed to wait until the assessment period at    which point the assessors graded the appearance of the panelist    against their baseline photograph-   14. After assessment the panelist was then given an assessment form    to leave their impressions and comments on each product-   15. After assessment was finished the panelist was then instructed    on the removal of the product using makeup remover and did so-   16. A commercial skin care moisturizer with SPF15 was then applied    to the panelist's face as a moisturizer-   17. The panelist was then dismissed

Visit 2:

-   1. Upon arrival, the panelist had their face cleaned with a gentle    facial cleanser-   2. After washing the face, a baseline photograph was be taken of the    subject's whole face-   3. After the baseline photograph, the subject was instructed on the    method of application (see below) for each formulation and allowed    to apply each formulation to the entire upper half of their face    according to the randomization scheme in Appendix A (switching the    side of application compared to the previous visit)-   4. The procedure then continued as in Visit 1 step 7

Photographic Analysis:

After the study concluded, the “baseline”, “after application”, and“after 6-8 hour” photographs were compiled into a blinded deck andsubmitted to an expert assessor to grade the extent of wrinkling in eachphotograph using the Griffiths scale exampled below:

-   -   0-1: No damage    -   2-3: Mild damage    -   4-5: Moderate damage    -   6-7: Moderate to severe damage    -   8-9: Severe damage

The deck was assembled such that the timepoint for the picture beingevaluated was not known. This was done to eliminate any bias for anexpected result from the evaluation. Because the Griffiths score is anabsolute one, differences from baseline were calculated afterwards inthe data analysis.

Results:

Evaluation Forms: From the Investigator Evaluation Forms a scale of −2,−1, 0, +1, +2 (for Strong Reduction/Lift, Some Reduction/Lift, NoReduction/Lift, Some Increase/Drop and Strong Increase/Drop), wascreated for all of the different parameters evaluated. For eachformulation, the average value on this scale was determined across thepanelists along with the standard deviation to give an indication ofperformance for each attribute being evaluated.

From the Assessor Evaluation Forms the same scale of −2, −1, 0, +1, +2were applied to obtain the same statistical data in regards to theevaluations it contained. From these average values and standarddeviations, confidence in the ability of each individual formula toaffect the parameter being investigated was determined.

Panelist Evaluation Forms were on a scale of −1, 0, +1 for eachattribute being evaluated. The average value on this scale wasdetermined per panelist both after application and after duration togive an indication of short and long term performance. The trending ofthis result was evaluated against the assessor and investigatorevaluation results for correlation.

Comments on all three forms were tracked and examined for anysimilarities. Because the expert assessor did not have an evaluation foreach week, only the investigator and panelist forms were compared acrossthe week for consistency in efficacy for each formulation despite theside of the face to which it was applied.

Photographic Analysis:

For the post-clinical photographic analysis, each picture was assigned aGriffiths score by the evaluator. The average change in this score fromthe corresponding baseline picture for each formulation gave anindication of its efficacy at smoothening the appearance of fine linesand wrinkles as well as creating a more youthful look. These resultswere compared to the live assessments for correlation.

Week 2 Results Overview:

As Table 3 below shows, 60-140-LX2 was far less durable compared to60-140-1.

TABLE 3 Formula % Didn't Fail n= 60-140-LX2 65.38% 26 60-140-1 86.84% 38

The Investigator assessment of the panelists revealed two significantdifferences between the performance of the two formulations (see FIG.3). Formulation 60-140-LX2 showed a significantly greater overallimprovement in the appearance of Forehead wrinkles. Conversely 60-140-1showed a significantly greater improvement in the appearance of UnderEye wrinkles. This is significant in that it confirmed the hypothesisthat a softer formulation should be applied to the thinner skin underthe eyes to achieve a positive result. Alternatively, because the skinis thicker on the forehead, a stiffer film may be needed to produce astronger wrinkle reduction. Mattification, reduction of Fine Wrinklesand Pore Reduction were the top three overall performers according tothe investigator assessments.

The assessors were able to distinguish differences in three attributesbetween the two formulations (see FIG. 4). Formulation 60-140-LX2 showeda significant increase in More Youthful Appearance and Natural Feel vs.60-140-1, while formulation 60-140-1 showed a significantly greater Lookof Tightening vs. 60-140-LX2. All other attributes showed no significantdifference between the two formulas. The top three attributes forgreatest overall change observed show that no matter what the formulamattification, reduced pores and improved fine wrinkles consistentlyshowed the largest noticeable improvement vs. baseline.

Panelist data showed no significant differences between the two formulastested (see FIG. 5). The top average scorer for 60-140-LX2 was the Lookof Tightening attribute. The difference between 60-140-LX2 and 60-140-1for this attribute was not significant (p˜0.24), but it was the mostsignificantly different attribute of those examined below. The samplesize was very small for this study so the difference may not have beensignificantly detectable without further testing. One hypothesis for whythis attribute stands above More Youthful Appearance, Extent ofWrinkling and Mattification is that the panelist's may have perceivedthe feeling of Tightness greatest in 60-140-LX2 thus rating that formulahigher than 60-140-1. Discounting this result, the top three performingattributes are More Youthful overall, Reduced Wrinkling andMattification. Pore size did not stand out among the panelists althoughfor both the assessors and investigators, this attribute was alwayshighly ranked. It may be that the panelists do not remember theirbaseline pore size.

Finally, assessors were asked to estimate the Panelist's age at eachassessment. The difference between this age and their real age was thencalculated and it was found that 60-140-LX2 had a more significanteffect on the age estimate by −8.7 years compared to −7.7 years with60-140-1. (see FIG. 6).

The Panelist's were also assessed on the Griffith's scale; using beforeand after pictures. FIG. 7 illustrates the average Griffith's scoreresult from the blinded evaluation of the panelist's photographs. Forthe two examples, the average Griffith's score was reduced by 2.15 andby 1.25 points, following application of formula 60-140-LX2 and60-140-1, respectively. This result is consistent with FIGS. 4 and 5,where panelists appeared younger following formulation application.

Study Investigator's Evaluation:

A significant improvement was observed in the reduced appearances ofwrinkles, pores and shine. The treatments using two formulationsselected from the first week (60-140-LX2 and 60-140-1) on the panelist'supper half face reduced appearance of fine wrinkles of the panelistsaccording to the study investigator evaluations. 60-140-LX2 reduced theappearance of fine wrinkles by 100% while 60-140-1 reduced them by 96%(Table 4). These formulations also reduced deep wrinkles but to a lesserextent (75% and 67% respectively) compared to fine wrinkles.

TABLE 4 Wrinkle A Reduction No Reduction Reductio

Target Seen or Worsene

Out of 60-140-LX2 Deep Wrinkles  75.49% 24.51% 102 Fine Wrinkles 100.00% 0.00%  78 60-140-1 Deep Wrinkles  67.11% 32.89% 152 Fine Wrinkles 95.76%  4.24% 118

indicates data missing or illegible when filed

Among different types of wrinkles, wrinkles on the forehead (94% and93%) and crow's feet (96% and 87%) areas were shown to be reduced themost by 60-140-LX2 and 60-140-1 formulations. Under eye wrinkles werealso shown to be moderately reduced (81% and 79%) along with theforehead frowning wrinkles (The deep #11's wrinkles), which were onlymarginally reduced (58% and 31%) (Table 5).

TABLE 5 Wrinkle A Reduction No Reduction Out Reductio

Target Seen or Worsene

of 60-140-LX2 Forehead Wrinkles 94.23%  5.77% 52 #11's Dp. Wrink.?58.33% 41.67% 24 Crows Feet Wrinkle

96.15%  3.85% 52 Under Eye Wrinkles 80.77% 19.23% 52 60-140-1 ForeheadWrinkles 92.50%  7.50% 80 #11's Dp. Wrink.? 31.25% 68.75% 32 Crows FeetWrinkle

87.18% 12.82% 78 Under Eye Wrinkles 78.75% 21.25% 80

indicates data missing or illegible when filed

The pores on the forehead appeared to reduce by 100% for both treatmentsand pores in the cheek also appeared to reduce by 50% and 67% upontreatment using 60-140-LX2 and 60-140-1 (Table 6).

TABLE 6 A Reduction No Reduction Out Pores Target Seen or Worsene

of 60-140-LX2 Forehead Pores? 100.00%  0.00% 26 Cheek Pores  50.00%50.00% 8 60-140-1 Forehead Pores? 100.00%  0.00% 40 Cheek Pores  66.67%33.33% 6

indicates data missing or illegible when filed

Both formulations reduced the appearance of shine on the panelists'treated skin (Table 6).

TABLE 7 A Reduction No Reduction or Out Shine? Seen Worsene

of 60-140-LX2 100.00% 0.00% 26 60-140-1  95.00% 5.00% 40

indicates data missing or illegible when filed

Overall the aesthetic performance of these two formulations wascomparable in terms of reduction in wrinkles, pores and shine. However,the mechanical performance showed the difference in terms of filmintactness and failure where the stiffer film showed failure modes likepeeling and cracking (see Tables 8 and 9)

TABLE 8 Formula % Didn't Fail Out of 60-140-LX2 65.38% 26 60-140-186.84% 38

TABLE 9 Other Issues Cracking Peeling Whitening Out of 60-140-LX2 26.92%11.54% 34.62% 26 60-140-1  2.63%  2.63% 44.74% 38

Formulation 60-140-1 showed greater film durability after formed on theskin surface and only about 13% showed film failure as determined byfilm cracking and peeling. 60-140-LX2, however, showed greater filmfailure (35%) indicating poor durability of the film when formed on theskin which resulted in more cases of film cracking (27%) and peeling(12%). In summary, 60-140-1 was able to provide an “all day” durablefilm and was a desirable skin care treatment for improving the skinappearance by reducing wrinkles, pores and shine.

Assessors' Evaluation:

The assessors' evaluation showed reduction of wrinkles, pores and shinein the panelists' applied skin. Wrinkle reduction by the treatment of60-140-LX2 and 60-140-1 were comparable (Table 10).

TABLE 10 Improved No Change or Wrinkles ShortQ Group Worsened Out of60-140-LX2 Overall Wrinkle

80.22% 19.78% 182 Deep Wrinkles 70.73% 29.27%  82 Fine Wrinkles? 88.00%12.00% 100 60-140-1 Overall Wrinkl

80.70% 19.30% 285 Deep Wrinkles 66.93% 33.07% 127 Fine Wrinkles? 91.77% 8.23% 158

indicates data missing or illegible when filed

The assessors noticed a great reduction in the pores (Table 11) and animprovement in mattification (Table 12) in the panelists' skin followingtreatment. The panelists' skin tone was also slightly improved and theskin looked tightened based on the evaluations from the assessors (Table11).

TABLE 11 Improved Group No Change or Worsened Out of Pore Size60-140-LX2 95.92%  4.08% 98 60-140-1 93.13%  6.88% 160 Skin Tone60-140-LX2 67.00% 33.00% 100 60-140-1 58.23% 41.77% 158 Looks Tight60-140-LX2 78.79% 21.21% 99 60-140-1 75.00% 25.00% 152

TABLE 12 Mattification Improved Group No Change or Worsened Out of60-140-LX2 99.00% 1.00% 100 60-140-1 98.13% 1.88% 160

While both formulations seemed to give a more youthful look to the skin,60-140-LX2 showed a greater improvement in creating a youthful look(90%) and having a natural feeling (86%) compared to the 60-140-1formulation (73% and 79% respectively) (Table 13). Striking observationswere also made on the tactile feelings of the treated skin with theseformulations.

TABLE 13 More Youthful? Improved Group No Change or Worsened Out of60-140-LX2 89.90% 10.10%  99 60-140-1 72.50% 27.50% 160 Natural LookingNatural Artificial or Very Artificial Out of 60-140-LX2 55.00% 45.00%100 60-140-1 55.00% 45.00% 160 Natural Feeling Natural Artificial orVery Artificial Out of 60-140-LX2 86.00% 14.00% 100 60-140-1 78.21%21.79% 156

Silky, Smooth and Soft are the top three descriptors that the assessorschose to describe the feeling of the treated skin. (Table 14)

TABLE 14 Feeling Desc: Rough Rubbery Silky Smooth Soft Tacky Dry Out of60-140-LX2 3.00% 20.00% 53.00% 69.00% 70.00% 2.00% 0.00% 100 60-140-13.13% 12.50% 56.25% 71.25% 78.13% 0.63% 0.63% 160

Example 7 Development of Cleanser to Remove Body Corrective Compositions

It was found that commercially available cleansers were not effective atremoving the film formed upon application of the body correctivecompositions of the invention. To evaluate the performance of thecleansers, the film was applied to facial skin of volunteers. Followingsix to eight hours, the cleanser was rubbed onto the film and left onthe film for 30 seconds. The subject was then instructed to remove thefilm with a towelette of a given surface roughness by gentle wiping theswollen film from the skin. The following commercially availableproducts were tested:

Philosophy Purity Made Simple

-   -   Shiseido Benefiance Creamy Cleansing foam    -   Noxema    -   Estee Lauder Perfectly Clean Splash Away Foaming Cleanser    -   Makeup forever sens'eyes    -   Loreal go 360clean deep    -   Clinique naturally gentle eye makeup remover    -   Olay Total Effects 7 in 1 antiaging cleanser    -   Olay dual action cleanser and pore scrub    -   Garnier Skin Renew    -   Lancome Bi-Facil double action make-up remover    -   Neutrogena deep clean invigorating foaming scrub    -   Olay regenerist daily regenerating cleanser    -   CVS pharmacy deep cleansing makeup remover    -   Neutrogena Ageless essentials Continuous Hydration Cream        Cleanser    -   CVS cleansing and makeup remover    -   Yes to cucumbers natural glow facial towelettes

As none of the aforementioned products were effective at removing thefilm, a cleanser was prepared to disrupt the mechanical integrity of thefilm and to facilitate the delivery of the cleanser components into thefilm. Without being bound by theory, the removal mechanism can bedescribed in four steps with key formula components for each stepindicated in parentheses:

-   -   1. Film wetting (Silsoft 034, Silsoft ETS, 5CS dimethicone)    -   2. Penetration of formula components (siloxane emulsifiers,        siloxane phase, glycols, Cremaphor EL)    -   3. Film swelling (Silsoft 034, Silsoft ETS, Isododecane, 5CS        dimethicone)    -   4. Film release from skin (glycols, water)

Silsoft 034, Silsoft ETS, 5CS dimethicone readily wet the surface of thefilm. The siloxane emulsifiers or the Cremaphor EL incorporate theaqueous phase into the siloxane phase, and may facilitate delivery ofthe film swelling components into the film. Silsoft 034, isododecane,and Silsoft ETS contribute to swelling the film and mechanicaldisruption. This enables penetration of the aqueous phase, hydration ofthe skin and reduction of the film's adhesion to the skin.

Tables 15-17; below, provide compositions that were effective inremoving the film:

TABLE 15 w/w gm siloxane phase Silsoft 034 (caprylyl methicone)  9.7% 5Isododecane 19.4% 10 Silsoft ETS (ethyl trisiloxane) 19.4% 10 AerogelVM2270  1.5% 0.763 siloxane emulsifiers Shin Etsu KSG 820  3.9% 2 ShinEtsu KF 6038  3.9% 2 aqueous phase propylene glycol  4.9% 2.5 butylenediglycol  4.9% 2.5 glycerol  1.9% 1 MPDiol  7.8% 4 DI water 19.4% 10neolone PE  0.5% 0.27 chronosphere optical brite  0.6% 0.3 granpowdernylon  2.1% 1.1

TABLE 16 Component Percent of No. Component Formulation (%) 1 Glycerin 3.00% 2 water 43.98% 3 dowanol DPM  6.00% 5 cremaphor EL  6.00% 6silsoft ETS 30.00% 7 DM5 CS 10.00% 8 prestige pearlescent  0.02% beige 9Jeecide cap 5  1.00%

TABLE 17 Percent of Component Formulation No. Component (%) 1 Glycerin 3.11% 2 water 46.23% 3 dowanol DPM  6.20% 4 cremaphor EL  6.22% 5silsoft ETS 12.43% 6 DC 200 Fluid (1cSt) 15.49% 7 DM5 CS  9.30% 8 Xironacaribbean  0.02% blue 9 Jeecide cap 5  1.00%

Procedure:

Components 1-4 and 9, were mixed until a clear dispersion formed (PhaseA). Compounds 5-8 were mixed separately until a uniform solidsdispersion was formed. Phase A was subsequently added to Phase B andmixed.

Example 8 Viscosity Measurements

The viscosity of a fluid can be measured by many methods known to one ofskill in the art. Specifically, “The rheology handbook: for users ofrotational and oscillatory rheometers By Thomas G. Mezger” or ASTMstandards such as ASTM D3835-08, ASTM D2857-95, ASTM D2196-10, and ASTMD2983-09 instruct one of skill in the art on how to measure theviscosity of a fluid. Illustrative methods also include the followingmethods:

Method A I. Overview

-   -   This protocol determines the viscosity (cP) on a Brookfield        Viscometer. This protocol can be performed on a wide variety of        formulations including but not limited to immediate effects        treatment, and perfector.

II. Background

-   -   The viscosity of formulation is critical to its performance and        its aesthetics. Furthermore a change in viscosity with time or        exposure to a stress condition is an important indicator of        formulation instability. As such, it is important to be able to        reproducibly and accurately evaluate formulation viscosity. The        following protocol can be used to determine the viscosity at        single shear rate of a formulation whose viscosity is between 50        and 300 Pas.

III. Materials

-   -   A full 2 oz to 8 oz jar containing formulation of interest    -   Brookfield DV-II+Pro EXTRA Viscometer and RV-6 spindle.    -   Test requires ˜5 minutes per sample

IV. Analytical Precautions

-   -   Clean the viscometer geometry prior to use    -   Insert the geometry to the appropriate depth in the center of        the sample container    -   Insure the container is stationary during the test

V. Protocol

5.1 Preparing Equipment:

-   -   1. Turn on the Brookfield DV-II+Pro EXTRA Viscometer by pressing        a switch in the back of the instrument. Select “External Mode”        by pressing the up arrow on the instrument control panel.    -   2. Start the Rheocalc software, a shortcut to which can be found        on the desktop    -   3. Zero the viscometer by clicking the lightning symbol on the        dashboard tab (instrument geometry should NOT be installed)    -   4. Find RV-6 test geometry and clean with 50%/50% IPA/Mineral        Spirits mixture, then wipe dry    -   5. Insert RV-6 geometry by pulling the instrument geometry        holder sleeve up.    -   6. Pick the test method by Clicking Test tab, and opening        Hold0.5-RV6-081511.RCP method.

5.2 Preparing Sample:

-   -   1. No special sample preparation is required other than doing a        visual inspection to ensure the sample appears uniform.

5.3 Perform Viscosity Measurement:

-   -   1. Insert the geometry into the 2 to 8 oz of sample under.        -   i. Insure that the geometry is inserted to the correct            measuring hight as indicated by thin section in the rod of            the geometry        -   ii. Insure that the geometry is centered in the jar    -   2. Adjust the stand so as to keep the sample and the geometry in        the appropriate relative position.    -   3. Click the small play button in the test tab to start the test    -   4. Name the data file appropriately and save the file to the        appropriate location    -   5. Allow the test to run to completion, then save your data for        later analysis    -   6. To test another sample:        -   i. Slide the sample stand out and remove the sample from the            instrument        -   ii. Remove the geometry from the instrument and gently wipe            down all surfaces with 50% IPA, 50% Mineral Spirit mixture.            Dry with a lint free wipe.        -   iii. Replace the geometry, return to test tab and start next            test    -   7. After finishing with the last test sample, clean geometry        with 50% WA, 50% Mineral Spirit mixture, then wipe dry and place        back in geometry box.

VI. Data Analysis

-   -   1. Open datafile (*.DB) and click the export button to obtain an        excel file containing the data.    -   2. Locate the ViscometerPerfectorTemplate_JL-081511-v1-beta        1.xlsx Excel template for data analysis    -   3. Paste the data into the first sheet    -   4. Record the average viscosity and the standard deviation    -   5. Save the template as an electronic record with a new name        that references the analyzed sample.    -   1. Repeat analysis for each data set.

Method B I. Overview

-   -   This protocol determines the viscosity (Pas) at 0.5 l/s, Shear        Thinning factor (Pa*ŝ2), and the strain rate of instability.        This protocol can be performed on a wide variety of formulations        including but not limited to immediate effects treatment, and        perfector, along with any other “cream” or “lotion”

II. Background

-   -   The viscosity of formulas and its change has been correlated to        stability of formulations. As such, it is important to be able        to reproducibly and accurately evaluate their viscosity        properties to be used as a predictive tool for stability of        Immediate Effects active prototypes. The following protocol can        be used to determine the viscosity, shear thinning factor, and        strain rate of instability.

III. Materials

-   -   >1 g Formulation of Interest    -   Bohlin CVO100 Rheometer mounted with 20 mm Parallel plate        geometry    -   Test requires ˜12 minutes per sample

IV. Analytical Precautions

-   -   Clean sides of the geometry are critical for accurate test        results    -   Any deviations must be noted

V. Protocol

5.1 Preparing Equipment:

-   -   8. Set up the Bohlin Rheometer        -   a. Turn on the instrument        -   b. Turn on the temperature controller        -   c. Start the Bohlin software        -   d. Load the viscosity stability test template        -   e. Make sure both the geometry and plate are clean    -   9. Install the geometry        -   a. Zero the instrument and you are now ready to being            testing.    -   10. For testing of multiple samples simply raise and clean the        geometry first with a dry wipe, then with a 50%/50% IPA/Mineral        Spirits mixture, then again with a dry wipe.

5.2 Preparing Sample:

-   -   1. No special sample preparation is required other than doing a        visual inspection to ensure the sample appears uniform.

VI. Perform the Viscosity Test

-   -   7. Place ˜1 g of mixed material onto the bottom plate in a mound        centered below the geometry    -   8. Lower the geometry to the correct gap (250 um)    -   9. Clean the excess material from the sides of the geometry        using the flat end of a spatula    -   10. Allow the test to run to completion, then save your data for        later analysis    -   11. To continue onto the next test, raise the geometry and        remove the sample from the instrument. Gently wipe down all        surfaces with 50% ipa/50% mineral spirits mixture. Dry with a        lint free wipe.    -   12. You are now ready to commence the next cure test

VII. Data Analysis:

-   -   2. Locate the following Excel Template for the data analysis        ViscosityStabilityTemplate061411-v2    -   3. Paste the raw instrument data from the appropriate Bohlin        Viscometry Data File file into A:2 of sheet 1 (near the left        corner) of the excel document    -   4. Paste the sample name into A:1 of sheet 1 of the excel        document    -   5. Record the calculated “Viscosity (Pas) at 0.5 Vs” as        viscosity    -   6. Record the calculated “Shear Thining factor (Pa*ŝ2)” as the        shear thinning factor    -   7. Record the calculated “Strain Rate of instability” as the        Strain Stability (Scale is out of 100)    -   8. Save the completed template as an electronic record with an        appropriate file name    -   9. Repeat steps 2 to 7 for remaining raw data

EQUIVALENTS

Those skilled in the art will recognize, or be able to ascertain usingno more than routine experimentation, numerous equivalents to thespecific polypeptides, nucleic acids, methods, assays and reagentsdescribed herein. Such equivalents are considered to be within the scopeof this invention and are covered by the following claims.

1. A body corrective formulation for application to the skin,comprising: a) a reactive reinforcing component; and b) a cross-linkingcomponent; wherein said cross-linking component facilitates in situcross-linking of the reactive reinforcing component, such that a bodycorrective film is formed on skin, and wherein said film when formed hasan appearance of natural skin. 2.-4. (canceled)
 5. The formulation ofclaim 1, wherein said reactive reinforcing component and saidcross-linking component are prevented from contacting each other priorto use.
 6. The formulation of claim 1, wherein said reactive reinforcingcomponent comprises a reactive constituent and a reinforcingconstituent.
 7. The formulation of claim 6, wherein said reactiveconstituent comprises at least one organopolysiloxane and at least onehydride functionalized polysiloxane.
 8. The formulation of claim 7,wherein said organopolysiloxane is a high viscosity organopolysiloxaneor a low viscosity organopolysiloxane or a combination thereof. 9.-10.(canceled)
 11. The formulation of claim 8, wherein said high viscosityorganopolysiloxane is substantially vinyl terminated.
 12. Theformulation of claim 8, wherein said high viscosity organopolysiloxaneis polydimethylsiloxane.
 13. The formulation of claim 8, wherein saidhigh viscosity organopolysiloxane has a weight percent of vinyl ofbetween about 0.05 and about 0.1 or a vinyl equivalent per kilogram ofbetween about 0.001 and about 0.05 or a combination thereof. 14.(canceled)
 15. The formulation of claim 8, wherein said low viscosityorganopolysiloxane has a viscosity of between about 1,000 and about50,000 cSt or cP at 25° C.; a weight percent of vinyl of between about0.01 and about 0.5; or a vinyl equivalent per kilogram of between about0.001 and about 0.1 or a combination thereof. 16.-19. (canceled)
 20. Theformulation of claim 8, wherein said low viscosity organopolysiloxane issubstantially vinyl terminated.
 21. The formulation of claim 8, whereinsaid low viscosity organopolysiloxane is vinyl terminatedpolydimethylsiloxane.
 22. The formulation of claim 7, wherein saidhydride functionalized polysiloxane has a viscosity of between about 2and 10,000 cSt or cP at 25° C.; a percent SiH content of between about 5and about 75%; or a SiH content of between about 0.5 and about 10mmol/g; or a combination thereof. 23.-24. (canceled)
 25. The formulationof claim 7, wherein said hydride functionalized polysiloxane is selectedfrom the group consisting of hydride terminated polydimethylsiloxane;polyphenyl-(dimethylhydrosiloxy)siloxane, hydride terminated;methylhydrosiloxane-phenylmethylsiloxane copolymer, hydride terminated;methylhydrosiloxane-dimethylsiloxane copolymers, trimethylsiloxyterminated; polymethylhydrosiloxanes, trimethylsiloxy terminated;polyethylhydrosiloxane, triethylsiloxane,methylhydrosiloxane-phenyloctylmethylsiloxane copolymer;methylhydrosiloxane-phenyloctylmethylsiloxane terpolymer andcombinations thereof.
 26. The formulation of claim 25, wherein saidhydride functionalized polysiloxane is substantially alkyl terminated.27. (canceled)
 28. The formulation of claim 7, wherein said hydridefunctionalized polysiloxane has at least 2 Si—H units on average. 29.(canceled)
 30. The formulation of claim 1, wherein said reactivereinforcing component has a vinyl organopolysiloxane to functionalhydride molar ratio of between about 1:10 and about 1:100. 31.-32.(canceled)
 33. The formulation of claim 6, wherein said reinforcingconstituent is selected from the group consisting of optionally surfacetreated mica, zinc oxide, titanium dioxide, aluminum oxide, clay orsilica. 34.-40. (canceled)
 41. The formulation of claim 1, wherein thecrosslinking component comprises a metal catalyst.
 42. The formulationof claim 41, wherein said catalyst is a platinum catalyst.
 43. Theformulation of claim 42, wherein said catalyst is selected from thegroup consisting of platinum carbonyl cyclovinylmethylsiloxanecomplexes, platinum divinyltetramethyldisiloxane complexes, platinumcyclovinylmethylsiloxane complexes, platinum octanaldehyde/octanolcomplexes and combinations thereof. 44.-46. (canceled)
 47. Theformulation of claim 1, wherein said formulation further comprises acosmetic agent or a therapeutic agent.
 48. A body corrective filmprepared by a process comprising the steps of: a) applying a reactivereinforcing component to skin; and b) applying a cross-linking componentto said reactive reinforcing component, wherein said cross-linkingcomponent facilitates in situ cross-linking of the reactive reinforcingcomponent, such that a body corrective film is formed on skin. 49.-50.(canceled)
 51. The film of claim 48, wherein the film has a leatheradhesive force of greater than about 20 N/mm; a Young's Modulus ofbetween about 0.01 and about 1 MPa; a fracture strain is at least about150%; a hysteresis of less than about 5%; or an adhesion of betweenabout 20 N/mm and about 80 N/mm; or a combination thereof. 52.-55.(canceled)
 56. The film of claim 48, wherein the film is less than about100 microns thick.
 57. The film of claim 48, wherein the film shrinks byless than about 1 to about 15%.
 58. The film of claim 48, wherein saidfilm upon application to the body has the appearance of natural skin; orprovides elasticity and recoil approaching that of youthful skin; or acombination thereof.
 59. (canceled)
 60. A method for correcting skinimperfections on a subject's skin comprising applying to said subject'sskin a formulation comprising: a) a first reactive reinforcingcomponent; and b) a second cross-linking component; wherein saidcross-linking component facilitates in situ cross-linking of thereactive reinforcing component, such that a film is formed on skin,thereby correcting skin imperfections. 61.-62. (canceled)
 63. A methodof shaping a subject's body, comprising applying to said subject's bodya formulation comprising: a) a first reactive reinforcing component; andb) a second cross-linking component; wherein said cross-linkingcomponent facilitates in situ cross-linking of the reactive reinforcingcomponent such that a film is formed on body, thereby shaping the body.64. The method of claim 63, wherein the film shapes the body byproviding support to soft body tissues; or reduces sagging of soft bodytissues or a combination thereof. 65.-66. (canceled)
 67. A method fordelivering an agent to a subject, comprising applying to the subject'sskin a formulation comprising: a) a first reactive reinforcing componentoptionally comprising one or more agents; and b) a second cross-linkingcomponent optionally comprising one or more agents; wherein saidcross-linking component facilitates in situ cross-linking of thereactive reinforcing component such that a film is formed on skin,thereby delivering the agent to the subject.
 68. (canceled)
 69. A bodycorrective composition for application to a subject's body, comprisingat least one preselected function modulating component, wherein saidcomposition forms a body corrective film upon application to thesubject's body, and wherein said film has an appearance of natural skin.70.-71. (canceled)
 72. A film removing cleanser comprising a filmwetting component, a penetration component, a film swelling componentand a film release component 73.-91. (canceled)
 92. The formulation ofclaim 1, wherein the formulation further comprises a finishingformulation applied to the film after formation of the film. 93.-95.(canceled)
 96. The formulation of claims 1 further comprising a pigmentdispersion formulation. 97.-109. (canceled)
 110. A wrinkle correctiveformulation for application to the skin, comprising: a) a reactivereinforcing component; and b) a cross-linking component; wherein saidcross-linking component facilitates in situ cross-linking of thereactive reinforcing component, such that a wrinkle corrective film isformed on skin, and wherein said film when formed reduces the appearanceof wrinkles.
 111. A bag reducing formulation for application to theskin, comprising: a) a reactive reinforcing component; and b) across-linking component; wherein said cross-linking componentfacilitates in situ cross-linking of the reactive reinforcing component,such that a bag reducing film is formed on skin, and wherein said filmwhen formed reduces the appearance of bags under the eyes.
 112. Afirmness imparting formulation for application to the skin, comprising:a) a reactive reinforcing component; and b) a cross-linking component;wherein said cross-linking component facilitates in situ cross-linkingof the reactive reinforcing component, such that a firmness impartingfilm is formed on skin, and wherein said film when formed imparts anappearance of firmness to the skin.